- W2084682337 abstract "An approximate permanent strain of 0.3% was generated in Ce-TZP/alumina nanocomposite during static fatigue tests carried out at room temperature under ≈800 MPa for up to 106 s. For the deformed specimens, changes in the crystalline phase, ferroelastic domain orientation, and residual stresses were investigated. No evidence to support crystalline orientation due to ferroelasticity was observed. The monoclinic content of the deformed surface was determined to be 27 and 17 vol% by using small-area XRD and Raman spectroscopy, respectively. The estimated and experimental strains corresponding to the transformed monoclinic content were roughly in good agreement. A fairly high transformation zone and compressive residual stresses were observed up to 100 μm depth from the surface. Generated permanent strain and residual stresses disappeared completely upon annealing at 1100 °C. The obtained results revealed plastic deformation to be principally attributable to volume dilatation caused by t–m transformation and that it developed with residual strains." @default.
- W2084682337 created "2016-06-24" @default.
- W2084682337 creator A5022318994 @default.
- W2084682337 creator A5025379608 @default.
- W2084682337 creator A5032298702 @default.
- W2084682337 creator A5080849084 @default.
- W2084682337 date "2014-12-01" @default.
- W2084682337 modified "2023-09-28" @default.
- W2084682337 title "Transformation-induced plastic deformation in Ce-TZP/alumina nanocomposite generated during fatigue tests at room temperature" @default.
- W2084682337 cites W1606071295 @default.
- W2084682337 cites W1967600763 @default.
- W2084682337 cites W1980649443 @default.
- W2084682337 cites W1991336888 @default.
- W2084682337 cites W2003290679 @default.
- W2084682337 cites W2007337114 @default.
- W2084682337 cites W2010830411 @default.
- W2084682337 cites W2051925808 @default.
- W2084682337 cites W2054990670 @default.
- W2084682337 cites W2085240875 @default.
- W2084682337 cites W2087785560 @default.
- W2084682337 cites W2087974380 @default.
- W2084682337 cites W2120381938 @default.
- W2084682337 cites W2171587350 @default.
- W2084682337 cites W2316644488 @default.
- W2084682337 cites W2505787129 @default.
- W2084682337 doi "https://doi.org/10.1016/j.jeurceramsoc.2014.06.025" @default.
- W2084682337 hasPublicationYear "2014" @default.
- W2084682337 type Work @default.
- W2084682337 sameAs 2084682337 @default.
- W2084682337 citedByCount "10" @default.
- W2084682337 countsByYear W20846823372014 @default.
- W2084682337 countsByYear W20846823372016 @default.
- W2084682337 countsByYear W20846823372017 @default.
- W2084682337 countsByYear W20846823372018 @default.
- W2084682337 countsByYear W20846823372019 @default.
- W2084682337 countsByYear W20846823372023 @default.
- W2084682337 crossrefType "journal-article" @default.
- W2084682337 hasAuthorship W2084682337A5022318994 @default.
- W2084682337 hasAuthorship W2084682337A5025379608 @default.
- W2084682337 hasAuthorship W2084682337A5032298702 @default.
- W2084682337 hasAuthorship W2084682337A5080849084 @default.
- W2084682337 hasConcept C112413289 @default.
- W2084682337 hasConcept C115624301 @default.
- W2084682337 hasConcept C120665830 @default.
- W2084682337 hasConcept C121332964 @default.
- W2084682337 hasConcept C133386390 @default.
- W2084682337 hasConcept C159985019 @default.
- W2084682337 hasConcept C185592680 @default.
- W2084682337 hasConcept C192562407 @default.
- W2084682337 hasConcept C2777855556 @default.
- W2084682337 hasConcept C37292000 @default.
- W2084682337 hasConcept C40003534 @default.
- W2084682337 hasConcept C49040817 @default.
- W2084682337 hasConcept C61276311 @default.
- W2084682337 hasConcept C79090758 @default.
- W2084682337 hasConcept C8010536 @default.
- W2084682337 hasConcept C92880739 @default.
- W2084682337 hasConceptScore W2084682337C112413289 @default.
- W2084682337 hasConceptScore W2084682337C115624301 @default.
- W2084682337 hasConceptScore W2084682337C120665830 @default.
- W2084682337 hasConceptScore W2084682337C121332964 @default.
- W2084682337 hasConceptScore W2084682337C133386390 @default.
- W2084682337 hasConceptScore W2084682337C159985019 @default.
- W2084682337 hasConceptScore W2084682337C185592680 @default.
- W2084682337 hasConceptScore W2084682337C192562407 @default.
- W2084682337 hasConceptScore W2084682337C2777855556 @default.
- W2084682337 hasConceptScore W2084682337C37292000 @default.
- W2084682337 hasConceptScore W2084682337C40003534 @default.
- W2084682337 hasConceptScore W2084682337C49040817 @default.
- W2084682337 hasConceptScore W2084682337C61276311 @default.
- W2084682337 hasConceptScore W2084682337C79090758 @default.
- W2084682337 hasConceptScore W2084682337C8010536 @default.
- W2084682337 hasConceptScore W2084682337C92880739 @default.
- W2084682337 hasIssue "16" @default.
- W2084682337 hasLocation W20846823371 @default.
- W2084682337 hasOpenAccess W2084682337 @default.
- W2084682337 hasPrimaryLocation W20846823371 @default.
- W2084682337 hasRelatedWork W1972304764 @default.
- W2084682337 hasRelatedWork W2055011530 @default.
- W2084682337 hasRelatedWork W2170022756 @default.
- W2084682337 hasRelatedWork W2322906071 @default.
- W2084682337 hasRelatedWork W2323084632 @default.
- W2084682337 hasRelatedWork W2339889154 @default.
- W2084682337 hasRelatedWork W2396312082 @default.
- W2084682337 hasRelatedWork W2806697811 @default.
- W2084682337 hasRelatedWork W2896665349 @default.
- W2084682337 hasRelatedWork W4385652438 @default.
- W2084682337 hasVolume "34" @default.
- W2084682337 isParatext "false" @default.
- W2084682337 isRetracted "false" @default.
- W2084682337 magId "2084682337" @default.
- W2084682337 workType "article" @default.