• W2079388445 endingPage "277" @default.
• W2079388445 startingPage "269" @default.
• W2079388445 abstract "Cr–Al–N coatings with Zr alloying (Zr contents from 0 to 29.5 at.%) were deposited by d.c. reactive magnetron sputtering. The chemical composition and the morphology of as-deposited coatings were characterized, and the phase structure, mechanical properties and wear resistance of the coatings before and after thermal annealing were analyzed and evaluated. With the increase of Zr content, both Cr and N contents decrease whereas Al shows a growing trend. Low Zr (<26.9 at.%) coatings are stoichiometric and present a fcc NaCl-type B1 structure with columnar morphology, while high Zr (≥26.9 at.%) coatings are in N deficiency and have low crystallinity degree. The alloying of low contents of Zr improves the coating hardness and H/E ratio; however, for low ordered coatings these properties decrease significantly. After thermal annealing, fcc structure is kept in low Zr films whereas the crystalline degree is improved in the high Zr ones and their mechanical properties were slightly improved. Two coatings were selected for further testing, representatives of low (CrAlZr5N) and high (CrAlZr27N) Zr contents. The onset oxidation temperature is ∼900 °C and 600 °C for CrAlZr5N and CrAlZr27N coatings, respectively. Mainly Cr2O3 is formed on low Zr coatings whereas mixed oxides of ZrO2 and Cr2O3 are detected on CrAlZr27N sample after thermal exposure. In all tribological tests, low Zr coating presents lower wear rate than the CrAlZr27N coating. In general, the addition of very high Zr contents (>20 at.%) with N deficiency markedly weakens the mechanical properties and the oxidation resistance of Cr–Al–Zr–N coatings." @default.
• W2079388445 created "2016-06-24" @default.
• W2079388445 creator A5002533270 @default.
• W2079388445 creator A5047103030 @default.
• W2079388445 creator A5056397894 @default.
• W2079388445 creator A5066153738 @default.
• W2079388445 creator A5066731066 @default.
• W2079388445 date "2014-10-01" @default.
• W2079388445 modified "2023-10-18" @default.
• W2079388445 title "Influence of Zr alloying on the mechanical properties, thermal stability and oxidation resistance of Cr–Al–N coatings" @default.
• W2079388445 cites W1979851670 @default.
• W2079388445 cites W1994818243 @default.
• W2079388445 cites W2002468578 @default.
• W2079388445 cites W2015970265 @default.
• W2079388445 cites W2028208869 @default.
• W2079388445 cites W2036610634 @default.
• W2079388445 cites W2043125800 @default.
• W2079388445 cites W2053497436 @default.
• W2079388445 cites W2054091243 @default.
• W2079388445 cites W2055712105 @default.
• W2079388445 cites W2058638690 @default.
• W2079388445 cites W2086933933 @default.
• W2079388445 cites W2091686787 @default.
• W2079388445 cites W2093123893 @default.
• W2079388445 cites W2094159114 @default.
• W2079388445 cites W2094929073 @default.
• W2079388445 cites W2114118942 @default.
• W2079388445 cites W2114233088 @default.
• W2079388445 cites W2134142547 @default.
• W2079388445 cites W2146063318 @default.
• W2079388445 cites W2157568501 @default.
• W2079388445 doi "https://doi.org/10.1016/j.apsusc.2014.08.115" @default.
• W2079388445 hasPublicationYear "2014" @default.
• W2079388445 type Work @default.
• W2079388445 sameAs 2079388445 @default.
• W2079388445 citedByCount "28" @default.
• W2079388445 countsByYear W20793884452015 @default.
• W2079388445 countsByYear W20793884452016 @default.
• W2079388445 countsByYear W20793884452017 @default.
• W2079388445 countsByYear W20793884452018 @default.
• W2079388445 countsByYear W20793884452019 @default.
• W2079388445 countsByYear W20793884452020 @default.
• W2079388445 countsByYear W20793884452021 @default.
• W2079388445 countsByYear W20793884452022 @default.
• W2079388445 crossrefType "journal-article" @default.
• W2079388445 hasAuthorship W2079388445A5002533270 @default.
• W2079388445 hasAuthorship W2079388445A5047103030 @default.
• W2079388445 hasAuthorship W2079388445A5056397894 @default.
• W2079388445 hasAuthorship W2079388445A5066153738 @default.
• W2079388445 hasAuthorship W2079388445A5066731066 @default.
• W2079388445 hasBestOaLocation W20793884452 @default.
• W2079388445 hasConcept C127413603 @default.
• W2079388445 hasConcept C144082473 @default.
• W2079388445 hasConcept C159985019 @default.
• W2079388445 hasConcept C171250308 @default.
• W2079388445 hasConcept C178790620 @default.
• W2079388445 hasConcept C185592680 @default.
• W2079388445 hasConcept C19067145 @default.
• W2079388445 hasConcept C191897082 @default.
• W2079388445 hasConcept C192562407 @default.
• W2079388445 hasConcept C22423302 @default.
• W2079388445 hasConcept C2777855556 @default.
• W2079388445 hasConcept C2781448156 @default.
• W2079388445 hasConcept C42360764 @default.
• W2079388445 hasConcept C46275449 @default.
• W2079388445 hasConcept C59061564 @default.
• W2079388445 hasConcept C61427134 @default.
• W2079388445 hasConceptScore W2079388445C127413603 @default.
• W2079388445 hasConceptScore W2079388445C144082473 @default.
• W2079388445 hasConceptScore W2079388445C159985019 @default.
• W2079388445 hasConceptScore W2079388445C171250308 @default.
• W2079388445 hasConceptScore W2079388445C178790620 @default.
• W2079388445 hasConceptScore W2079388445C185592680 @default.
• W2079388445 hasConceptScore W2079388445C19067145 @default.
• W2079388445 hasConceptScore W2079388445C191897082 @default.
• W2079388445 hasConceptScore W2079388445C192562407 @default.
• W2079388445 hasConceptScore W2079388445C22423302 @default.
• W2079388445 hasConceptScore W2079388445C2777855556 @default.
• W2079388445 hasConceptScore W2079388445C2781448156 @default.
• W2079388445 hasConceptScore W2079388445C42360764 @default.
• W2079388445 hasConceptScore W2079388445C46275449 @default.
• W2079388445 hasConceptScore W2079388445C59061564 @default.
• W2079388445 hasConceptScore W2079388445C61427134 @default.
• W2079388445 hasFunder F4320321001 @default.
• W2079388445 hasLocation W20793884451 @default.
• W2079388445 hasLocation W20793884452 @default.
• W2079388445 hasOpenAccess W2079388445 @default.
• W2079388445 hasPrimaryLocation W20793884451 @default.
• W2079388445 hasRelatedWork W1963791028 @default.
• W2079388445 hasRelatedWork W2005366662 @default.
• W2079388445 hasRelatedWork W2012271150 @default.
• W2079388445 hasRelatedWork W2070016632 @default.
• W2079388445 hasRelatedWork W2086692853 @default.
• W2079388445 hasRelatedWork W2297003625 @default.
• W2079388445 hasRelatedWork W2747856433 @default.
• W2079388445 hasRelatedWork W2793446430 @default.
• W2079388445 hasRelatedWork W3097783663 @default.
• W2079388445 hasRelatedWork W817500458 @default.

• next