- W2110843969 abstract "Tin-zinc solder with the low melting temperature below 200 /spl deg/C is an attractive alternative to eutectic tin-lead. The addition of bismuth improves wettability of Sn-Zn alloy. Low cycle isothermal mechanical fatigue testing of solder joints of Sn-8Zn-3Bi (wt%) and Sn-37Pb were tested in a solder joint of single lap shear sample with a multi-functional Instron 4458-Microtester. Solder joints around 0.5mm high and 1.6mm in diameter was used. The testing was executed in a displacement -controlled mode, at three different amplitudes namely, 40, 50 and 60/spl mu/m. The test frequency was kept constant at 0.2Hz for all tests. The failure of the solder joint was defined as a 50% load reduction. Finite element (FE) modeling were simulated to analyze the strain and stress distribution in solder joint and compared with the experimental results. The cross-section showed that there were mixed phase of small cellular-shape and coarse needle-shape in the microstructure of Sn-8Zn-3Bi. SEM-EDS analysis indicated that the Au-Zn intermetallic compound was observed near the interface. The total average lifetime of Sn-8Zn-3Bi solder joint was 17% increase comparing with Sn-37Pb solder joint from low cycle fatigue testing. The ductile-fracture manner and brittle-fracture manner were both involved in fracture surface, and more features of brittle-fracture manner appeared in small displacement loading and more features of ductile-fracture manner in large displacement loading. From FE simulation, the maximum stress was found at two corners, coinciding with the experimental observation of crack initiation and propagation." @default.
- W2110843969 created "2016-06-24" @default.
- W2110843969 creator A5018255654 @default.
- W2110843969 creator A5027962680 @default.
- W2110843969 creator A5037217237 @default.
- W2110843969 creator A5041014194 @default.
- W2110843969 creator A5065642759 @default.
- W2110843969 creator A5083314215 @default.
- W2110843969 creator A5085835611 @default.
- W2110843969 date "2005-07-28" @default.
- W2110843969 modified "2023-09-23" @default.
- W2110843969 title "Isothermal low cycle fatigue behavior of Sn-8Zn-3Bi on single shear solder joint" @default.
- W2110843969 cites W2016201835 @default.
- W2110843969 cites W2031534830 @default.
- W2110843969 cites W2061159846 @default.
- W2110843969 cites W2071099144 @default.
- W2110843969 cites W2168111264 @default.
- W2110843969 doi "https://doi.org/10.1109/ectc.2005.1441345" @default.
- W2110843969 hasPublicationYear "2005" @default.
- W2110843969 type Work @default.
- W2110843969 sameAs 2110843969 @default.
- W2110843969 citedByCount "1" @default.
- W2110843969 crossrefType "proceedings-article" @default.
- W2110843969 hasAuthorship W2110843969A5018255654 @default.
- W2110843969 hasAuthorship W2110843969A5027962680 @default.
- W2110843969 hasAuthorship W2110843969A5037217237 @default.
- W2110843969 hasAuthorship W2110843969A5041014194 @default.
- W2110843969 hasAuthorship W2110843969A5065642759 @default.
- W2110843969 hasAuthorship W2110843969A5083314215 @default.
- W2110843969 hasAuthorship W2110843969A5085835611 @default.
- W2110843969 hasConcept C121332964 @default.
- W2110843969 hasConcept C127413603 @default.
- W2110843969 hasConcept C133347239 @default.
- W2110843969 hasConcept C136478896 @default.
- W2110843969 hasConcept C159985019 @default.
- W2110843969 hasConcept C18168003 @default.
- W2110843969 hasConcept C18555067 @default.
- W2110843969 hasConcept C191897082 @default.
- W2110843969 hasConcept C192562407 @default.
- W2110843969 hasConcept C27501479 @default.
- W2110843969 hasConcept C2780026712 @default.
- W2110843969 hasConcept C41151612 @default.
- W2110843969 hasConcept C43369102 @default.
- W2110843969 hasConcept C50296614 @default.
- W2110843969 hasConcept C66938386 @default.
- W2110843969 hasConcept C87976508 @default.
- W2110843969 hasConcept C96035792 @default.
- W2110843969 hasConcept C97355855 @default.
- W2110843969 hasConceptScore W2110843969C121332964 @default.
- W2110843969 hasConceptScore W2110843969C127413603 @default.
- W2110843969 hasConceptScore W2110843969C133347239 @default.
- W2110843969 hasConceptScore W2110843969C136478896 @default.
- W2110843969 hasConceptScore W2110843969C159985019 @default.
- W2110843969 hasConceptScore W2110843969C18168003 @default.
- W2110843969 hasConceptScore W2110843969C18555067 @default.
- W2110843969 hasConceptScore W2110843969C191897082 @default.
- W2110843969 hasConceptScore W2110843969C192562407 @default.
- W2110843969 hasConceptScore W2110843969C27501479 @default.
- W2110843969 hasConceptScore W2110843969C2780026712 @default.
- W2110843969 hasConceptScore W2110843969C41151612 @default.
- W2110843969 hasConceptScore W2110843969C43369102 @default.
- W2110843969 hasConceptScore W2110843969C50296614 @default.
- W2110843969 hasConceptScore W2110843969C66938386 @default.
- W2110843969 hasConceptScore W2110843969C87976508 @default.
- W2110843969 hasConceptScore W2110843969C96035792 @default.
- W2110843969 hasConceptScore W2110843969C97355855 @default.
- W2110843969 hasLocation W21108439691 @default.
- W2110843969 hasOpenAccess W2110843969 @default.
- W2110843969 hasPrimaryLocation W21108439691 @default.
- W2110843969 hasRelatedWork W1596840987 @default.
- W2110843969 hasRelatedWork W1965277880 @default.
- W2110843969 hasRelatedWork W1966835883 @default.
- W2110843969 hasRelatedWork W1969319609 @default.
- W2110843969 hasRelatedWork W1969830829 @default.
- W2110843969 hasRelatedWork W2013005457 @default.
- W2110843969 hasRelatedWork W2029000605 @default.
- W2110843969 hasRelatedWork W2039062065 @default.
- W2110843969 hasRelatedWork W2066326512 @default.
- W2110843969 hasRelatedWork W2086753069 @default.
- W2110843969 hasRelatedWork W2138904158 @default.
- W2110843969 hasRelatedWork W2150431808 @default.
- W2110843969 hasRelatedWork W2161423145 @default.
- W2110843969 hasRelatedWork W2275446799 @default.
- W2110843969 hasRelatedWork W2335704115 @default.
- W2110843969 hasRelatedWork W2369499312 @default.
- W2110843969 hasRelatedWork W2554133965 @default.
- W2110843969 hasRelatedWork W2610851358 @default.
- W2110843969 hasRelatedWork W817146574 @default.
- W2110843969 hasRelatedWork W2137323665 @default.
- W2110843969 isParatext "false" @default.
- W2110843969 isRetracted "false" @default.
- W2110843969 magId "2110843969" @default.
- W2110843969 workType "article" @default.