• W2093777815 abstract "Single crystals of the hexagonal metals and alloys Zn, Zn + 0.2 at.% Ga and Zn + 0.2 at.% Ag were deformed between 4.2 and 295 K. The deformation was interrupted after a shear strain of about a = 10%, followed by annealing at 295 K for certain times, subsequently the specimens were further deformed at the original deformation temperature. This annealing changes the flow stress. The sign and magnitude of the stress change depends on the chosen parameters deformation temperature and annealing time. In some cases annealing after low temperature deformation leads to a dramatical increase of the flow stress, up to a factor of 2.4. It is possible to explain the observed effects by a model considering diffusion processes of point defects that are produced during deformation. The characteristics of the experimental effects suggest that the processes that are responsible for the change of the flow stress play also an important role during plastic deformation of h.c.p. metals. This implies that they also determine at least partly the work hardening coefficient and its temperature dependence. Nous avons déformé entre 4,2 et 295 K des monocristaux de zinc et des alliages Zn + 0,2 at.% Ga et Zn + 0,2 at.% Ag de structure hexagonale. On arrêtait la déformation après un cisaillement a d'environ 10%, suivi par un recuit à 295 K. Les échantillons étaient ensuite déformés à la température de la première déformation. Le recuit modifiait la contrainte d'écoulement. Le signe et la grandeur du changement de contrainte dépendaient des paramétres choisis: température de déformation et duré de recuit. Dans certains cas, un recuit après déformation à basse température conduisait à une augmentation dramatique de la contrainte d'écoulement, d'un facteur pouvant atteindre 2,4. On peut expliquer ces phénomènes i l'aide d'un modèle considérant la diffusion de défauts ponctuels produits au cours de la déformation. Les observations expérimentales suggèrent que les phénomènes responsables du changement de contrainte d'écoulement jouent égalment un rôle important au cours de la déformation plastique des métaux h.c.p. Ceci implique qu'ils déterminent également au moins partiellement le coefficient de durcissement et sa variation en fonction de la température. Einkristalle der hexagonalen Metalle und Legierungen Zn, Zn + 0.2 at.% Ga und Zn + 0.2 at.% Ag wurden zwischen 4 und 295 K verformt. Die Verformung wurde nach einer Abgleitung von etwa a = 10% unterbrochen. Dann wurde bei 295 K für verschiedene Zeiten ausgelagert, und anschliessend wurden die Proben bei der ursprünglichen Verformungstemperatur weiterverformt. Die Auslagerung bewirkt eine Äderung der Fliesspannung, wobei Grosse und Vorzeichen der Spannungsänderung von der Verformungstemperatur und Auslagerungszeit abhängen. Auslagerung nach Verformung bei tiefen Temperaturen kann zu einer Erhöhung der Fliesspannung um den Faktor 2.4 führen. Die Beobachtungen werden durch Diffusion der während der Verformung produzierten Punktdefekte erklärt. Die Resultate legen nahe, dass dieselben Mechanismen auch bei der ungestörten plastischen Verformung von hexagonalen Metallen eine Rolle spielen. Sie beeinflussen damit wenigstens teilweise den Verfestigungskoeffizienten und dessen Temperaturabhängigkeit." @default.
• W2093777815 created "2016-06-24" @default.
• W2093777815 creator A5018557458 @default.
• W2093777815 creator A5026707519 @default.
• W2093777815 creator A5034487759 @default.
• W2093777815 date "1982-03-01" @default.
• W2093777815 modified "2023-10-01" @default.
• W2093777815 title "Anneal hardening of Zn and Zn-alloys" @default.
• W2093777815 cites W1989117453 @default.
• W2093777815 cites W1989508726 @default.
• W2093777815 cites W1989598675 @default.
• W2093777815 cites W1994863599 @default.
• W2093777815 cites W1996900808 @default.
• W2093777815 cites W2016765623 @default.
• W2093777815 cites W2027595239 @default.
• W2093777815 cites W2050394322 @default.
• W2093777815 cites W2052753058 @default.
• W2093777815 cites W2059682282 @default.
• W2093777815 cites W2064244177 @default.
• W2093777815 cites W2086457261 @default.
• W2093777815 cites W2092480778 @default.
• W2093777815 cites W2117681156 @default.
• W2093777815 doi "https://doi.org/10.1016/0001-6160(82)90112-2" @default.
• W2093777815 hasPublicationYear "1982" @default.
• W2093777815 type Work @default.
• W2093777815 sameAs 2093777815 @default.
• W2093777815 citedByCount "14" @default.
• W2093777815 countsByYear W20937778152019 @default.
• W2093777815 countsByYear W20937778152022 @default.
• W2093777815 countsByYear W20937778152023 @default.
• W2093777815 crossrefType "journal-article" @default.
• W2093777815 hasAuthorship W2093777815A5018557458 @default.
• W2093777815 hasAuthorship W2093777815A5026707519 @default.
• W2093777815 hasAuthorship W2093777815A5034487759 @default.
• W2093777815 hasConcept C121332964 @default.
• W2093777815 hasConcept C127172972 @default.
• W2093777815 hasConcept C149342994 @default.
• W2093777815 hasConcept C159985019 @default.
• W2093777815 hasConcept C162611839 @default.
• W2093777815 hasConcept C165682214 @default.
• W2093777815 hasConcept C185592680 @default.
• W2093777815 hasConcept C191897082 @default.
• W2093777815 hasConcept C192562407 @default.
• W2093777815 hasConcept C2776704300 @default.
• W2093777815 hasConcept C2777855556 @default.
• W2093777815 hasConcept C2779227376 @default.
• W2093777815 hasConcept C30445746 @default.
• W2093777815 hasConcept C44255700 @default.
• W2093777815 hasConcept C535196362 @default.
• W2093777815 hasConcept C8010536 @default.
• W2093777815 hasConcept C87976508 @default.
• W2093777815 hasConcept C97355855 @default.
• W2093777815 hasConceptScore W2093777815C121332964 @default.
• W2093777815 hasConceptScore W2093777815C127172972 @default.
• W2093777815 hasConceptScore W2093777815C149342994 @default.
• W2093777815 hasConceptScore W2093777815C159985019 @default.
• W2093777815 hasConceptScore W2093777815C162611839 @default.
• W2093777815 hasConceptScore W2093777815C165682214 @default.
• W2093777815 hasConceptScore W2093777815C185592680 @default.
• W2093777815 hasConceptScore W2093777815C191897082 @default.
• W2093777815 hasConceptScore W2093777815C192562407 @default.
• W2093777815 hasConceptScore W2093777815C2776704300 @default.
• W2093777815 hasConceptScore W2093777815C2777855556 @default.
• W2093777815 hasConceptScore W2093777815C2779227376 @default.
• W2093777815 hasConceptScore W2093777815C30445746 @default.
• W2093777815 hasConceptScore W2093777815C44255700 @default.
• W2093777815 hasConceptScore W2093777815C535196362 @default.
• W2093777815 hasConceptScore W2093777815C8010536 @default.
• W2093777815 hasConceptScore W2093777815C87976508 @default.
• W2093777815 hasConceptScore W2093777815C97355855 @default.
• W2093777815 hasIssue "3" @default.
• W2093777815 hasLocation W20937778151 @default.
• W2093777815 hasOpenAccess W2093777815 @default.
• W2093777815 hasPrimaryLocation W20937778151 @default.
• W2093777815 hasRelatedWork W1603487225 @default.
• W2093777815 hasRelatedWork W187290626 @default.
• W2093777815 hasRelatedWork W1982928192 @default.
• W2093777815 hasRelatedWork W1997277812 @default.
• W2093777815 hasRelatedWork W2044814285 @default.
• W2093777815 hasRelatedWork W2088297201 @default.
• W2093777815 hasRelatedWork W2137567472 @default.
• W2093777815 hasRelatedWork W2371918943 @default.
• W2093777815 hasRelatedWork W3036844351 @default.
• W2093777815 hasRelatedWork W3172491093 @default.
• W2093777815 hasVolume "30" @default.
• W2093777815 isParatext "false" @default.
• W2093777815 isRetracted "false" @default.
• W2093777815 magId "2093777815" @default.
• W2093777815 workType "article" @default.