- W2079480623 abstract "Magnesium crystals were irradiated at 77 °K in the RA-1 reactor to neutron doses up to 4 × 1018 ncm−2, and the deformation properties were studied at this temperature without warm-up. The yield stress increased with dose to a value of (465 ± 45) p/mm2 at 1 × × 1017 ncm−2. For neutron doses greater than this value, it was found that the deformation mechanism changed with an upper yield point being formed with an accompanying yield drop. The upper yield point and yield drop increased with dose and became very substantial at 4 × 1018 ncm−2 with the resolved yield stress increasing to 1000 p/mm2 and the yield drop to the order of 50%. The lower yield stress was independent of dose in the higher dose region. Annealing experiments showed an annealing peak centered at 240 °K. For large doses, recovery first occurred in the upper yield stress with the lower yield stress being unaffected until complete recovery of the upper yield stress occurred. Strain markings were studied and found inhomogeneous in character but different from a typical Lüders band. Magnesiumeinkristalle wurden bei 77 °K im RA-1-Reaktor mit Neutronendosen bis zu 4 × 1018 ncm−2 bestrahlt und die Deformationseigenschaften bei dieser Temperatur ohne Aufwärmung untersucht. Die Streckgrenze steigt mit der Dosis auf einen Wert von (465 ± ± 45) p/mm2 bei 1 × 1017 ncm−2 an. Für Neutronendosen, die größer als dieser Wert sind, wurde gefunden, daß sich der Deformationsmechanismus mit einer oberen Fließgrenze, die mit einem begleitenden Flußabfall gebildet wird, ändert. Die obere Fließgrenze und der Flußabfall steigen mit der Dosis an und werden bei 4 × 1018 ncm−2 sehr wesentlich, wobei die aufgelöste Streckgrenze auf 1000 p/mm2 ansteigt und der Flußabfall auf die Größenordnung 50%. Die untere Streckgrenze war unabhängig von der Dosis im Bereich der höheren Dosen. Temperungsexperimente zeigten ein Temperungsmaximum bei 240 °K. Für große Dosen tritt Erholung zuerst in der oberen Streckgrenze auf, wobei die untere Fließgrenze unbeeinflußt bleibt bis vollständige Erholung der oberen Strekgrenze eingetreten ist. Deformationsmarkierungen wurden untersucht und es wurde gefunden, daß sie inhomogen im Charakter, jedoch von typischen Lüdersbanden verschieden waren." @default.
- W2079480623 created "2016-06-24" @default.
- W2079480623 creator A5013675824 @default.
- W2079480623 creator A5025831052 @default.
- W2079480623 creator A5065005986 @default.
- W2079480623 date "1972-04-16" @default.
- W2079480623 modified "2023-09-27" @default.
- W2079480623 title "Mechanical properties of low temperature irradiated magnesium" @default.
- W2079480623 cites W12120800 @default.
- W2079480623 cites W1510972903 @default.
- W2079480623 cites W1971630422 @default.
- W2079480623 cites W2020303004 @default.
- W2079480623 cites W2049221375 @default.
- W2079480623 cites W2088297199 @default.
- W2079480623 cites W4255049663 @default.
- W2079480623 doi "https://doi.org/10.1002/pssa.2210100221" @default.
- W2079480623 hasPublicationYear "1972" @default.
- W2079480623 type Work @default.
- W2079480623 sameAs 2079480623 @default.
- W2079480623 citedByCount "3" @default.
- W2079480623 crossrefType "journal-article" @default.
- W2079480623 hasAuthorship W2079480623A5013675824 @default.
- W2079480623 hasAuthorship W2079480623A5025831052 @default.
- W2079480623 hasAuthorship W2079480623A5065005986 @default.
- W2079480623 hasConcept C111337013 @default.
- W2079480623 hasConcept C113196181 @default.
- W2079480623 hasConcept C121332964 @default.
- W2079480623 hasConcept C134121241 @default.
- W2079480623 hasConcept C13965031 @default.
- W2079480623 hasConcept C185544564 @default.
- W2079480623 hasConcept C185592680 @default.
- W2079480623 hasConcept C191897082 @default.
- W2079480623 hasConcept C192562407 @default.
- W2079480623 hasConcept C2777855556 @default.
- W2079480623 hasConcept C2781345722 @default.
- W2079480623 hasConcept C2982764207 @default.
- W2079480623 hasConcept C41008148 @default.
- W2079480623 hasConcept C43617362 @default.
- W2079480623 hasConcept C543218039 @default.
- W2079480623 hasConcept C76155785 @default.
- W2079480623 hasConceptScore W2079480623C111337013 @default.
- W2079480623 hasConceptScore W2079480623C113196181 @default.
- W2079480623 hasConceptScore W2079480623C121332964 @default.
- W2079480623 hasConceptScore W2079480623C134121241 @default.
- W2079480623 hasConceptScore W2079480623C13965031 @default.
- W2079480623 hasConceptScore W2079480623C185544564 @default.
- W2079480623 hasConceptScore W2079480623C185592680 @default.
- W2079480623 hasConceptScore W2079480623C191897082 @default.
- W2079480623 hasConceptScore W2079480623C192562407 @default.
- W2079480623 hasConceptScore W2079480623C2777855556 @default.
- W2079480623 hasConceptScore W2079480623C2781345722 @default.
- W2079480623 hasConceptScore W2079480623C2982764207 @default.
- W2079480623 hasConceptScore W2079480623C41008148 @default.
- W2079480623 hasConceptScore W2079480623C43617362 @default.
- W2079480623 hasConceptScore W2079480623C543218039 @default.
- W2079480623 hasConceptScore W2079480623C76155785 @default.
- W2079480623 hasIssue "2" @default.
- W2079480623 hasLocation W20794806231 @default.
- W2079480623 hasOpenAccess W2079480623 @default.
- W2079480623 hasPrimaryLocation W20794806231 @default.
- W2079480623 hasRelatedWork W1966822393 @default.
- W2079480623 hasRelatedWork W1972990362 @default.
- W2079480623 hasRelatedWork W1975411231 @default.
- W2079480623 hasRelatedWork W2004821781 @default.
- W2079480623 hasRelatedWork W2025263419 @default.
- W2079480623 hasRelatedWork W2046985241 @default.
- W2079480623 hasRelatedWork W2093366886 @default.
- W2079480623 hasRelatedWork W2365304130 @default.
- W2079480623 hasRelatedWork W2414483147 @default.
- W2079480623 hasRelatedWork W3177099499 @default.
- W2079480623 hasVolume "10" @default.
- W2079480623 isParatext "false" @default.
- W2079480623 isRetracted "false" @default.
- W2079480623 magId "2079480623" @default.
- W2079480623 workType "article" @default.