• W2080291944 abstract "The integrity of ceramic/metal joints is investigated under mechanically applied cyclic stresses using double-cantilever-beam, and compact-tension, sandwich test specimens. Specifically, fatigue-crack propagation rates for interfacial cracks are characterized over a range of velocities from 10 -9 to 10 -4 m/s for glass/copper and alumina/aluminum-alloy interfaces tested in moist air. Compared to corresponding (stress-corrosion) results under sustained loading, it is found that true interfacial cracks in glass-copper joints are significantly accelerated under cyclic loads. In addition, crack extension force (G) thresholds for interfacial crack growth under cyclic loads are some 46% lower than under sustained loads and are typically over six times lower than the interface toughness (Go). For the alumina/aluminum-alloy system, conversely, fracture never occurs in the interface; under monotonic loading cracking progresses near the interface in the ceramic layer whereas under cyclic loading failure may occur either in the ceramic or in the metal. Based on a comparison with fatigue-crack growth data in bulk alumina and bulk aluminum alloys, it is found that near interfacial crack-growth rates in the metal are much lower than those of the bulk ceramic and show a far higher dependency on the range of G than behavior in the bulk metal. Rfsumf----L'intfgrit6 des jonctions ma sous charge monotone; la fissuration progresse au voisinage de l'interface dans la couche de cframique, alors que sous charge cyclique, il peut y avoir rupture soit dans la cframique soit dans le mftal. En comparant les rfsultats concernant la croissance des fissures de fatigue dans de l'alumine massive d'une part et dans des alliages d'aluminium massifs de l'autre, on trouve que les vitesses de croissance des fissures proches de l'interface, dans le mftal, sont bien inffrieures ~i celles qu'on mesure dans la cframique massive, et qu'elles d6pendent bien plus de la gamme de G que dans le cas du mftal massif. Zusammenfassung--Die Best~indigkeit von Keramik-Metall-Verbindungen wird unter/iuBerer zyklischer Spannung im Umlauf-Biegeversuch und im Zugversuch an Sandwich-Proben untersucht. Insbesondere werden Ausbreitungsraten der Ermiidungsrisse an der Glas/Kupfer- und Aluminiumoxid/ Aluminiumlegierungs-Grenzflfiche im Bereich zwischen 10 -9 bis l0 -4 m/s in feuchter Luft gemessen. Im Vergleich zu entsprechenden (Spannungs-Korrosions-) Ergebnissen unter konstanter Spannung ergibt sich, dab die echten Grenzflfichenrisse in den Glas-Kupfer-Grenzfl~ichen unter zyklischer Spannung betrfichtlich schneller sind. AuBerdem ist die Schwelle der Ril3ausbreitungskraft G ffir Wachstum der Grenzfl/ichenrisse unter zyklischer Belastung etwa 46% niedriger als unter konstanter Last und typischw- erweise sechsmal geringer als die Grenzflfichenz~ihigkeit G c. Dagegen tritt bei dem System Aluminiu- moxid/Aluminiumlegierung Bruch niemals in der Grenzflfiche auf; unter monotoner Belastung schreitet die Ril3bildung in der Niihe der GRenzflfiche fort, dagegen unter zyklischer Belastung entweder in der Keramik oder in dem Metall. Aus einem Vergleich mit dem RiBverhalten im Volumen yon Aluminiumoxid oder der Legierung folgt, dab die Wachstumsraten der Risse in der N/ihe der Grenzfl/iche im Metall viel geringer sind als in Keramikvolumen und weitaus stiirker abh~ingen yon dem Bereich yon G als dem Verhalten im Metallvolumen." @default.
• W2080291944 created "2016-06-24" @default.
• W2080291944 creator A5029792207 @default.
• W2080291944 creator A5054566323 @default.
• W2080291944 creator A5061198627 @default.
• W2080291944 creator A5062068428 @default.
• W2080291944 creator A5065203509 @default.
• W2080291944 date "1991-09-01" @default.
• W2080291944 modified "2023-10-16" @default.
• W2080291944 title "Cyclic fatigue-crack propagation along ceramic/metal interfaces" @default.
• W2080291944 cites W1966529620 @default.
• W2080291944 cites W1973141381 @default.
• W2080291944 cites W1987416508 @default.
• W2080291944 cites W1991326949 @default.
• W2080291944 cites W2000733649 @default.
• W2080291944 cites W2000828375 @default.
• W2080291944 cites W2005621973 @default.
• W2080291944 cites W2006648350 @default.
• W2080291944 cites W2046239195 @default.
• W2080291944 cites W2060429465 @default.
• W2080291944 cites W2066442620 @default.
• W2080291944 cites W2090363099 @default.
• W2080291944 cites W2114423906 @default.
• W2080291944 cites W2146113645 @default.
• W2080291944 cites W2159749952 @default.
• W2080291944 cites W2162357431 @default.
• W2080291944 cites W4254126919 @default.
• W2080291944 doi "https://doi.org/10.1016/0956-7151(91)90184-3" @default.
• W2080291944 hasPublicationYear "1991" @default.
• W2080291944 type Work @default.
• W2080291944 sameAs 2080291944 @default.
• W2080291944 citedByCount "80" @default.
• W2080291944 countsByYear W20802919442012 @default.
• W2080291944 countsByYear W20802919442013 @default.
• W2080291944 countsByYear W20802919442014 @default.
• W2080291944 countsByYear W20802919442015 @default.
• W2080291944 countsByYear W20802919442016 @default.
• W2080291944 countsByYear W20802919442018 @default.
• W2080291944 countsByYear W20802919442019 @default.
• W2080291944 countsByYear W20802919442021 @default.
• W2080291944 countsByYear W20802919442023 @default.
• W2080291944 crossrefType "journal-article" @default.
• W2080291944 hasAuthorship W2080291944A5029792207 @default.
• W2080291944 hasAuthorship W2080291944A5054566323 @default.
• W2080291944 hasAuthorship W2080291944A5061198627 @default.
• W2080291944 hasAuthorship W2080291944A5062068428 @default.
• W2080291944 hasAuthorship W2080291944A5065203509 @default.
• W2080291944 hasConcept C134132462 @default.
• W2080291944 hasConcept C159985019 @default.
• W2080291944 hasConcept C191897082 @default.
• W2080291944 hasConcept C192562407 @default.
• W2080291944 hasConcept C544153396 @default.
• W2080291944 hasConcept C59085676 @default.
• W2080291944 hasConcept C61039299 @default.
• W2080291944 hasConceptScore W2080291944C134132462 @default.
• W2080291944 hasConceptScore W2080291944C159985019 @default.
• W2080291944 hasConceptScore W2080291944C191897082 @default.
• W2080291944 hasConceptScore W2080291944C192562407 @default.
• W2080291944 hasConceptScore W2080291944C544153396 @default.
• W2080291944 hasConceptScore W2080291944C59085676 @default.
• W2080291944 hasConceptScore W2080291944C61039299 @default.
• W2080291944 hasIssue "9" @default.
• W2080291944 hasLocation W20802919441 @default.
• W2080291944 hasOpenAccess W2080291944 @default.
• W2080291944 hasPrimaryLocation W20802919441 @default.
• W2080291944 hasRelatedWork W1963765618 @default.
• W2080291944 hasRelatedWork W1985201439 @default.
• W2080291944 hasRelatedWork W1985469821 @default.
• W2080291944 hasRelatedWork W2062108412 @default.
• W2080291944 hasRelatedWork W2084463405 @default.
• W2080291944 hasRelatedWork W2281145519 @default.
• W2080291944 hasRelatedWork W2366934632 @default.
• W2080291944 hasRelatedWork W2473372441 @default.
• W2080291944 hasRelatedWork W3082341486 @default.
• W2080291944 hasRelatedWork W4305082739 @default.
• W2080291944 hasVolume "39" @default.
• W2080291944 isParatext "false" @default.
• W2080291944 isRetracted "false" @default.
• W2080291944 magId "2080291944" @default.
• W2080291944 workType "article" @default.