- W2093271151 abstract "Antireflective films on glass were prepared by a dip-coating method from a sol-gel, which consisted of 50 nm monodisperse silica particles mixed with ethanol and water. The solar transmittance increased by 5.4% for the best made sample. A visible transmittance as high as 99.2%, with a peak transmittance of 99.5%, was achieved. A super insulated triple glazed window was made up of two low emissive glazings and an intermediate glazing which was either a standard float glass or an antireflective coated low iron one. At low angels of incidence the visible transmittance is more than 10% higher for the unit with the antireflective glazing, but at high angles of incidence they become almost identical. The scratch resistance of the film and the adhesion between the film and the substrate was considerably improved by baking the film at elevated temperatures. A slight decrease in the transmittance is noticed after the baking and the peak transmittance is displaced towards shorter wavelengths. It is believed that the particles fuse together and to the substrate upon baking. Transmission electron microscopy was used to study the baking process and preliminary results support the fusion theory. One large scale sample was tempered in a commercial oven with strongly improved mechanical properties as a result. The minimum reflectance was slightly increased to 1.5% from the initial 1%, but on the whole the antireflective properties were preserved." @default.
- W2093271151 created "2016-06-24" @default.
- W2093271151 creator A5011264053 @default.
- W2093271151 creator A5056392432 @default.
- W2093271151 creator A5077914391 @default.
- W2093271151 date "1999-08-01" @default.
- W2093271151 modified "2023-10-17" @default.
- W2093271151 title "Optical and mechanical properties of sol-gel antireflective films for solar energy applications" @default.
- W2093271151 cites W1985456030 @default.
- W2093271151 cites W2023256731 @default.
- W2093271151 cites W2024353914 @default.
- W2093271151 cites W2028482727 @default.
- W2093271151 cites W2038316371 @default.
- W2093271151 cites W2054318933 @default.
- W2093271151 cites W2064349675 @default.
- W2093271151 cites W2065463461 @default.
- W2093271151 cites W2093725808 @default.
- W2093271151 doi "https://doi.org/10.1016/s0040-6090(99)00257-6" @default.
- W2093271151 hasPublicationYear "1999" @default.
- W2093271151 type Work @default.
- W2093271151 sameAs 2093271151 @default.
- W2093271151 citedByCount "126" @default.
- W2093271151 countsByYear W20932711512012 @default.
- W2093271151 countsByYear W20932711512013 @default.
- W2093271151 countsByYear W20932711512014 @default.
- W2093271151 countsByYear W20932711512015 @default.
- W2093271151 countsByYear W20932711512016 @default.
- W2093271151 countsByYear W20932711512017 @default.
- W2093271151 countsByYear W20932711512018 @default.
- W2093271151 countsByYear W20932711512019 @default.
- W2093271151 countsByYear W20932711512020 @default.
- W2093271151 countsByYear W20932711512021 @default.
- W2093271151 countsByYear W20932711512022 @default.
- W2093271151 crossrefType "journal-article" @default.
- W2093271151 hasAuthorship W2093271151A5011264053 @default.
- W2093271151 hasAuthorship W2093271151A5056392432 @default.
- W2093271151 hasAuthorship W2093271151A5077914391 @default.
- W2093271151 hasConcept C104663316 @default.
- W2093271151 hasConcept C108406538 @default.
- W2093271151 hasConcept C111368507 @default.
- W2093271151 hasConcept C120665830 @default.
- W2093271151 hasConcept C121332964 @default.
- W2093271151 hasConcept C127313418 @default.
- W2093271151 hasConcept C150493377 @default.
- W2093271151 hasConcept C159985019 @default.
- W2093271151 hasConcept C171250308 @default.
- W2093271151 hasConcept C19067145 @default.
- W2093271151 hasConcept C192562407 @default.
- W2093271151 hasConcept C2777289219 @default.
- W2093271151 hasConcept C2781448156 @default.
- W2093271151 hasConcept C49040817 @default.
- W2093271151 hasConcept C53559285 @default.
- W2093271151 hasConceptScore W2093271151C104663316 @default.
- W2093271151 hasConceptScore W2093271151C108406538 @default.
- W2093271151 hasConceptScore W2093271151C111368507 @default.
- W2093271151 hasConceptScore W2093271151C120665830 @default.
- W2093271151 hasConceptScore W2093271151C121332964 @default.
- W2093271151 hasConceptScore W2093271151C127313418 @default.
- W2093271151 hasConceptScore W2093271151C150493377 @default.
- W2093271151 hasConceptScore W2093271151C159985019 @default.
- W2093271151 hasConceptScore W2093271151C171250308 @default.
- W2093271151 hasConceptScore W2093271151C19067145 @default.
- W2093271151 hasConceptScore W2093271151C192562407 @default.
- W2093271151 hasConceptScore W2093271151C2777289219 @default.
- W2093271151 hasConceptScore W2093271151C2781448156 @default.
- W2093271151 hasConceptScore W2093271151C49040817 @default.
- W2093271151 hasConceptScore W2093271151C53559285 @default.
- W2093271151 hasIssue "1-2" @default.
- W2093271151 hasLocation W20932711511 @default.
- W2093271151 hasOpenAccess W2093271151 @default.
- W2093271151 hasPrimaryLocation W20932711511 @default.
- W2093271151 hasRelatedWork W1968347890 @default.
- W2093271151 hasRelatedWork W1986610506 @default.
- W2093271151 hasRelatedWork W2014911770 @default.
- W2093271151 hasRelatedWork W2080032372 @default.
- W2093271151 hasRelatedWork W2093271151 @default.
- W2093271151 hasRelatedWork W2297003625 @default.
- W2093271151 hasRelatedWork W2388711754 @default.
- W2093271151 hasRelatedWork W2793446430 @default.
- W2093271151 hasRelatedWork W3088333650 @default.
- W2093271151 hasRelatedWork W3213825854 @default.
- W2093271151 hasVolume "351" @default.
- W2093271151 isParatext "false" @default.
- W2093271151 isRetracted "false" @default.
- W2093271151 magId "2093271151" @default.
- W2093271151 workType "article" @default.