- W2087897294 abstract "Melamine and melamine resins are widely used as fire-retardants for polymer building materials. Cured melamine systems are used in heat-sensitive items, such as furniture and window frames and sills. In this work, differently cured methylated poly(melamine-co-formaldehyde) (cmPMF) resins were used as fire-retardant coverage for poly(styrene) (PS) and poly(ethylene) (PE) building materials. Such polymer layers should have several tenths of micrometers thickness to produce sufficient fire retardancy. These thick layers were produced by dip-coating. To promote sufficient adhesion of such thick coating to the polyolefin substrates, also in the case of high temperatures occurring at fire exposure, the polymer substrates were firstly coated with a few hundred nanometer thick adhesion-promoting plasma polymer layer. Such thin plasma polymer layers were deposited by low-pressure plasma polymerization of allyl alcohol (ppAAl). It was assumed that the hydroxyl groups of ppAAl interact with the melamine resin; therefore, ppAAl was well suited as adhesion promoter for thick melamine resin coatings. Chemical structure and composition of polymer films were investigated using infrared-attenuated total reflectance and X-ray photoelectron spectroscopy (XPS). Peel strengths of coatings were measured. After peeling, the peeled polymer surfaces were also investigated using optical microscopy and XPS the layers for identification of the locus of peel front propagation. Thermal properties were analyzed using TGA (thermo-gravimetric analyses). Finally, the fire-retardant properties of such thick coated polymers were evaluated by exposure to flames." @default.
- W2087897294 created "2016-06-24" @default.
- W2087897294 creator A5060729177 @default.
- W2087897294 creator A5071005044 @default.
- W2087897294 creator A5071842735 @default.
- W2087897294 date "2015-02-06" @default.
- W2087897294 modified "2023-09-30" @default.
- W2087897294 title "Cured melamine systems as thick fire-retardant layers deposited by combination of plasma technology and dip-coating" @default.
- W2087897294 cites W1971032876 @default.
- W2087897294 cites W1994011571 @default.
- W2087897294 cites W2007440393 @default.
- W2087897294 cites W2017426137 @default.
- W2087897294 cites W2032640677 @default.
- W2087897294 cites W2051059298 @default.
- W2087897294 cites W2052162051 @default.
- W2087897294 cites W2058772079 @default.
- W2087897294 cites W2079071691 @default.
- W2087897294 cites W2081602673 @default.
- W2087897294 cites W2096867121 @default.
- W2087897294 cites W2966860231 @default.
- W2087897294 doi "https://doi.org/10.1080/01694243.2014.995911" @default.
- W2087897294 hasPublicationYear "2015" @default.
- W2087897294 type Work @default.
- W2087897294 sameAs 2087897294 @default.
- W2087897294 citedByCount "7" @default.
- W2087897294 countsByYear W20878972942017 @default.
- W2087897294 countsByYear W20878972942020 @default.
- W2087897294 countsByYear W20878972942022 @default.
- W2087897294 countsByYear W20878972942023 @default.
- W2087897294 crossrefType "journal-article" @default.
- W2087897294 hasAuthorship W2087897294A5060729177 @default.
- W2087897294 hasAuthorship W2087897294A5071005044 @default.
- W2087897294 hasAuthorship W2087897294A5071842735 @default.
- W2087897294 hasConcept C115545448 @default.
- W2087897294 hasConcept C127413603 @default.
- W2087897294 hasConcept C159985019 @default.
- W2087897294 hasConcept C175708663 @default.
- W2087897294 hasConcept C192562407 @default.
- W2087897294 hasConcept C205474432 @default.
- W2087897294 hasConcept C2775979504 @default.
- W2087897294 hasConcept C2778393666 @default.
- W2087897294 hasConcept C2781448156 @default.
- W2087897294 hasConcept C42360764 @default.
- W2087897294 hasConcept C44228677 @default.
- W2087897294 hasConcept C521977710 @default.
- W2087897294 hasConcept C60100273 @default.
- W2087897294 hasConceptScore W2087897294C115545448 @default.
- W2087897294 hasConceptScore W2087897294C127413603 @default.
- W2087897294 hasConceptScore W2087897294C159985019 @default.
- W2087897294 hasConceptScore W2087897294C175708663 @default.
- W2087897294 hasConceptScore W2087897294C192562407 @default.
- W2087897294 hasConceptScore W2087897294C205474432 @default.
- W2087897294 hasConceptScore W2087897294C2775979504 @default.
- W2087897294 hasConceptScore W2087897294C2778393666 @default.
- W2087897294 hasConceptScore W2087897294C2781448156 @default.
- W2087897294 hasConceptScore W2087897294C42360764 @default.
- W2087897294 hasConceptScore W2087897294C44228677 @default.
- W2087897294 hasConceptScore W2087897294C521977710 @default.
- W2087897294 hasConceptScore W2087897294C60100273 @default.
- W2087897294 hasIssue "9" @default.
- W2087897294 hasLocation W20878972941 @default.
- W2087897294 hasOpenAccess W2087897294 @default.
- W2087897294 hasPrimaryLocation W20878972941 @default.
- W2087897294 hasRelatedWork W1991028458 @default.
- W2087897294 hasRelatedWork W1996117009 @default.
- W2087897294 hasRelatedWork W2038188137 @default.
- W2087897294 hasRelatedWork W2146713126 @default.
- W2087897294 hasRelatedWork W2159306309 @default.
- W2087897294 hasRelatedWork W2348823480 @default.
- W2087897294 hasRelatedWork W2384384972 @default.
- W2087897294 hasRelatedWork W2386402034 @default.
- W2087897294 hasRelatedWork W2621108856 @default.
- W2087897294 hasRelatedWork W2766497033 @default.
- W2087897294 hasVolume "29" @default.
- W2087897294 isParatext "false" @default.
- W2087897294 isRetracted "false" @default.
- W2087897294 magId "2087897294" @default.
- W2087897294 workType "article" @default.