• W2078356887 abstract "The amorphous alloys Nd40Fe40Co5Al8B7, Nd57Fe20Co5Al10B8, and Nd57Fe20Cu5Al10B8 were prepared by copper mold casting, melt spinning, and mechanical alloying. Despite their similar x-ray diffraction patterns, samples display different magnetic and thermal behavior correlated with the method of preparation. The fully amorphous melt-spun ribbons exhibit relatively soft magnetic properties with coercivities ≈40 kA/m at room temperature and a Curie temperature (TC)≈474 K. Apparently only the mold-cast cylinders of 3 mm diameter show hard magnetic behavior with a coercivity in the range of 258–270 kA/m (depending on composition) and have approximately the same TC as that of the melt-spun ribbons. An additional magnetic transition at 585 K due to the presence of Nd2Fe14B phase in the case of Nd40Fe40Co5Al8B7 cast rod has been observed. Heat treatment above crystallization temperature in as-cast Nd57Fe20Co5Al10B8 and Nd57Fe20Cu5Al10B8 samples destroys the hard magnetic properties. In contrast, mechanically alloyed amorphous samples are soft magnetic with maximum coercivity up to 11 kA/m but show an entirely different TC≈680–740 K, which is rather characteristic of an Fe solid solution. The magnetic properties are discussed in terms of different local atomic environment and cluster sizes in amorphous samples prepared by different methods." @default.
• W2078356887 created "2016-06-24" @default.
• W2078356887 creator A5028967959 @default.
• W2078356887 creator A5062020381 @default.
• W2078356887 creator A5077421413 @default.
• W2078356887 creator A5077858913 @default.
• W2078356887 creator A5078052571 @default.
• W2078356887 creator A5080343347 @default.
• W2078356887 date "2002-03-15" @default.
• W2078356887 modified "2023-09-27" @default.
• W2078356887 title "Magnetic properties of Nd–Fe–Co(Cu)–Al–B amorphous alloys prepared by nonequilibrium techniques" @default.
• W2078356887 cites W1029978615 @default.
• W2078356887 cites W1555328909 @default.
• W2078356887 cites W1639381188 @default.
• W2078356887 cites W180281154 @default.
• W2078356887 cites W1987117496 @default.
• W2078356887 cites W2002166267 @default.
• W2078356887 cites W2009154952 @default.
• W2078356887 cites W2017323493 @default.
• W2078356887 cites W2023807099 @default.
• W2078356887 cites W2024360227 @default.
• W2078356887 cites W2024527730 @default.
• W2078356887 cites W2033040893 @default.
• W2078356887 cites W2035349234 @default.
• W2078356887 cites W2041702900 @default.
• W2078356887 cites W2049414833 @default.
• W2078356887 cites W2064691647 @default.
• W2078356887 cites W2067445187 @default.
• W2078356887 cites W2080679168 @default.
• W2078356887 cites W2082179795 @default.
• W2078356887 cites W2088815315 @default.
• W2078356887 cites W2088918906 @default.
• W2078356887 cites W2089182979 @default.
• W2078356887 cites W2106048245 @default.
• W2078356887 doi "https://doi.org/10.1063/1.1448884" @default.
• W2078356887 hasPublicationYear "2002" @default.
• W2078356887 type Work @default.
• W2078356887 sameAs 2078356887 @default.
• W2078356887 citedByCount "14" @default.
• W2078356887 countsByYear W20783568872013 @default.
• W2078356887 crossrefType "journal-article" @default.
• W2078356887 hasAuthorship W2078356887A5028967959 @default.
• W2078356887 hasAuthorship W2078356887A5062020381 @default.
• W2078356887 hasAuthorship W2078356887A5077421413 @default.
• W2078356887 hasAuthorship W2078356887A5077858913 @default.
• W2078356887 hasAuthorship W2078356887A5078052571 @default.
• W2078356887 hasAuthorship W2078356887A5080343347 @default.
• W2078356887 hasConcept C113196181 @default.
• W2078356887 hasConcept C121332964 @default.
• W2078356887 hasConcept C123266363 @default.
• W2078356887 hasConcept C124712363 @default.
• W2078356887 hasConcept C126530901 @default.
• W2078356887 hasConcept C127413603 @default.
• W2078356887 hasConcept C154815118 @default.
• W2078356887 hasConcept C159985019 @default.
• W2078356887 hasConcept C16635281 @default.
• W2078356887 hasConcept C185592680 @default.
• W2078356887 hasConcept C191897082 @default.
• W2078356887 hasConcept C192562407 @default.
• W2078356887 hasConcept C203036418 @default.
• W2078356887 hasConcept C26873012 @default.
• W2078356887 hasConcept C2776820801 @default.
• W2078356887 hasConcept C2779784324 @default.
• W2078356887 hasConcept C2780026712 @default.
• W2078356887 hasConcept C42360764 @default.
• W2078356887 hasConcept C43617362 @default.
• W2078356887 hasConcept C46141821 @default.
• W2078356887 hasConcept C56052488 @default.
• W2078356887 hasConcept C63648874 @default.
• W2078356887 hasConcept C8010536 @default.
• W2078356887 hasConcept C82217956 @default.
• W2078356887 hasConceptScore W2078356887C113196181 @default.
• W2078356887 hasConceptScore W2078356887C121332964 @default.
• W2078356887 hasConceptScore W2078356887C123266363 @default.
• W2078356887 hasConceptScore W2078356887C124712363 @default.
• W2078356887 hasConceptScore W2078356887C126530901 @default.
• W2078356887 hasConceptScore W2078356887C127413603 @default.
• W2078356887 hasConceptScore W2078356887C154815118 @default.
• W2078356887 hasConceptScore W2078356887C159985019 @default.
• W2078356887 hasConceptScore W2078356887C16635281 @default.
• W2078356887 hasConceptScore W2078356887C185592680 @default.
• W2078356887 hasConceptScore W2078356887C191897082 @default.
• W2078356887 hasConceptScore W2078356887C192562407 @default.
• W2078356887 hasConceptScore W2078356887C203036418 @default.
• W2078356887 hasConceptScore W2078356887C26873012 @default.
• W2078356887 hasConceptScore W2078356887C2776820801 @default.
• W2078356887 hasConceptScore W2078356887C2779784324 @default.
• W2078356887 hasConceptScore W2078356887C2780026712 @default.
• W2078356887 hasConceptScore W2078356887C42360764 @default.
• W2078356887 hasConceptScore W2078356887C43617362 @default.
• W2078356887 hasConceptScore W2078356887C46141821 @default.
• W2078356887 hasConceptScore W2078356887C56052488 @default.
• W2078356887 hasConceptScore W2078356887C63648874 @default.
• W2078356887 hasConceptScore W2078356887C8010536 @default.
• W2078356887 hasConceptScore W2078356887C82217956 @default.
• W2078356887 hasIssue "6" @default.
• W2078356887 hasLocation W20783568871 @default.
• W2078356887 hasOpenAccess W2078356887 @default.

• next