- W2078241427 endingPage "4212" @default.
- W2078241427 startingPage "4212" @default.
- W2078241427 abstract "Superconducting Ba (X=Y, Nd, Sm, Gd, Dy, Er, Yb) CuO were made independently by the solid reaction method via mixing barium carbonate, (X) oxides, and copper oxide with atomic ion ratio Ba:X:Cu=R:1:R+1 with R=1−4, and sintering at 900–1000 °C for 24–72 h. (1) The best superconductor was found to be formed via R=2 and sintering near 950 °C. All samples studied were found to have layered perovskite x-ray diffraction patterns. Samples via R=1,3, and 4 were also found to have structures similar to those via R=2, and found to have two phases by the x-ray diffraction. The temperature-dependent magnetizations M(T) were measured by using the BTi SQUID susceptometer. The transition temperature Tc was determined by extrapolating M(T) and was found to be sensitive to the cooling rate of the sample during its synthesis. The Meissner effect was observed up to 78–92 K, and the fluxoids were found to be trapped while the samples cooled in a finite field at all temperatures below Tc. M(T) was found to be of three types: type 1 being similar to that of Pb, type 2 having a knee perhaps due to the two crystal structures, and type 3 having zero slope near Tc, perhaps due to the sample crystal sizes being less than the effective penetration depth. Samples with large crystal sizes were found to be of type 1 or 2. The measured M(T) can be understood in the framework of the BCS theory, and 2Δ(0)/k Tc were deduced to be in the range of 3–4.4. However, the magnetic hysteresis was found to be present at even low field 30 G at 10 K, and M(T) near Tc was found to be sensitive to thermal fluctuations. Various mechanisms for superconductivity in these systems will also be discussed." @default.
- W2078241427 created "2016-06-24" @default.
- W2078241427 creator A5044651915 @default.
- W2078241427 date "1988-04-15" @default.
- W2078241427 modified "2023-09-23" @default.
- W2078241427 title "Magnetization of high-temperature superconductors (abstract)" @default.
- W2078241427 doi "https://doi.org/10.1063/1.340230" @default.
- W2078241427 hasPublicationYear "1988" @default.
- W2078241427 type Work @default.
- W2078241427 sameAs 2078241427 @default.
- W2078241427 citedByCount "0" @default.
- W2078241427 crossrefType "journal-article" @default.
- W2078241427 hasAuthorship W2078241427A5044651915 @default.
- W2078241427 hasConcept C10874694 @default.
- W2078241427 hasConcept C113196181 @default.
- W2078241427 hasConcept C115260700 @default.
- W2078241427 hasConcept C115624301 @default.
- W2078241427 hasConcept C120665830 @default.
- W2078241427 hasConcept C121332964 @default.
- W2078241427 hasConcept C16889073 @default.
- W2078241427 hasConcept C185592680 @default.
- W2078241427 hasConcept C190561674 @default.
- W2078241427 hasConcept C191897082 @default.
- W2078241427 hasConcept C192562407 @default.
- W2078241427 hasConcept C193493375 @default.
- W2078241427 hasConcept C26873012 @default.
- W2078241427 hasConcept C2777581544 @default.
- W2078241427 hasConcept C32546565 @default.
- W2078241427 hasConcept C43617362 @default.
- W2078241427 hasConcept C47542005 @default.
- W2078241427 hasConcept C54101563 @default.
- W2078241427 hasConcept C542576722 @default.
- W2078241427 hasConcept C62520636 @default.
- W2078241427 hasConcept C73922627 @default.
- W2078241427 hasConcept C8010536 @default.
- W2078241427 hasConceptScore W2078241427C10874694 @default.
- W2078241427 hasConceptScore W2078241427C113196181 @default.
- W2078241427 hasConceptScore W2078241427C115260700 @default.
- W2078241427 hasConceptScore W2078241427C115624301 @default.
- W2078241427 hasConceptScore W2078241427C120665830 @default.
- W2078241427 hasConceptScore W2078241427C121332964 @default.
- W2078241427 hasConceptScore W2078241427C16889073 @default.
- W2078241427 hasConceptScore W2078241427C185592680 @default.
- W2078241427 hasConceptScore W2078241427C190561674 @default.
- W2078241427 hasConceptScore W2078241427C191897082 @default.
- W2078241427 hasConceptScore W2078241427C192562407 @default.
- W2078241427 hasConceptScore W2078241427C193493375 @default.
- W2078241427 hasConceptScore W2078241427C26873012 @default.
- W2078241427 hasConceptScore W2078241427C2777581544 @default.
- W2078241427 hasConceptScore W2078241427C32546565 @default.
- W2078241427 hasConceptScore W2078241427C43617362 @default.
- W2078241427 hasConceptScore W2078241427C47542005 @default.
- W2078241427 hasConceptScore W2078241427C54101563 @default.
- W2078241427 hasConceptScore W2078241427C542576722 @default.
- W2078241427 hasConceptScore W2078241427C62520636 @default.
- W2078241427 hasConceptScore W2078241427C73922627 @default.
- W2078241427 hasConceptScore W2078241427C8010536 @default.
- W2078241427 hasIssue "8" @default.
- W2078241427 hasLocation W20782414271 @default.
- W2078241427 hasOpenAccess W2078241427 @default.
- W2078241427 hasPrimaryLocation W20782414271 @default.
- W2078241427 hasRelatedWork W1589807630 @default.
- W2078241427 hasRelatedWork W2000437984 @default.
- W2078241427 hasRelatedWork W2016367309 @default.
- W2078241427 hasRelatedWork W2026347827 @default.
- W2078241427 hasRelatedWork W2035340167 @default.
- W2078241427 hasRelatedWork W2093376385 @default.
- W2078241427 hasRelatedWork W2240519871 @default.
- W2078241427 hasRelatedWork W2531671180 @default.
- W2078241427 hasRelatedWork W3105533862 @default.
- W2078241427 hasRelatedWork W2524104328 @default.
- W2078241427 hasVolume "63" @default.
- W2078241427 isParatext "false" @default.
- W2078241427 isRetracted "false" @default.
- W2078241427 magId "2078241427" @default.
- W2078241427 workType "article" @default.