- W2089315512 abstract "Sub-micron and nano-sized β-SiC powders were sintered with AlN and Y2O3 as sintering additives by spark plasma sintering (SPS). The sintered densities reached >95% of theoretical with a different molar ratio of AlN to Y2O3 at total amount of 10vol% and temperature of 1900oC for 10min in N2 atmosphere under a pressure of 30MPa. With increasing amount of the AlN additive, the size of SiC grains decreased and the shape changed from globular to columnar. The fully densified SiC at AlN:Y2O3=95:5mol% had an average grain size of 0.5-1µm and 50-100nm in diameter by using sub-micron and nano-sized SiC starting powders, respectively. Flexural strength of the specimen having grain size of 0.5-1µm was approximately 1200MPa at room temperature." @default.
- W2089315512 created "2016-06-24" @default.
- W2089315512 creator A5041032986 @default.
- W2089315512 creator A5091344358 @default.
- W2089315512 date "2006-03-01" @default.
- W2089315512 modified "2023-10-10" @default.
- W2089315512 title "Microstructural Development of SiC Ceramics by Liquid-Phase Sintering with Spark Plasma Sintering Technique" @default.
- W2089315512 cites W1973573946 @default.
- W2089315512 cites W1988399868 @default.
- W2089315512 cites W1997993839 @default.
- W2089315512 cites W2007533679 @default.
- W2089315512 cites W2022776420 @default.
- W2089315512 cites W2069248168 @default.
- W2089315512 cites W2106560049 @default.
- W2089315512 cites W2133565104 @default.
- W2089315512 doi "https://doi.org/10.4028/www.scientific.net/msf.510-511.1022" @default.
- W2089315512 hasPublicationYear "2006" @default.
- W2089315512 type Work @default.
- W2089315512 sameAs 2089315512 @default.
- W2089315512 citedByCount "4" @default.
- W2089315512 countsByYear W20893155122014 @default.
- W2089315512 crossrefType "journal-article" @default.
- W2089315512 hasAuthorship W2089315512A5041032986 @default.
- W2089315512 hasAuthorship W2089315512A5091344358 @default.
- W2089315512 hasConcept C121332964 @default.
- W2089315512 hasConcept C134132462 @default.
- W2089315512 hasConcept C159985019 @default.
- W2089315512 hasConcept C161790260 @default.
- W2089315512 hasConcept C178405089 @default.
- W2089315512 hasConcept C178790620 @default.
- W2089315512 hasConcept C185592680 @default.
- W2089315512 hasConcept C191897082 @default.
- W2089315512 hasConcept C192191005 @default.
- W2089315512 hasConcept C192562407 @default.
- W2089315512 hasConcept C2776014600 @default.
- W2089315512 hasConcept C2777581544 @default.
- W2089315512 hasConcept C2780357685 @default.
- W2089315512 hasConcept C2994067411 @default.
- W2089315512 hasConcept C3020315061 @default.
- W2089315512 hasConcept C44280652 @default.
- W2089315512 hasConcept C55493867 @default.
- W2089315512 hasConcept C97355855 @default.
- W2089315512 hasConcept C98390173 @default.
- W2089315512 hasConceptScore W2089315512C121332964 @default.
- W2089315512 hasConceptScore W2089315512C134132462 @default.
- W2089315512 hasConceptScore W2089315512C159985019 @default.
- W2089315512 hasConceptScore W2089315512C161790260 @default.
- W2089315512 hasConceptScore W2089315512C178405089 @default.
- W2089315512 hasConceptScore W2089315512C178790620 @default.
- W2089315512 hasConceptScore W2089315512C185592680 @default.
- W2089315512 hasConceptScore W2089315512C191897082 @default.
- W2089315512 hasConceptScore W2089315512C192191005 @default.
- W2089315512 hasConceptScore W2089315512C192562407 @default.
- W2089315512 hasConceptScore W2089315512C2776014600 @default.
- W2089315512 hasConceptScore W2089315512C2777581544 @default.
- W2089315512 hasConceptScore W2089315512C2780357685 @default.
- W2089315512 hasConceptScore W2089315512C2994067411 @default.
- W2089315512 hasConceptScore W2089315512C3020315061 @default.
- W2089315512 hasConceptScore W2089315512C44280652 @default.
- W2089315512 hasConceptScore W2089315512C55493867 @default.
- W2089315512 hasConceptScore W2089315512C97355855 @default.
- W2089315512 hasConceptScore W2089315512C98390173 @default.
- W2089315512 hasLocation W20893155121 @default.
- W2089315512 hasOpenAccess W2089315512 @default.
- W2089315512 hasPrimaryLocation W20893155121 @default.
- W2089315512 hasRelatedWork W1494274803 @default.
- W2089315512 hasRelatedWork W1586485836 @default.
- W2089315512 hasRelatedWork W2001288410 @default.
- W2089315512 hasRelatedWork W2059271568 @default.
- W2089315512 hasRelatedWork W2064411628 @default.
- W2089315512 hasRelatedWork W2099632912 @default.
- W2089315512 hasRelatedWork W2244538170 @default.
- W2089315512 hasRelatedWork W2384445010 @default.
- W2089315512 hasRelatedWork W2534137123 @default.
- W2089315512 hasRelatedWork W2992606064 @default.
- W2089315512 hasVolume "510-511" @default.
- W2089315512 isParatext "false" @default.
- W2089315512 isRetracted "false" @default.
- W2089315512 magId "2089315512" @default.
- W2089315512 workType "article" @default.