- W2091092115 abstract "The lattice imperfections in GaAs single crystals introduced as a result of the in-diffusion of lithium at high temperatures were investigated by using transmission electron microscopy. The effects of diffusion temperature, time, postdiffusion annealing treatments, and the presence of other impurities (primarily Zn at concentration levels of 1×1019 cm−3) in the host crystal, on the defect structure have been determined. The results indicate that when Li-saturated GaAs single crystals are cooled to room temperature following high-temperature diffusion, precipitation of Li occurs readily in the form of tetrahedral particles, the size and density of which decrease with decreases in diffusion temperature. Postdiffusion annealing at temperatures of 600 °C and above caused the formation of additional precipitates, vacancy-type prismatic dislocation loops, and a few extrinsic stacking faults. Diffusion of Li into originally Zn-doped GaAs ([Zn]∼1×1019 cm−3) at 700 °C, on the other hand, did not lead to the formation of Li precipitates; however, a moderately high density of small vacancy-type prismatic loops was observed in the microstructure. On increasing the diffusion temperature to 850 °C the substructure revealed the presence of stacking faults and a small density of precipitates in addition to a number of large vacancy-type prismatic loops. The size density and distribution of these defects were found to be dependent on the diffusion time at 850 °C. The origins of the observed lattice defects have been discussed in the light of the previous localized-vibrational-mode (LVM) infrared spectroscopy measurements on materials with identical chemical composition and thermal history as in the present study. A definite correlation between the microstructural features and defect structure as determined by infrared absorption measurements was found to exist." @default.
- W2091092115 created "2016-06-24" @default.
- W2091092115 creator A5004131549 @default.
- W2091092115 creator A5032337770 @default.
- W2091092115 date "1977-07-01" @default.
- W2091092115 modified "2023-09-27" @default.
- W2091092115 title "A study of the lattice imperfections in Li-diffused GaAs by transmission electron microscopy" @default.
- W2091092115 cites W1975377221 @default.
- W2091092115 cites W1980155902 @default.
- W2091092115 cites W1993714181 @default.
- W2091092115 cites W1999301006 @default.
- W2091092115 cites W2000092558 @default.
- W2091092115 cites W2008491676 @default.
- W2091092115 cites W2009664608 @default.
- W2091092115 cites W2014207798 @default.
- W2091092115 cites W2032512083 @default.
- W2091092115 cites W2036598858 @default.
- W2091092115 cites W2038906058 @default.
- W2091092115 cites W2040544996 @default.
- W2091092115 cites W2055588585 @default.
- W2091092115 cites W2066183455 @default.
- W2091092115 cites W2068225651 @default.
- W2091092115 cites W2093576695 @default.
- W2091092115 doi "https://doi.org/10.1063/1.324139" @default.
- W2091092115 hasPublicationYear "1977" @default.
- W2091092115 type Work @default.
- W2091092115 sameAs 2091092115 @default.
- W2091092115 citedByCount "14" @default.
- W2091092115 crossrefType "journal-article" @default.
- W2091092115 hasAuthorship W2091092115A5004131549 @default.
- W2091092115 hasAuthorship W2091092115A5032337770 @default.
- W2091092115 hasConcept C113196181 @default.
- W2091092115 hasConcept C114221277 @default.
- W2091092115 hasConcept C121332964 @default.
- W2091092115 hasConcept C127413603 @default.
- W2091092115 hasConcept C146088050 @default.
- W2091092115 hasConcept C164675345 @default.
- W2091092115 hasConcept C171250308 @default.
- W2091092115 hasConcept C178790620 @default.
- W2091092115 hasConcept C185592680 @default.
- W2091092115 hasConcept C191897082 @default.
- W2091092115 hasConcept C192562407 @default.
- W2091092115 hasConcept C26873012 @default.
- W2091092115 hasConcept C2777855556 @default.
- W2091092115 hasConcept C33347731 @default.
- W2091092115 hasConcept C43617362 @default.
- W2091092115 hasConcept C66938386 @default.
- W2091092115 hasConcept C8010536 @default.
- W2091092115 hasConcept C87976508 @default.
- W2091092115 hasConcept C99679407 @default.
- W2091092115 hasConceptScore W2091092115C113196181 @default.
- W2091092115 hasConceptScore W2091092115C114221277 @default.
- W2091092115 hasConceptScore W2091092115C121332964 @default.
- W2091092115 hasConceptScore W2091092115C127413603 @default.
- W2091092115 hasConceptScore W2091092115C146088050 @default.
- W2091092115 hasConceptScore W2091092115C164675345 @default.
- W2091092115 hasConceptScore W2091092115C171250308 @default.
- W2091092115 hasConceptScore W2091092115C178790620 @default.
- W2091092115 hasConceptScore W2091092115C185592680 @default.
- W2091092115 hasConceptScore W2091092115C191897082 @default.
- W2091092115 hasConceptScore W2091092115C192562407 @default.
- W2091092115 hasConceptScore W2091092115C26873012 @default.
- W2091092115 hasConceptScore W2091092115C2777855556 @default.
- W2091092115 hasConceptScore W2091092115C33347731 @default.
- W2091092115 hasConceptScore W2091092115C43617362 @default.
- W2091092115 hasConceptScore W2091092115C66938386 @default.
- W2091092115 hasConceptScore W2091092115C8010536 @default.
- W2091092115 hasConceptScore W2091092115C87976508 @default.
- W2091092115 hasConceptScore W2091092115C99679407 @default.
- W2091092115 hasIssue "7" @default.
- W2091092115 hasLocation W20910921151 @default.
- W2091092115 hasOpenAccess W2091092115 @default.
- W2091092115 hasPrimaryLocation W20910921151 @default.
- W2091092115 hasRelatedWork W1972469921 @default.
- W2091092115 hasRelatedWork W2002007529 @default.
- W2091092115 hasRelatedWork W2029072960 @default.
- W2091092115 hasRelatedWork W2032948614 @default.
- W2091092115 hasRelatedWork W2050569025 @default.
- W2091092115 hasRelatedWork W2064660438 @default.
- W2091092115 hasRelatedWork W2114380448 @default.
- W2091092115 hasRelatedWork W2347531304 @default.
- W2091092115 hasRelatedWork W242636638 @default.
- W2091092115 hasRelatedWork W3012159059 @default.
- W2091092115 hasVolume "48" @default.
- W2091092115 isParatext "false" @default.
- W2091092115 isRetracted "false" @default.
- W2091092115 magId "2091092115" @default.
- W2091092115 workType "article" @default.