• W2087737572 abstract "The effects of test environment humidity and temperature on the fatigue threshold and crack growth behavior of P2-etched and commercial coil-coated (CC) aluminum adhesive joints were studied under mixed-mode loading using aluminum asymmetric double cantilever beam (ADCB) specimens. Under dry conditions, increasing the temperature to 80 °C had an insignificant effect on the fatigue threshold, but caused an increase in the crack growth rates. At 40 °C, the fatigue behavior was insensitive to moisture at higher crack growth rates, but became sensitive to moisture level in the test environment as crack growth rates slowed to the threshold. The effect of moisture and temperature were explained by the observed changes in the crack path, which in general moved progressively closer to the more highly-strained adherend as the applied strain energy release rate, and consequently the crack growth rate, decreased. Furthermore, the residual adhesive thickness on the more highly-strained adherend, tr, increased with increasing temperature, and the crack path shifted to the hydrated aluminum oxide interface when the test environment was saturated with moisture. The degrading effect of a hot-wet environment was similar for both P2-etch and CC pretreatments. At higher crack growth rates, the joint fatigue performance was degraded solely due to the effect of the increased temperature, whereas at low crack growth rates, the fatigue performance was degraded predominantly because of elevated moisture." @default.
• W2087737572 created "2016-06-24" @default.
• W2087737572 creator A5033724493 @default.
• W2087737572 creator A5044118850 @default.
• W2087737572 creator A5074956473 @default.
• W2087737572 creator A5076784900 @default.
• W2087737572 creator A5079580602 @default.
• W2087737572 date "2011-04-01" @default.
• W2087737572 modified "2023-09-25" @default.
• W2087737572 title "The effects of test temperature and humidity on the mixed-mode fatigue behavior of a toughened adhesive aluminum joint" @default.
• W2087737572 cites W1490561883 @default.
• W2087737572 cites W1549923431 @default.
• W2087737572 cites W1965675594 @default.
• W2087737572 cites W1979503194 @default.
• W2087737572 cites W1986527725 @default.
• W2087737572 cites W1987416508 @default.
• W2087737572 cites W1991336169 @default.
• W2087737572 cites W1994395058 @default.
• W2087737572 cites W2003662813 @default.
• W2087737572 cites W2007246988 @default.
• W2087737572 cites W2012364380 @default.
• W2087737572 cites W2013026484 @default.
• W2087737572 cites W2018976384 @default.
• W2087737572 cites W2023920265 @default.
• W2087737572 cites W2038292995 @default.
• W2087737572 cites W2038390211 @default.
• W2087737572 cites W2046418402 @default.
• W2087737572 cites W2048180305 @default.
• W2087737572 cites W2056456534 @default.
• W2087737572 cites W2074807190 @default.
• W2087737572 cites W2076104510 @default.
• W2087737572 cites W2082935420 @default.
• W2087737572 cites W2088556778 @default.
• W2087737572 cites W2116806944 @default.
• W2087737572 cites W2117669255 @default.
• W2087737572 cites W2121247028 @default.
• W2087737572 cites W2162991610 @default.
• W2087737572 cites W2168405852 @default.
• W2087737572 cites W2169907762 @default.
• W2087737572 doi "https://doi.org/10.1016/j.engfracmech.2011.01.028" @default.
• W2087737572 hasPublicationYear "2011" @default.
• W2087737572 type Work @default.
• W2087737572 sameAs 2087737572 @default.
• W2087737572 citedByCount "45" @default.
• W2087737572 countsByYear W20877375722012 @default.
• W2087737572 countsByYear W20877375722013 @default.
• W2087737572 countsByYear W20877375722014 @default.
• W2087737572 countsByYear W20877375722015 @default.
• W2087737572 countsByYear W20877375722016 @default.
• W2087737572 countsByYear W20877375722017 @default.
• W2087737572 countsByYear W20877375722018 @default.
• W2087737572 countsByYear W20877375722020 @default.
• W2087737572 countsByYear W20877375722021 @default.
• W2087737572 countsByYear W20877375722022 @default.
• W2087737572 countsByYear W20877375722023 @default.
• W2087737572 crossrefType "journal-article" @default.
• W2087737572 hasAuthorship W2087737572A5033724493 @default.
• W2087737572 hasAuthorship W2087737572A5044118850 @default.
• W2087737572 hasAuthorship W2087737572A5074956473 @default.
• W2087737572 hasAuthorship W2087737572A5076784900 @default.
• W2087737572 hasAuthorship W2087737572A5079580602 @default.
• W2087737572 hasConcept C121332964 @default.
• W2087737572 hasConcept C127413603 @default.
• W2087737572 hasConcept C151420433 @default.
• W2087737572 hasConcept C159985019 @default.
• W2087737572 hasConcept C176864760 @default.
• W2087737572 hasConcept C18555067 @default.
• W2087737572 hasConcept C192562407 @default.
• W2087737572 hasConcept C2524010 @default.
• W2087737572 hasConcept C2778312390 @default.
• W2087737572 hasConcept C2779227376 @default.
• W2087737572 hasConcept C33923547 @default.
• W2087737572 hasConcept C513153333 @default.
• W2087737572 hasConcept C59085676 @default.
• W2087737572 hasConcept C66938386 @default.
• W2087737572 hasConcept C68928338 @default.
• W2087737572 hasConcept C69809600 @default.
• W2087737572 hasConcept C75512024 @default.
• W2087737572 hasConcept C97355855 @default.
• W2087737572 hasConceptScore W2087737572C121332964 @default.
• W2087737572 hasConceptScore W2087737572C127413603 @default.
• W2087737572 hasConceptScore W2087737572C151420433 @default.
• W2087737572 hasConceptScore W2087737572C159985019 @default.
• W2087737572 hasConceptScore W2087737572C176864760 @default.
• W2087737572 hasConceptScore W2087737572C18555067 @default.
• W2087737572 hasConceptScore W2087737572C192562407 @default.
• W2087737572 hasConceptScore W2087737572C2524010 @default.
• W2087737572 hasConceptScore W2087737572C2778312390 @default.
• W2087737572 hasConceptScore W2087737572C2779227376 @default.
• W2087737572 hasConceptScore W2087737572C33923547 @default.
• W2087737572 hasConceptScore W2087737572C513153333 @default.
• W2087737572 hasConceptScore W2087737572C59085676 @default.
• W2087737572 hasConceptScore W2087737572C66938386 @default.
• W2087737572 hasConceptScore W2087737572C68928338 @default.
• W2087737572 hasConceptScore W2087737572C69809600 @default.
• W2087737572 hasConceptScore W2087737572C75512024 @default.
• W2087737572 hasConceptScore W2087737572C97355855 @default.
• W2087737572 hasIssue "6" @default.

• next