• W2092241195 abstract "High-purity aluminum foil was used to join alumina substrates directly in air at temperatures ranging from 800° to 1200°C and soak times of 1-100 h. It was found that the bend strengths of the resulting Al 2 O 3 /Al/Al 2 O 3 joints generally increase with increasing brazing temperature and time, with a maximum bend strength of 135 MPa on average achieved in samples joined at 1200°C for 100 h. Additionally it was determined that measurable ductility is retained in the joint even after exposure under extended high-temperature conditions. During joining, an Al 2 O 3 scale forms along the interface between the aluminum and adjacent substrates. An increase in brazing temperature and/or time leads to intergrowth and sintering between this thermally grown oxide layer and the substrate surface, which appears to be the primary source of improved joint strength. Fracture analysis indicates that the Al 2 O 3 /Al/ Al 2 O 3 joints generally fail via one of three mechanisms, (1) by de-bonding along the foil/substrate interface in specimens that were joined at low temperature or held at temperature for an insufficient period of time; (2) by ductile rupture in specimens that were joined at conditions that promoted sintering between the oxidized foil and adjacent alumina faying surfaces, but left behind a continuous residual aluminum layer within the joint; or (3) by mixed-mode fracture in specimens joined at high temperature and long exposure times, in which the thermally grown alumina that forms between the two substrates is interrupted by dispersed pockets of residual aluminum metal." @default.
• W2092241195 created "2016-06-24" @default.
• W2092241195 creator A5064074422 @default.
• W2092241195 creator A5070702171 @default.
• W2092241195 date "2007-09-26" @default.
• W2092241195 modified "2023-10-18" @default.
• W2092241195 title "Effects of Brazing Time and Temperature on the Microstructure and Mechanical Properties of Aluminum Air Brazed Joints" @default.
• W2092241195 cites W103911822 @default.
• W2092241195 cites W1963577039 @default.
• W2092241195 cites W1971244307 @default.
• W2092241195 cites W1974476643 @default.
• W2092241195 cites W1988312775 @default.
• W2092241195 cites W1991575729 @default.
• W2092241195 cites W1993151573 @default.
• W2092241195 cites W1996824260 @default.
• W2092241195 cites W2006767327 @default.
• W2092241195 cites W2011262374 @default.
• W2092241195 cites W2014602933 @default.
• W2092241195 cites W2015099234 @default.
• W2092241195 cites W2018659102 @default.
• W2092241195 cites W2028564599 @default.
• W2092241195 cites W2044279911 @default.
• W2092241195 cites W2071506607 @default.
• W2092241195 cites W2072254648 @default.
• W2092241195 cites W2075373240 @default.
• W2092241195 cites W2088655506 @default.
• W2092241195 cites W2099928031 @default.
• W2092241195 cites W2103944216 @default.
• W2092241195 cites W2111840646 @default.
• W2092241195 cites W2146474937 @default.
• W2092241195 cites W2146550966 @default.
• W2092241195 cites W2165393121 @default.
• W2092241195 cites W2166403274 @default.
• W2092241195 cites W4246908124 @default.
• W2092241195 doi "https://doi.org/10.1111/j.1551-2916.2007.02075.x" @default.
• W2092241195 hasPublicationYear "2007" @default.
• W2092241195 type Work @default.
• W2092241195 sameAs 2092241195 @default.
• W2092241195 citedByCount "5" @default.
• W2092241195 countsByYear W20922411952016 @default.
• W2092241195 countsByYear W20922411952017 @default.
• W2092241195 countsByYear W20922411952018 @default.
• W2092241195 countsByYear W20922411952019 @default.
• W2092241195 crossrefType "journal-article" @default.
• W2092241195 hasAuthorship W2092241195A5064074422 @default.
• W2092241195 hasAuthorship W2092241195A5070702171 @default.
• W2092241195 hasConcept C111368507 @default.
• W2092241195 hasConcept C127313418 @default.
• W2092241195 hasConcept C127413603 @default.
• W2092241195 hasConcept C149912024 @default.
• W2092241195 hasConcept C159985019 @default.
• W2092241195 hasConcept C170154142 @default.
• W2092241195 hasConcept C18555067 @default.
• W2092241195 hasConcept C191897082 @default.
• W2092241195 hasConcept C192562407 @default.
• W2092241195 hasConcept C2776512210 @default.
• W2092241195 hasConcept C2777289219 @default.
• W2092241195 hasConcept C2777581544 @default.
• W2092241195 hasConcept C2779227376 @default.
• W2092241195 hasConcept C2779851234 @default.
• W2092241195 hasConcept C2780026712 @default.
• W2092241195 hasConcept C513153333 @default.
• W2092241195 hasConcept C7363328 @default.
• W2092241195 hasConcept C86171150 @default.
• W2092241195 hasConcept C87976508 @default.
• W2092241195 hasConceptScore W2092241195C111368507 @default.
• W2092241195 hasConceptScore W2092241195C127313418 @default.
• W2092241195 hasConceptScore W2092241195C127413603 @default.
• W2092241195 hasConceptScore W2092241195C149912024 @default.
• W2092241195 hasConceptScore W2092241195C159985019 @default.
• W2092241195 hasConceptScore W2092241195C170154142 @default.
• W2092241195 hasConceptScore W2092241195C18555067 @default.
• W2092241195 hasConceptScore W2092241195C191897082 @default.
• W2092241195 hasConceptScore W2092241195C192562407 @default.
• W2092241195 hasConceptScore W2092241195C2776512210 @default.
• W2092241195 hasConceptScore W2092241195C2777289219 @default.
• W2092241195 hasConceptScore W2092241195C2777581544 @default.
• W2092241195 hasConceptScore W2092241195C2779227376 @default.
• W2092241195 hasConceptScore W2092241195C2779851234 @default.
• W2092241195 hasConceptScore W2092241195C2780026712 @default.
• W2092241195 hasConceptScore W2092241195C513153333 @default.
• W2092241195 hasConceptScore W2092241195C7363328 @default.
• W2092241195 hasConceptScore W2092241195C86171150 @default.
• W2092241195 hasConceptScore W2092241195C87976508 @default.
• W2092241195 hasLocation W20922411951 @default.
• W2092241195 hasOpenAccess W2092241195 @default.
• W2092241195 hasPrimaryLocation W20922411951 @default.
• W2092241195 hasRelatedWork W1102762025 @default.
• W2092241195 hasRelatedWork W1104396509 @default.
• W2092241195 hasRelatedWork W1980826224 @default.
• W2092241195 hasRelatedWork W1985853371 @default.
• W2092241195 hasRelatedWork W2041102963 @default.
• W2092241195 hasRelatedWork W2057689287 @default.
• W2092241195 hasRelatedWork W2913515405 @default.
• W2092241195 hasRelatedWork W2914425956 @default.
• W2092241195 hasRelatedWork W3133275257 @default.
• W2092241195 hasRelatedWork W3138802658 @default.
• W2092241195 isParatext "false" @default.
• W2092241195 isRetracted "false" @default.
• W2092241195 magId "2092241195" @default.

• next