- W2085748110 abstract "Abstract Tensile specimens of 9Cr–1Mo (EM10) and mod 9Cr–1Mo (T91) martensitic steels in the normalized and tempered metallurgical conditions were irradiated with high energy protons and neutrons up to 20 dpa at average temperatures up to about 360 °C. Tensile tests were carried out at room temperature and 250 °C and a few samples were tested at 350 °C. The fracture surfaces of selected specimens were characterized by Scanning Electron Microscopy (SEM). While all irradiated specimens displayed at room temperature considerable hardening and loss of ductility, those irradiated to doses above approximately 16 dpa exhibited a fully brittle behaviour and the SEM observations revealed significant amounts of intergranular fracture. Helium accumulation, up to about 0.18 at.% in the specimens irradiated to 20 dpa, is believed to be one of the main factors which triggered the brittle behaviour and intergranular fracture mode. One EM10 and one T91 specimen irradiated to 20 dpa were annealed at 700 °C for 1 h following irradiation and subsequently tensile tested. In both cases, a remarkable recovery of ductility and strain-hardening capacity was observed after annealing, while the strength remained significantly above that of the unirradiated material." @default.
- W2085748110 created "2016-06-24" @default.
- W2085748110 creator A5010205416 @default.
- W2085748110 creator A5018787253 @default.
- W2085748110 creator A5044029236 @default.
- W2085748110 creator A5078701812 @default.
- W2085748110 date "2008-06-01" @default.
- W2085748110 modified "2023-10-16" @default.
- W2085748110 title "Tensile behaviour of 9Cr–1Mo tempered martensitic steels irradiated up to 20dpa in a spallation environment" @default.
- W2085748110 cites W1970406703 @default.
- W2085748110 cites W1975556723 @default.
- W2085748110 cites W1993796768 @default.
- W2085748110 cites W2025966927 @default.
- W2085748110 cites W2028098852 @default.
- W2085748110 cites W2040572614 @default.
- W2085748110 cites W2049498744 @default.
- W2085748110 cites W2076991165 @default.
- W2085748110 cites W2083417772 @default.
- W2085748110 doi "https://doi.org/10.1016/j.jnucmat.2008.02.027" @default.
- W2085748110 hasPublicationYear "2008" @default.
- W2085748110 type Work @default.
- W2085748110 sameAs 2085748110 @default.
- W2085748110 citedByCount "16" @default.
- W2085748110 countsByYear W20857481102012 @default.
- W2085748110 countsByYear W20857481102013 @default.
- W2085748110 countsByYear W20857481102014 @default.
- W2085748110 countsByYear W20857481102017 @default.
- W2085748110 countsByYear W20857481102018 @default.
- W2085748110 countsByYear W20857481102019 @default.
- W2085748110 countsByYear W20857481102020 @default.
- W2085748110 countsByYear W20857481102022 @default.
- W2085748110 countsByYear W20857481102023 @default.
- W2085748110 crossrefType "journal-article" @default.
- W2085748110 hasAuthorship W2085748110A5010205416 @default.
- W2085748110 hasAuthorship W2085748110A5018787253 @default.
- W2085748110 hasAuthorship W2085748110A5044029236 @default.
- W2085748110 hasAuthorship W2085748110A5078701812 @default.
- W2085748110 hasBestOaLocation W20857481102 @default.
- W2085748110 hasConcept C111337013 @default.
- W2085748110 hasConcept C112950240 @default.
- W2085748110 hasConcept C11608111 @default.
- W2085748110 hasConcept C121332964 @default.
- W2085748110 hasConcept C152568617 @default.
- W2085748110 hasConcept C159985019 @default.
- W2085748110 hasConcept C185544564 @default.
- W2085748110 hasConcept C18747287 @default.
- W2085748110 hasConcept C191897082 @default.
- W2085748110 hasConcept C192562407 @default.
- W2085748110 hasConcept C87976508 @default.
- W2085748110 hasConceptScore W2085748110C111337013 @default.
- W2085748110 hasConceptScore W2085748110C112950240 @default.
- W2085748110 hasConceptScore W2085748110C11608111 @default.
- W2085748110 hasConceptScore W2085748110C121332964 @default.
- W2085748110 hasConceptScore W2085748110C152568617 @default.
- W2085748110 hasConceptScore W2085748110C159985019 @default.
- W2085748110 hasConceptScore W2085748110C185544564 @default.
- W2085748110 hasConceptScore W2085748110C18747287 @default.
- W2085748110 hasConceptScore W2085748110C191897082 @default.
- W2085748110 hasConceptScore W2085748110C192562407 @default.
- W2085748110 hasConceptScore W2085748110C87976508 @default.
- W2085748110 hasIssue "1" @default.
- W2085748110 hasLocation W20857481101 @default.
- W2085748110 hasLocation W20857481102 @default.
- W2085748110 hasLocation W20857481103 @default.
- W2085748110 hasLocation W20857481104 @default.
- W2085748110 hasOpenAccess W2085748110 @default.
- W2085748110 hasPrimaryLocation W20857481101 @default.
- W2085748110 hasRelatedWork W1545496076 @default.
- W2085748110 hasRelatedWork W1975608897 @default.
- W2085748110 hasRelatedWork W1997159941 @default.
- W2085748110 hasRelatedWork W2044949441 @default.
- W2085748110 hasRelatedWork W2332396214 @default.
- W2085748110 hasRelatedWork W2387616028 @default.
- W2085748110 hasRelatedWork W2531393654 @default.
- W2085748110 hasRelatedWork W2795554382 @default.
- W2085748110 hasRelatedWork W3122552578 @default.
- W2085748110 hasRelatedWork W4285731133 @default.
- W2085748110 hasVolume "377" @default.
- W2085748110 isParatext "false" @default.
- W2085748110 isRetracted "false" @default.
- W2085748110 magId "2085748110" @default.
- W2085748110 workType "article" @default.