- W2085432873 abstract "Porous SiO2/carbon composites were fabricated by heating pellets composed of rice husk (RH) powders in small (<74 μm), medium(74–175 μm) and large(150–300 μm) sizes. The contents of the small RH were fixed at 30 mass% and the RH pellets molded at 10, 15, and 30 MPa were heated at 800–1150 °C in an inert atmosphere. The weight loss due to the thermal decomposition of the organic materials in the pellet peaked at 1000 °C, whereas the specimen heated at 1000 °C showed the lowest carbon content and density, 29 mass% and 0.40 g cm−3, respectively. The SiO2 phase of the specimens were amorphous at 800 and 1150 °C, but a cristobalite phase was visible at 1000 °C. The specimen fire at 1000 °C showed a higher compressive strength than the others, and the large RH particles were seen to increase the strength of the product while an increase in molding pressure decreased the medium pore size, from 17 to 7 μm, and increased the strength, from 0.25 to 3.52 MPa. The specific surface area (SSA) of the specimen peaked at 450 m2 g−1, at 1000 °C and finally, the mesopore size of the specimens was similar throughout, at ∼2 nm." @default.
- W2085432873 created "2016-06-24" @default.
- W2085432873 creator A5005178229 @default.
- W2085432873 creator A5018439905 @default.
- W2085432873 creator A5024360053 @default.
- W2085432873 creator A5053718032 @default.
- W2085432873 creator A5090240958 @default.
- W2085432873 date "2006-01-01" @default.
- W2085432873 modified "2023-10-03" @default.
- W2085432873 title "Fabrication of porous SiO2/C composite from rice husks" @default.
- W2085432873 cites W194163191 @default.
- W2085432873 cites W1981649435 @default.
- W2085432873 cites W1984110843 @default.
- W2085432873 cites W1987698464 @default.
- W2085432873 cites W2000713727 @default.
- W2085432873 cites W2019072387 @default.
- W2085432873 cites W2023791423 @default.
- W2085432873 cites W2159681363 @default.
- W2085432873 doi "https://doi.org/10.1016/j.jeurceramsoc.2005.06.013" @default.
- W2085432873 hasPublicationYear "2006" @default.
- W2085432873 type Work @default.
- W2085432873 sameAs 2085432873 @default.
- W2085432873 citedByCount "34" @default.
- W2085432873 countsByYear W20854328732012 @default.
- W2085432873 countsByYear W20854328732013 @default.
- W2085432873 countsByYear W20854328732014 @default.
- W2085432873 countsByYear W20854328732015 @default.
- W2085432873 countsByYear W20854328732016 @default.
- W2085432873 countsByYear W20854328732017 @default.
- W2085432873 countsByYear W20854328732018 @default.
- W2085432873 countsByYear W20854328732019 @default.
- W2085432873 countsByYear W20854328732021 @default.
- W2085432873 countsByYear W20854328732022 @default.
- W2085432873 countsByYear W20854328732023 @default.
- W2085432873 crossrefType "journal-article" @default.
- W2085432873 hasAuthorship W2085432873A5005178229 @default.
- W2085432873 hasAuthorship W2085432873A5018439905 @default.
- W2085432873 hasAuthorship W2085432873A5024360053 @default.
- W2085432873 hasAuthorship W2085432873A5053718032 @default.
- W2085432873 hasAuthorship W2085432873A5090240958 @default.
- W2085432873 hasConcept C104779481 @default.
- W2085432873 hasConcept C140205800 @default.
- W2085432873 hasConcept C150581940 @default.
- W2085432873 hasConcept C159985019 @default.
- W2085432873 hasConcept C160434732 @default.
- W2085432873 hasConcept C161790260 @default.
- W2085432873 hasConcept C178790620 @default.
- W2085432873 hasConcept C17923525 @default.
- W2085432873 hasConcept C185592680 @default.
- W2085432873 hasConcept C192562407 @default.
- W2085432873 hasConcept C2779870107 @default.
- W2085432873 hasConcept C2780490245 @default.
- W2085432873 hasConcept C2780584874 @default.
- W2085432873 hasConcept C30407753 @default.
- W2085432873 hasConcept C44280652 @default.
- W2085432873 hasConcept C55493867 @default.
- W2085432873 hasConcept C55766333 @default.
- W2085432873 hasConcept C56052488 @default.
- W2085432873 hasConcept C59822182 @default.
- W2085432873 hasConcept C6648577 @default.
- W2085432873 hasConcept C75296557 @default.
- W2085432873 hasConcept C86803240 @default.
- W2085432873 hasConceptScore W2085432873C104779481 @default.
- W2085432873 hasConceptScore W2085432873C140205800 @default.
- W2085432873 hasConceptScore W2085432873C150581940 @default.
- W2085432873 hasConceptScore W2085432873C159985019 @default.
- W2085432873 hasConceptScore W2085432873C160434732 @default.
- W2085432873 hasConceptScore W2085432873C161790260 @default.
- W2085432873 hasConceptScore W2085432873C178790620 @default.
- W2085432873 hasConceptScore W2085432873C17923525 @default.
- W2085432873 hasConceptScore W2085432873C185592680 @default.
- W2085432873 hasConceptScore W2085432873C192562407 @default.
- W2085432873 hasConceptScore W2085432873C2779870107 @default.
- W2085432873 hasConceptScore W2085432873C2780490245 @default.
- W2085432873 hasConceptScore W2085432873C2780584874 @default.
- W2085432873 hasConceptScore W2085432873C30407753 @default.
- W2085432873 hasConceptScore W2085432873C44280652 @default.
- W2085432873 hasConceptScore W2085432873C55493867 @default.
- W2085432873 hasConceptScore W2085432873C55766333 @default.
- W2085432873 hasConceptScore W2085432873C56052488 @default.
- W2085432873 hasConceptScore W2085432873C59822182 @default.
- W2085432873 hasConceptScore W2085432873C6648577 @default.
- W2085432873 hasConceptScore W2085432873C75296557 @default.
- W2085432873 hasConceptScore W2085432873C86803240 @default.
- W2085432873 hasFunder F4320320907 @default.
- W2085432873 hasIssue "4-5" @default.
- W2085432873 hasLocation W20854328731 @default.
- W2085432873 hasOpenAccess W2085432873 @default.
- W2085432873 hasPrimaryLocation W20854328731 @default.
- W2085432873 hasRelatedWork W2005496670 @default.
- W2085432873 hasRelatedWork W2022856623 @default.
- W2085432873 hasRelatedWork W2048186367 @default.
- W2085432873 hasRelatedWork W2068690720 @default.
- W2085432873 hasRelatedWork W2946287956 @default.
- W2085432873 hasRelatedWork W2954617748 @default.
- W2085432873 hasRelatedWork W3196940922 @default.
- W2085432873 hasRelatedWork W4250644067 @default.
- W2085432873 hasRelatedWork W4307710227 @default.