- W2078035229 endingPage "745" @default.
- W2078035229 startingPage "740" @default.
- W2078035229 abstract "Resistance spot welded joints made of two advanced high strength steels (AHSS) and one high strength steel (HSS) were examined. In the high cycle fatigue regime tests were realised for one loading condition, and the load and the displacement were measured. From the load and displacement range, the stiffness was calculated and in situ normalised to its value after 1000 cycles. It was thus possible to use the normalised stiffness evaluated during the experiment as failure criterion for the fatigue test of resistance spot welded joints. In order to evaluate this failure criterion, fatigue cracks were produced in the three different steel grades mentioned above according to user-specified levels of the normalised stiffness. It was found that the fatigue crack area increases linearly and the through-sheet-thickness crack length exponentially with decreasing stiffness. The comparison of the fatigue crack propagation during the fatigue test of the three different tested base metals showed very similar values. The comparability of fatigue tests performed on spot welded joints might thus be improved by the in situ evaluated stiffness as a failure criterion. This can be also used in further work to verify results of computer simulations of the stress intensity factor at spot welds with the help of experimental results." @default.
- W2078035229 created "2016-06-24" @default.
- W2078035229 creator A5001877876 @default.
- W2078035229 creator A5055734389 @default.
- W2078035229 creator A5086454847 @default.
- W2078035229 date "2011-05-01" @default.
- W2078035229 modified "2023-10-04" @default.
- W2078035229 title "Evaluation of fatigue crack propagation in spot welded joints by stiffness measurements" @default.
- W2078035229 cites W126647422 @default.
- W2078035229 cites W1905112784 @default.
- W2078035229 cites W1980336216 @default.
- W2078035229 cites W1991360649 @default.
- W2078035229 cites W1996026551 @default.
- W2078035229 cites W2013660521 @default.
- W2078035229 cites W2039904893 @default.
- W2078035229 cites W2077121149 @default.
- W2078035229 cites W2117786811 @default.
- W2078035229 cites W2139308248 @default.
- W2078035229 cites W2338645479 @default.
- W2078035229 cites W2510491519 @default.
- W2078035229 cites W3133873000 @default.
- W2078035229 cites W57100142 @default.
- W2078035229 doi "https://doi.org/10.1016/j.ijfatigue.2010.12.005" @default.
- W2078035229 hasPublicationYear "2011" @default.
- W2078035229 type Work @default.
- W2078035229 sameAs 2078035229 @default.
- W2078035229 citedByCount "14" @default.
- W2078035229 countsByYear W20780352292012 @default.
- W2078035229 countsByYear W20780352292013 @default.
- W2078035229 countsByYear W20780352292014 @default.
- W2078035229 countsByYear W20780352292015 @default.
- W2078035229 countsByYear W20780352292016 @default.
- W2078035229 countsByYear W20780352292023 @default.
- W2078035229 crossrefType "journal-article" @default.
- W2078035229 hasAuthorship W2078035229A5001877876 @default.
- W2078035229 hasAuthorship W2078035229A5055734389 @default.
- W2078035229 hasAuthorship W2078035229A5086454847 @default.
- W2078035229 hasConcept C107551265 @default.
- W2078035229 hasConcept C110209231 @default.
- W2078035229 hasConcept C127413603 @default.
- W2078035229 hasConcept C131850400 @default.
- W2078035229 hasConcept C15744967 @default.
- W2078035229 hasConcept C159985019 @default.
- W2078035229 hasConcept C18555067 @default.
- W2078035229 hasConcept C192562407 @default.
- W2078035229 hasConcept C19474535 @default.
- W2078035229 hasConcept C2779372316 @default.
- W2078035229 hasConcept C28539199 @default.
- W2078035229 hasConcept C542102704 @default.
- W2078035229 hasConcept C59085676 @default.
- W2078035229 hasConcept C66938386 @default.
- W2078035229 hasConceptScore W2078035229C107551265 @default.
- W2078035229 hasConceptScore W2078035229C110209231 @default.
- W2078035229 hasConceptScore W2078035229C127413603 @default.
- W2078035229 hasConceptScore W2078035229C131850400 @default.
- W2078035229 hasConceptScore W2078035229C15744967 @default.
- W2078035229 hasConceptScore W2078035229C159985019 @default.
- W2078035229 hasConceptScore W2078035229C18555067 @default.
- W2078035229 hasConceptScore W2078035229C192562407 @default.
- W2078035229 hasConceptScore W2078035229C19474535 @default.
- W2078035229 hasConceptScore W2078035229C2779372316 @default.
- W2078035229 hasConceptScore W2078035229C28539199 @default.
- W2078035229 hasConceptScore W2078035229C542102704 @default.
- W2078035229 hasConceptScore W2078035229C59085676 @default.
- W2078035229 hasConceptScore W2078035229C66938386 @default.
- W2078035229 hasIssue "5" @default.
- W2078035229 hasLocation W20780352291 @default.
- W2078035229 hasOpenAccess W2078035229 @default.
- W2078035229 hasPrimaryLocation W20780352291 @default.
- W2078035229 hasRelatedWork W1989376198 @default.
- W2078035229 hasRelatedWork W2169161539 @default.
- W2078035229 hasRelatedWork W2357537980 @default.
- W2078035229 hasRelatedWork W2374676405 @default.
- W2078035229 hasRelatedWork W2606135462 @default.
- W2078035229 hasRelatedWork W2974073757 @default.
- W2078035229 hasRelatedWork W3036125250 @default.
- W2078035229 hasRelatedWork W3106912962 @default.
- W2078035229 hasRelatedWork W3190750232 @default.
- W2078035229 hasRelatedWork W863198876 @default.
- W2078035229 hasVolume "33" @default.
- W2078035229 isParatext "false" @default.
- W2078035229 isRetracted "false" @default.
- W2078035229 magId "2078035229" @default.
- W2078035229 workType "article" @default.