- W2079201900 abstract "The application of sputtering in a mixed gas of argon (Ar) and nitrogen (N2) to Al80Ti20 resulted in the formation of compositionally and structurally gradient film consisting of amorphous Al(Ti, N) and hexagonal Al(Ti)N phases. By continuously changing the partial pressure (PN) of N2 from 0.02 to 0.1 Pa in a total Ar+N2 pressure of 1 Pa, the resulting phase is an amorphous Al(Ti, N) in the PN range below 0.06 Pa and changes to an Al(Ti)N through coexistent amorphous plus Al(Ti)N phases in the higher PN range. The average sputtered rate of the film was 0.9 μm/ks and the N2 concentration along the film thickness increases to 63 at% with an increase in PN to 0.1 Pa. As PN increases, the wave vector at the peak position of the amorphous halo in the X-ray diffraction patterns decreases continuously and crystallization temperature increases from 662 to 728 K. The Knoop hardness and the electrical resistivity measured along the film thickness increase from 325 to 2310 and from 2.4×10−7 Ωm to an infinite value, respectively, with an increase in N2 content in the amorphous phase and the subsequent phase transition to Al(Ti)N. The load leading to a failure in the film is 0.44 N which is about twice as large as that (0.24 N) for the Al(Ti)N phase. Thus, the sputtered amorphous-hexagonal phase film is concluded to have functionally gradient characteristics resulting from the compositional and structural" @default.
- W2079201900 created "2016-06-24" @default.
- W2079201900 creator A5000994341 @default.
- W2079201900 creator A5008412118 @default.
- W2079201900 creator A5087422295 @default.
- W2079201900 date "1993-01-01" @default.
- W2079201900 modified "2023-10-09" @default.
- W2079201900 title "Production and Properties of Functionally Gradient Films Varying from Amorphous Al(Ti, N) to Hexagonal Al(Ti)N Phase" @default.
- W2079201900 cites W1664744281 @default.
- W2079201900 cites W1972821452 @default.
- W2079201900 cites W2016031380 @default.
- W2079201900 cites W2053419236 @default.
- W2079201900 cites W2058381858 @default.
- W2079201900 cites W2063560031 @default.
- W2079201900 cites W2075328987 @default.
- W2079201900 cites W2094497208 @default.
- W2079201900 doi "https://doi.org/10.2320/matertrans1989.34.548" @default.
- W2079201900 hasPublicationYear "1993" @default.
- W2079201900 type Work @default.
- W2079201900 sameAs 2079201900 @default.
- W2079201900 citedByCount "3" @default.
- W2079201900 countsByYear W20792019002015 @default.
- W2079201900 crossrefType "journal-article" @default.
- W2079201900 hasAuthorship W2079201900A5000994341 @default.
- W2079201900 hasAuthorship W2079201900A5008412118 @default.
- W2079201900 hasAuthorship W2079201900A5087422295 @default.
- W2079201900 hasBestOaLocation W20792019001 @default.
- W2079201900 hasConcept C113196181 @default.
- W2079201900 hasConcept C119599485 @default.
- W2079201900 hasConcept C127413603 @default.
- W2079201900 hasConcept C159985019 @default.
- W2079201900 hasConcept C165720898 @default.
- W2079201900 hasConcept C171250308 @default.
- W2079201900 hasConcept C178790620 @default.
- W2079201900 hasConcept C184498911 @default.
- W2079201900 hasConcept C185592680 @default.
- W2079201900 hasConcept C19067145 @default.
- W2079201900 hasConcept C192562407 @default.
- W2079201900 hasConcept C203036418 @default.
- W2079201900 hasConcept C22423302 @default.
- W2079201900 hasConcept C43617362 @default.
- W2079201900 hasConcept C44280652 @default.
- W2079201900 hasConcept C56052488 @default.
- W2079201900 hasConcept C69990965 @default.
- W2079201900 hasConcept C8010536 @default.
- W2079201900 hasConcept C87976508 @default.
- W2079201900 hasConceptScore W2079201900C113196181 @default.
- W2079201900 hasConceptScore W2079201900C119599485 @default.
- W2079201900 hasConceptScore W2079201900C127413603 @default.
- W2079201900 hasConceptScore W2079201900C159985019 @default.
- W2079201900 hasConceptScore W2079201900C165720898 @default.
- W2079201900 hasConceptScore W2079201900C171250308 @default.
- W2079201900 hasConceptScore W2079201900C178790620 @default.
- W2079201900 hasConceptScore W2079201900C184498911 @default.
- W2079201900 hasConceptScore W2079201900C185592680 @default.
- W2079201900 hasConceptScore W2079201900C19067145 @default.
- W2079201900 hasConceptScore W2079201900C192562407 @default.
- W2079201900 hasConceptScore W2079201900C203036418 @default.
- W2079201900 hasConceptScore W2079201900C22423302 @default.
- W2079201900 hasConceptScore W2079201900C43617362 @default.
- W2079201900 hasConceptScore W2079201900C44280652 @default.
- W2079201900 hasConceptScore W2079201900C56052488 @default.
- W2079201900 hasConceptScore W2079201900C69990965 @default.
- W2079201900 hasConceptScore W2079201900C8010536 @default.
- W2079201900 hasConceptScore W2079201900C87976508 @default.
- W2079201900 hasIssue "6" @default.
- W2079201900 hasLocation W20792019001 @default.
- W2079201900 hasOpenAccess W2079201900 @default.
- W2079201900 hasPrimaryLocation W20792019001 @default.
- W2079201900 hasRelatedWork W1605767265 @default.
- W2079201900 hasRelatedWork W1974722815 @default.
- W2079201900 hasRelatedWork W2027787483 @default.
- W2079201900 hasRelatedWork W2092338581 @default.
- W2079201900 hasRelatedWork W2278917233 @default.
- W2079201900 hasRelatedWork W2324053432 @default.
- W2079201900 hasRelatedWork W2567465873 @default.
- W2079201900 hasRelatedWork W2587439893 @default.
- W2079201900 hasRelatedWork W4254441781 @default.
- W2079201900 hasRelatedWork W275947400 @default.
- W2079201900 hasVolume "34" @default.
- W2079201900 isParatext "false" @default.
- W2079201900 isRetracted "false" @default.
- W2079201900 magId "2079201900" @default.
- W2079201900 workType "article" @default.