- W2078497423 abstract "The corrosion test was performed for ferritic/martensitic steel HCM12A with and without Fe-Al alloy coating in LBE at temperatures of 550 and 650°C under loading for an immersion time up to 500 h. After the corrosion test at 550°C for 500 h, both of the uncoated and Fe-Al-coated HCM12A showed a good corrosion resistance without the influence of the tensile stress on the LBE corrosion. On the other hand, after the corrosion test at 650°C, the Fe-Al coating layer on the specimen surface exhibited no LBE dissolution corrosion because of the formation of a stable oxide protection film on the coating layer surface, although the coating layer cracked. The LBE penetrated into the cracks and corroded the base metal and the precoating layer. The uncoated HCM12A exhibited the double oxide layers of FeO and Fe- Cr spinel. The FeO was damaged in the bent zone by the stress, and the Fe-Cr spinel layer was not destroyed by the influence of cracking and the tensile stress. The cracking and stress did not have a large in..." @default.
- W2078497423 created "2016-06-24" @default.
- W2078497423 creator A5021340166 @default.
- W2078497423 creator A5065929763 @default.
- W2078497423 date "2011-05-01" @default.
- W2078497423 modified "2023-10-17" @default.
- W2078497423 title "Corrosion Resistance of Fe-Al-Alloy-Coated Ferritic/Martensitic Steel under Bending Stress in High-Temperature Lead-Bismuth Eutectic" @default.
- W2078497423 cites W1966446596 @default.
- W2078497423 cites W1974629080 @default.
- W2078497423 cites W1995509666 @default.
- W2078497423 cites W2011136860 @default.
- W2078497423 cites W2016879211 @default.
- W2078497423 cites W2022957865 @default.
- W2078497423 cites W2025769892 @default.
- W2078497423 cites W2053820471 @default.
- W2078497423 cites W2061160701 @default.
- W2078497423 cites W2094268656 @default.
- W2078497423 cites W2109180847 @default.
- W2078497423 cites W49801563 @default.
- W2078497423 doi "https://doi.org/10.1080/18811248.2011.9711762" @default.
- W2078497423 hasPublicationYear "2011" @default.
- W2078497423 type Work @default.
- W2078497423 sameAs 2078497423 @default.
- W2078497423 citedByCount "17" @default.
- W2078497423 countsByYear W20784974232012 @default.
- W2078497423 countsByYear W20784974232017 @default.
- W2078497423 countsByYear W20784974232019 @default.
- W2078497423 countsByYear W20784974232020 @default.
- W2078497423 countsByYear W20784974232021 @default.
- W2078497423 countsByYear W20784974232022 @default.
- W2078497423 countsByYear W20784974232023 @default.
- W2078497423 crossrefType "journal-article" @default.
- W2078497423 hasAuthorship W2078497423A5021340166 @default.
- W2078497423 hasAuthorship W2078497423A5065929763 @default.
- W2078497423 hasBestOaLocation W20784974231 @default.
- W2078497423 hasConcept C114793014 @default.
- W2078497423 hasConcept C127313418 @default.
- W2078497423 hasConcept C138885662 @default.
- W2078497423 hasConcept C159985019 @default.
- W2078497423 hasConcept C18168003 @default.
- W2078497423 hasConcept C18747287 @default.
- W2078497423 hasConcept C191897082 @default.
- W2078497423 hasConcept C192562407 @default.
- W2078497423 hasConcept C20625102 @default.
- W2078497423 hasConcept C21036866 @default.
- W2078497423 hasConcept C2777093003 @default.
- W2078497423 hasConcept C2780026712 @default.
- W2078497423 hasConcept C41895202 @default.
- W2078497423 hasConcept C533668322 @default.
- W2078497423 hasConcept C87210426 @default.
- W2078497423 hasConcept C87976508 @default.
- W2078497423 hasConceptScore W2078497423C114793014 @default.
- W2078497423 hasConceptScore W2078497423C127313418 @default.
- W2078497423 hasConceptScore W2078497423C138885662 @default.
- W2078497423 hasConceptScore W2078497423C159985019 @default.
- W2078497423 hasConceptScore W2078497423C18168003 @default.
- W2078497423 hasConceptScore W2078497423C18747287 @default.
- W2078497423 hasConceptScore W2078497423C191897082 @default.
- W2078497423 hasConceptScore W2078497423C192562407 @default.
- W2078497423 hasConceptScore W2078497423C20625102 @default.
- W2078497423 hasConceptScore W2078497423C21036866 @default.
- W2078497423 hasConceptScore W2078497423C2777093003 @default.
- W2078497423 hasConceptScore W2078497423C2780026712 @default.
- W2078497423 hasConceptScore W2078497423C41895202 @default.
- W2078497423 hasConceptScore W2078497423C533668322 @default.
- W2078497423 hasConceptScore W2078497423C87210426 @default.
- W2078497423 hasConceptScore W2078497423C87976508 @default.
- W2078497423 hasIssue "5" @default.
- W2078497423 hasLocation W20784974231 @default.
- W2078497423 hasOpenAccess W2078497423 @default.
- W2078497423 hasPrimaryLocation W20784974231 @default.
- W2078497423 hasRelatedWork W1966870498 @default.
- W2078497423 hasRelatedWork W1996164230 @default.
- W2078497423 hasRelatedWork W2011614197 @default.
- W2078497423 hasRelatedWork W2136264421 @default.
- W2078497423 hasRelatedWork W2352982341 @default.
- W2078497423 hasRelatedWork W2549444252 @default.
- W2078497423 hasRelatedWork W2751119901 @default.
- W2078497423 hasRelatedWork W2807399361 @default.
- W2078497423 hasRelatedWork W3097783663 @default.
- W2078497423 hasRelatedWork W4297902612 @default.
- W2078497423 hasVolume "48" @default.
- W2078497423 isParatext "false" @default.
- W2078497423 isRetracted "false" @default.
- W2078497423 magId "2078497423" @default.
- W2078497423 workType "article" @default.