- W2088070542 abstract "We report the results of the improved surface passivation of GaAs using Al2O3 films deposited by the e-beam evaporation technique. A low and stable density of the negative fixed interface charge density of ~1 × 1010 cm−2 and the fast interface state density of <3 × 1011 cm−2 eV−1 were obtained for the said films. Furthermore, using dc I–V measurements near zero bias, the typical leakage currents varying from 4 to 90 pA range were measured. The lowest near zero bias current was 0.5 pA which indicates a resistivity of 3.6 × 1011 Ω cm for our Al2O3 films, which is comparable to the values reported in the literature. To assess the uniformity of these films, a large number of devices from the 2 inch wafer were measured. It was observed that in general the shape of C–V curves remains the same except that there is only a 15% variation in accumulation capacitance across the whole wafer. This suggests a variation of dielectric constant from 4 to 4.5, which is indicative of acceptable film uniformity. Similarly, resistivity varied by three orders of magnitude from ~3.0 × 108 to ~3 × 1011 Ω cm." @default.
- W2088070542 created "2016-06-24" @default.
- W2088070542 creator A5037182934 @default.
- W2088070542 creator A5049500711 @default.
- W2088070542 creator A5051011002 @default.
- W2088070542 creator A5058953121 @default.
- W2088070542 creator A5081415034 @default.
- W2088070542 date "2008-01-15" @default.
- W2088070542 modified "2023-09-26" @default.
- W2088070542 title "Improved interface properties of Al2O3 optical coatings on GaAs deposited by e-beam" @default.
- W2088070542 cites W1616230297 @default.
- W2088070542 cites W1986331063 @default.
- W2088070542 cites W2003645630 @default.
- W2088070542 cites W2057568606 @default.
- W2088070542 cites W2074998815 @default.
- W2088070542 cites W2105042971 @default.
- W2088070542 doi "https://doi.org/10.1088/0268-1242/23/2/025017" @default.
- W2088070542 hasPublicationYear "2008" @default.
- W2088070542 type Work @default.
- W2088070542 sameAs 2088070542 @default.
- W2088070542 citedByCount "1" @default.
- W2088070542 crossrefType "journal-article" @default.
- W2088070542 hasAuthorship W2088070542A5037182934 @default.
- W2088070542 hasAuthorship W2088070542A5049500711 @default.
- W2088070542 hasAuthorship W2088070542A5051011002 @default.
- W2088070542 hasAuthorship W2088070542A5058953121 @default.
- W2088070542 hasAuthorship W2088070542A5081415034 @default.
- W2088070542 hasConcept C113843644 @default.
- W2088070542 hasConcept C120665830 @default.
- W2088070542 hasConcept C121332964 @default.
- W2088070542 hasConcept C159985019 @default.
- W2088070542 hasConcept C168834538 @default.
- W2088070542 hasConcept C192562407 @default.
- W2088070542 hasConcept C196806460 @default.
- W2088070542 hasConcept C28413391 @default.
- W2088070542 hasConcept C49040817 @default.
- W2088070542 hasConceptScore W2088070542C113843644 @default.
- W2088070542 hasConceptScore W2088070542C120665830 @default.
- W2088070542 hasConceptScore W2088070542C121332964 @default.
- W2088070542 hasConceptScore W2088070542C159985019 @default.
- W2088070542 hasConceptScore W2088070542C168834538 @default.
- W2088070542 hasConceptScore W2088070542C192562407 @default.
- W2088070542 hasConceptScore W2088070542C196806460 @default.
- W2088070542 hasConceptScore W2088070542C28413391 @default.
- W2088070542 hasConceptScore W2088070542C49040817 @default.
- W2088070542 hasIssue "2" @default.
- W2088070542 hasLocation W20880705421 @default.
- W2088070542 hasOpenAccess W2088070542 @default.
- W2088070542 hasPrimaryLocation W20880705421 @default.
- W2088070542 hasRelatedWork W1999421104 @default.
- W2088070542 hasRelatedWork W2006094476 @default.
- W2088070542 hasRelatedWork W2008764437 @default.
- W2088070542 hasRelatedWork W2058676402 @default.
- W2088070542 hasRelatedWork W2063061226 @default.
- W2088070542 hasRelatedWork W2137687570 @default.
- W2088070542 hasRelatedWork W2290864281 @default.
- W2088070542 hasRelatedWork W2329285141 @default.
- W2088070542 hasRelatedWork W2902546961 @default.
- W2088070542 hasRelatedWork W4313653414 @default.
- W2088070542 hasVolume "23" @default.
- W2088070542 isParatext "false" @default.
- W2088070542 isRetracted "false" @default.
- W2088070542 magId "2088070542" @default.
- W2088070542 workType "article" @default.