- W2079553206 endingPage "1071" @default.
- W2079553206 startingPage "1066" @default.
- W2079553206 abstract "The cordierite was synthesized at relatively low temperature by pressureless sintering method, using calcined bauxite, talcum , quartz and feldspar as raw materials in this paper. The water absorption (Wa), porosity (Pa), bulk density (D b ) and bending strength of samples have been tested, and the synthetic process and mechanism have been investigated by XRD, SEM, and so on. The results showed that the cordierite could be synthesized at 1280°C and the range of synthetic temperature is 1160~1300°C, when the sample was sintered at 1280°C for 2h, its bulk density and bending strength were 2.20g/cm 3 and 72.13MPa, respectively. XRD analysis showed that the main phase of sample was cordierite, the cordierite content was about 88wt%, and the minor phases were MgAl 2 O 4 spinel and corundum. SEM results showed that the samples were dense and the pore sizes were 5 μm~100μm, the grains were growth and development well, the grains size were 0.5μm~6μm. High reaction activity corundum and mullite were provided by calcined bauxite, then coupled with the role of feldspar, thus reduced the synthetic temperature of cordierite." @default.
- W2079553206 created "2016-06-24" @default.
- W2079553206 creator A5053331209 @default.
- W2079553206 creator A5059650976 @default.
- W2079553206 creator A5075242841 @default.
- W2079553206 creator A5090456481 @default.
- W2079553206 date "2013-09-01" @default.
- W2079553206 modified "2023-09-27" @default.
- W2079553206 title "Preparation and Mechanism of Cordierite by Using Calcined Bauxite as Raw Material at Relatively Low Temperature" @default.
- W2079553206 cites W1964637784 @default.
- W2079553206 cites W1983531871 @default.
- W2079553206 cites W1992475219 @default.
- W2079553206 cites W2016164675 @default.
- W2079553206 cites W2019072387 @default.
- W2079553206 cites W2041631190 @default.
- W2079553206 cites W2084307661 @default.
- W2079553206 doi "https://doi.org/10.4028/www.scientific.net/amr.785-786.1066" @default.
- W2079553206 hasPublicationYear "2013" @default.
- W2079553206 type Work @default.
- W2079553206 sameAs 2079553206 @default.
- W2079553206 citedByCount "0" @default.
- W2079553206 crossrefType "journal-article" @default.
- W2079553206 hasAuthorship W2079553206A5053331209 @default.
- W2079553206 hasAuthorship W2079553206A5059650976 @default.
- W2079553206 hasAuthorship W2079553206A5075242841 @default.
- W2079553206 hasAuthorship W2079553206A5090456481 @default.
- W2079553206 hasConcept C121332964 @default.
- W2079553206 hasConcept C127313418 @default.
- W2079553206 hasConcept C134132462 @default.
- W2079553206 hasConcept C153294291 @default.
- W2079553206 hasConcept C159985019 @default.
- W2079553206 hasConcept C161790260 @default.
- W2079553206 hasConcept C178790620 @default.
- W2079553206 hasConcept C185592680 @default.
- W2079553206 hasConcept C191897082 @default.
- W2079553206 hasConcept C192562407 @default.
- W2079553206 hasConcept C199289684 @default.
- W2079553206 hasConcept C206139338 @default.
- W2079553206 hasConcept C2776230739 @default.
- W2079553206 hasConcept C2776813687 @default.
- W2079553206 hasConcept C2777519835 @default.
- W2079553206 hasConcept C2777581544 @default.
- W2079553206 hasConcept C2778163720 @default.
- W2079553206 hasConcept C2779870107 @default.
- W2079553206 hasConcept C2781436864 @default.
- W2079553206 hasConcept C39353612 @default.
- W2079553206 hasConcept C55493867 @default.
- W2079553206 hasConcept C6648577 @default.
- W2079553206 hasConcept C7082614 @default.
- W2079553206 hasConceptScore W2079553206C121332964 @default.
- W2079553206 hasConceptScore W2079553206C127313418 @default.
- W2079553206 hasConceptScore W2079553206C134132462 @default.
- W2079553206 hasConceptScore W2079553206C153294291 @default.
- W2079553206 hasConceptScore W2079553206C159985019 @default.
- W2079553206 hasConceptScore W2079553206C161790260 @default.
- W2079553206 hasConceptScore W2079553206C178790620 @default.
- W2079553206 hasConceptScore W2079553206C185592680 @default.
- W2079553206 hasConceptScore W2079553206C191897082 @default.
- W2079553206 hasConceptScore W2079553206C192562407 @default.
- W2079553206 hasConceptScore W2079553206C199289684 @default.
- W2079553206 hasConceptScore W2079553206C206139338 @default.
- W2079553206 hasConceptScore W2079553206C2776230739 @default.
- W2079553206 hasConceptScore W2079553206C2776813687 @default.
- W2079553206 hasConceptScore W2079553206C2777519835 @default.
- W2079553206 hasConceptScore W2079553206C2777581544 @default.
- W2079553206 hasConceptScore W2079553206C2778163720 @default.
- W2079553206 hasConceptScore W2079553206C2779870107 @default.
- W2079553206 hasConceptScore W2079553206C2781436864 @default.
- W2079553206 hasConceptScore W2079553206C39353612 @default.
- W2079553206 hasConceptScore W2079553206C55493867 @default.
- W2079553206 hasConceptScore W2079553206C6648577 @default.
- W2079553206 hasConceptScore W2079553206C7082614 @default.
- W2079553206 hasLocation W20795532061 @default.
- W2079553206 hasOpenAccess W2079553206 @default.
- W2079553206 hasPrimaryLocation W20795532061 @default.
- W2079553206 hasRelatedWork W142561425 @default.
- W2079553206 hasRelatedWork W1986219864 @default.
- W2079553206 hasRelatedWork W1988880329 @default.
- W2079553206 hasRelatedWork W2011384262 @default.
- W2079553206 hasRelatedWork W2021908171 @default.
- W2079553206 hasRelatedWork W2031948255 @default.
- W2079553206 hasRelatedWork W2049570826 @default.
- W2079553206 hasRelatedWork W2079553206 @default.
- W2079553206 hasRelatedWork W2091078405 @default.
- W2079553206 hasRelatedWork W2803934826 @default.
- W2079553206 hasVolume "785-786" @default.
- W2079553206 isParatext "false" @default.
- W2079553206 isRetracted "false" @default.
- W2079553206 magId "2079553206" @default.
- W2079553206 workType "article" @default.