- W2113140864 abstract "Experimental damage mechanics of flip chip solder joints under current stressing is studied using 20 test vehicle flip chip modules. Three different failure modes are observed. The dominant damage mechanism is caused by the combined effect of electromigration and thermomigration, where void nucleation and growth lead to the ultimate failure of the module. It is observed that thermomigration driving forces are stronger than electromigration; as a result thermomigration, not electromigration, determines the site of void nucleation. The void nucleation and growth modes and their preferred sites are also observed and discussed in detail. The interface between the Ni barrier layer and the solder joint is found to be the favorite site of void nucleation and growth. The effect of pre-existing voids on the failure process of a solder joint is also studied. It is observed that Black’s time to failure law for thin films is unreliable for solder joints." @default.
- W2113140864 created "2016-06-24" @default.
- W2113140864 creator A5036052988 @default.
- W2113140864 creator A5047534866 @default.
- W2113140864 creator A5070803828 @default.
- W2113140864 date "2006-01-01" @default.
- W2113140864 modified "2023-09-23" @default.
- W2113140864 title "Experimental Damage Mechanics of Micro/Power Electronics Solder Joints under Electric Current Stresses" @default.
- W2113140864 cites W1970915642 @default.
- W2113140864 cites W1973301822 @default.
- W2113140864 cites W1984986587 @default.
- W2113140864 cites W1988271687 @default.
- W2113140864 cites W1990215011 @default.
- W2113140864 cites W1991223476 @default.
- W2113140864 cites W1994031878 @default.
- W2113140864 cites W2010689236 @default.
- W2113140864 cites W2012476220 @default.
- W2113140864 cites W2025060723 @default.
- W2113140864 cites W2031050377 @default.
- W2113140864 cites W2035218557 @default.
- W2113140864 cites W2044719521 @default.
- W2113140864 cites W2046340437 @default.
- W2113140864 cites W2046657456 @default.
- W2113140864 cites W2046896054 @default.
- W2113140864 cites W2070714784 @default.
- W2113140864 cites W2073909902 @default.
- W2113140864 cites W2074551030 @default.
- W2113140864 cites W2081786181 @default.
- W2113140864 cites W2083090974 @default.
- W2113140864 cites W2095470180 @default.
- W2113140864 cites W2109780615 @default.
- W2113140864 cites W2113965389 @default.
- W2113140864 cites W2114668332 @default.
- W2113140864 cites W2131502997 @default.
- W2113140864 cites W2561953621 @default.
- W2113140864 cites W2605984795 @default.
- W2113140864 cites W1985940613 @default.
- W2113140864 doi "https://doi.org/10.1177/1056789506054311" @default.
- W2113140864 hasPublicationYear "2006" @default.
- W2113140864 type Work @default.
- W2113140864 sameAs 2113140864 @default.
- W2113140864 citedByCount "29" @default.
- W2113140864 countsByYear W21131408642012 @default.
- W2113140864 countsByYear W21131408642013 @default.
- W2113140864 countsByYear W21131408642017 @default.
- W2113140864 countsByYear W21131408642018 @default.
- W2113140864 countsByYear W21131408642020 @default.
- W2113140864 countsByYear W21131408642021 @default.
- W2113140864 countsByYear W21131408642022 @default.
- W2113140864 crossrefType "journal-article" @default.
- W2113140864 hasAuthorship W2113140864A5036052988 @default.
- W2113140864 hasAuthorship W2113140864A5047534866 @default.
- W2113140864 hasAuthorship W2113140864A5070803828 @default.
- W2113140864 hasConcept C121332964 @default.
- W2113140864 hasConcept C127413603 @default.
- W2113140864 hasConcept C138055206 @default.
- W2113140864 hasConcept C159985019 @default.
- W2113140864 hasConcept C191897082 @default.
- W2113140864 hasConcept C192562407 @default.
- W2113140864 hasConcept C2779227376 @default.
- W2113140864 hasConcept C2779772531 @default.
- W2113140864 hasConcept C50296614 @default.
- W2113140864 hasConcept C61048295 @default.
- W2113140864 hasConcept C68928338 @default.
- W2113140864 hasConcept C77595967 @default.
- W2113140864 hasConcept C79072407 @default.
- W2113140864 hasConcept C97355855 @default.
- W2113140864 hasConceptScore W2113140864C121332964 @default.
- W2113140864 hasConceptScore W2113140864C127413603 @default.
- W2113140864 hasConceptScore W2113140864C138055206 @default.
- W2113140864 hasConceptScore W2113140864C159985019 @default.
- W2113140864 hasConceptScore W2113140864C191897082 @default.
- W2113140864 hasConceptScore W2113140864C192562407 @default.
- W2113140864 hasConceptScore W2113140864C2779227376 @default.
- W2113140864 hasConceptScore W2113140864C2779772531 @default.
- W2113140864 hasConceptScore W2113140864C50296614 @default.
- W2113140864 hasConceptScore W2113140864C61048295 @default.
- W2113140864 hasConceptScore W2113140864C68928338 @default.
- W2113140864 hasConceptScore W2113140864C77595967 @default.
- W2113140864 hasConceptScore W2113140864C79072407 @default.
- W2113140864 hasConceptScore W2113140864C97355855 @default.
- W2113140864 hasIssue "1" @default.
- W2113140864 hasLocation W21131408641 @default.
- W2113140864 hasOpenAccess W2113140864 @default.
- W2113140864 hasPrimaryLocation W21131408641 @default.
- W2113140864 hasRelatedWork W1963490782 @default.
- W2113140864 hasRelatedWork W2007138504 @default.
- W2113140864 hasRelatedWork W2011847960 @default.
- W2113140864 hasRelatedWork W2019658028 @default.
- W2113140864 hasRelatedWork W2034317187 @default.
- W2113140864 hasRelatedWork W2035514886 @default.
- W2113140864 hasRelatedWork W2048644706 @default.
- W2113140864 hasRelatedWork W2053240402 @default.
- W2113140864 hasRelatedWork W2133965655 @default.
- W2113140864 hasRelatedWork W2261565770 @default.
- W2113140864 hasVolume "15" @default.
- W2113140864 isParatext "false" @default.
- W2113140864 isRetracted "false" @default.