- W2084913946 abstract "The aim of this study is to explore alloy 718 that treated at an optimal HIP process, and then imposed various solid-solution temperatures and aging treatment. The experimental results indicated that Laves and δ precipitations obviously appeared within the grain boundary, under HIP treatment and lower solid-solution temperatures (940°C), which would result in poor mechanical properties. However, Laves and δ phase can be completely dissolved at 1020°C 1 hour solid-solution treatment. The tensile strength was increased to 1331.5 MPa, and elongation reached up to 6.1% under a 1020°C solid-solution and aging treatment. Increasing the solid-solution temperature to 1060°C would cause parts of the NbC to dissolve, thus a large number of the thin sheet-shaped NbC would appear in the solid-solution and aging specimen. The yield stress is slight increase, but a lot of NbC precipitations will result in the decreasing tensile strength (1298.8 MPa) and elongation (5.4%). As a result, the optimal solid-solution treatment parameter of alloy 718 is 1020°C for 1-hour." @default.
- W2084913946 created "2016-06-24" @default.
- W2084913946 creator A5036697918 @default.
- W2084913946 creator A5045566537 @default.
- W2084913946 creator A5058485748 @default.
- W2084913946 creator A5073045264 @default.
- W2084913946 date "2011-10-01" @default.
- W2084913946 modified "2023-10-16" @default.
- W2084913946 title "Effects of Solid-Solution Treatment on Microstructure and Mechanical Properties of HIP Treated Alloy 718" @default.
- W2084913946 cites W1974354642 @default.
- W2084913946 cites W1977781910 @default.
- W2084913946 cites W2022152795 @default.
- W2084913946 cites W2045134508 @default.
- W2084913946 cites W2048758091 @default.
- W2084913946 cites W2057524668 @default.
- W2084913946 cites W2081345804 @default.
- W2084913946 cites W2500363960 @default.
- W2084913946 cites W2005224450 @default.
- W2084913946 doi "https://doi.org/10.4028/www.scientific.net/amm.117-119.1315" @default.
- W2084913946 hasPublicationYear "2011" @default.
- W2084913946 type Work @default.
- W2084913946 sameAs 2084913946 @default.
- W2084913946 citedByCount "3" @default.
- W2084913946 countsByYear W20849139462019 @default.
- W2084913946 countsByYear W20849139462022 @default.
- W2084913946 crossrefType "journal-article" @default.
- W2084913946 hasAuthorship W2084913946A5036697918 @default.
- W2084913946 hasAuthorship W2084913946A5045566537 @default.
- W2084913946 hasAuthorship W2084913946A5058485748 @default.
- W2084913946 hasAuthorship W2084913946A5073045264 @default.
- W2084913946 hasConcept C112950240 @default.
- W2084913946 hasConcept C138999460 @default.
- W2084913946 hasConcept C159985019 @default.
- W2084913946 hasConcept C191897082 @default.
- W2084913946 hasConcept C192562407 @default.
- W2084913946 hasConcept C193705005 @default.
- W2084913946 hasConcept C27501479 @default.
- W2084913946 hasConcept C2776878729 @default.
- W2084913946 hasConcept C2780026712 @default.
- W2084913946 hasConcept C33947775 @default.
- W2084913946 hasConcept C47908070 @default.
- W2084913946 hasConcept C87976508 @default.
- W2084913946 hasConceptScore W2084913946C112950240 @default.
- W2084913946 hasConceptScore W2084913946C138999460 @default.
- W2084913946 hasConceptScore W2084913946C159985019 @default.
- W2084913946 hasConceptScore W2084913946C191897082 @default.
- W2084913946 hasConceptScore W2084913946C192562407 @default.
- W2084913946 hasConceptScore W2084913946C193705005 @default.
- W2084913946 hasConceptScore W2084913946C27501479 @default.
- W2084913946 hasConceptScore W2084913946C2776878729 @default.
- W2084913946 hasConceptScore W2084913946C2780026712 @default.
- W2084913946 hasConceptScore W2084913946C33947775 @default.
- W2084913946 hasConceptScore W2084913946C47908070 @default.
- W2084913946 hasConceptScore W2084913946C87976508 @default.
- W2084913946 hasLocation W20849139461 @default.
- W2084913946 hasOpenAccess W2084913946 @default.
- W2084913946 hasPrimaryLocation W20849139461 @default.
- W2084913946 hasRelatedWork W1969394951 @default.
- W2084913946 hasRelatedWork W1987487801 @default.
- W2084913946 hasRelatedWork W1988943651 @default.
- W2084913946 hasRelatedWork W2349027603 @default.
- W2084913946 hasRelatedWork W2368738051 @default.
- W2084913946 hasRelatedWork W2369154548 @default.
- W2084913946 hasRelatedWork W2371235204 @default.
- W2084913946 hasRelatedWork W2394138227 @default.
- W2084913946 hasRelatedWork W2992625840 @default.
- W2084913946 hasRelatedWork W4297517326 @default.
- W2084913946 hasVolume "117-119" @default.
- W2084913946 isParatext "false" @default.
- W2084913946 isRetracted "false" @default.
- W2084913946 magId "2084913946" @default.
- W2084913946 workType "article" @default.