- W2119073650 abstract "Microleakage is a major factor affecting longevity of composite restorations. This study evaluated the effect of polymerization mode of bonding agent on microleakage of composite restorations.Forty-eight Class V cavities were prepared on buccal and lingual surfaces of 24 extracted human premolars. Occlusal and gingival margins were placed in the enamel and dentin, respectively. Teeth were divided into four groups as follows: Group I: Optibond Solo Plus (light-cured); Group II: Optibond Solo Plus (dual-cured); Group III: Prime & Bond NT (light-cured), Group IV: Prime & Bond NT (dual-cured). Teeth were restored using Z250 composite in three increments. After polishing the restorations, samples were thermocycled for 1000 cycles and stored in distilled water for 3 months. Then they were placed in 2% fuchsine solution for 48 hours. The samples were sectioned longitudinally and evaluated for microleakage under a stereomicroscope at ×40 magnification. Dye penetration was scored on a 0-3 ordinal scale. Data were analyzed using Kruskal-Wallis, Bonferroni and Wilcoxon signed ranks test.Microleakage was significantly lower in enamel margins compared to dentin margins (P<0.05); multiple comparisons by Bonferroni tests revealed that the only factor with significant effect on leakage of the restoration is location of the restoration margin. Mode of adhesive polymerization had no significant influence on microleakage (P>0.05). Prime & Bond NT had less microleakage compared to Optibond SoloPlus, but the difference was not significant (P>0.05).There was no difference in the amount of microleakage in Class V composite restorations using light-cured and dual-cured bonding systems. Dentinal margins of restorations exhibited more microleakage than enamel margins." @default.
- W2119073650 created "2016-06-24" @default.
- W2119073650 creator A5009731425 @default.
- W2119073650 creator A5023187283 @default.
- W2119073650 creator A5035233057 @default.
- W2119073650 creator A5048873633 @default.
- W2119073650 date "2012-01-01" @default.
- W2119073650 modified "2023-09-23" @default.
- W2119073650 title "Microleakage of dual-cured adhesive systems in class v composite resin restorations." @default.
- W2119073650 cites W1658923407 @default.
- W2119073650 cites W1968882781 @default.
- W2119073650 cites W1981199429 @default.
- W2119073650 cites W1983915049 @default.
- W2119073650 cites W1997933708 @default.
- W2119073650 cites W2007152787 @default.
- W2119073650 cites W2015046796 @default.
- W2119073650 cites W2056819208 @default.
- W2119073650 cites W2064928657 @default.
- W2119073650 cites W2082753587 @default.
- W2119073650 cites W2111269106 @default.
- W2119073650 cites W2130733544 @default.
- W2119073650 cites W2131970270 @default.
- W2119073650 cites W2136010571 @default.
- W2119073650 cites W2147104125 @default.
- W2119073650 cites W2150442057 @default.
- W2119073650 cites W2151542045 @default.
- W2119073650 cites W2154874841 @default.
- W2119073650 cites W2166078454 @default.
- W2119073650 cites W2168270545 @default.
- W2119073650 cites W2252339834 @default.
- W2119073650 cites W2287055663 @default.
- W2119073650 cites W2409863089 @default.
- W2119073650 cites W2413103619 @default.
- W2119073650 cites W2415719034 @default.
- W2119073650 cites W2416809543 @default.
- W2119073650 cites W348600858 @default.
- W2119073650 cites W45931226 @default.
- W2119073650 cites W53602082 @default.
- W2119073650 hasPubMedCentralId "https://www.ncbi.nlm.nih.gov/pmc/articles/3466775" @default.
- W2119073650 hasPubMedId "https://pubmed.ncbi.nlm.nih.gov/23066474" @default.
- W2119073650 hasPublicationYear "2012" @default.
- W2119073650 type Work @default.
- W2119073650 sameAs 2119073650 @default.
- W2119073650 citedByCount "2" @default.
- W2119073650 countsByYear W21190736502016 @default.
- W2119073650 crossrefType "journal-article" @default.
- W2119073650 hasAuthorship W2119073650A5009731425 @default.
- W2119073650 hasAuthorship W2119073650A5023187283 @default.
- W2119073650 hasAuthorship W2119073650A5035233057 @default.
- W2119073650 hasAuthorship W2119073650A5048873633 @default.
- W2119073650 hasConcept C104779481 @default.
- W2119073650 hasConcept C155977592 @default.
- W2119073650 hasConcept C156887251 @default.
- W2119073650 hasConcept C159985019 @default.
- W2119073650 hasConcept C192562407 @default.
- W2119073650 hasConcept C199343813 @default.
- W2119073650 hasConcept C2779227376 @default.
- W2119073650 hasConcept C2779263046 @default.
- W2119073650 hasConcept C3019280483 @default.
- W2119073650 hasConcept C68928338 @default.
- W2119073650 hasConcept C71924100 @default.
- W2119073650 hasConceptScore W2119073650C104779481 @default.
- W2119073650 hasConceptScore W2119073650C155977592 @default.
- W2119073650 hasConceptScore W2119073650C156887251 @default.
- W2119073650 hasConceptScore W2119073650C159985019 @default.
- W2119073650 hasConceptScore W2119073650C192562407 @default.
- W2119073650 hasConceptScore W2119073650C199343813 @default.
- W2119073650 hasConceptScore W2119073650C2779227376 @default.
- W2119073650 hasConceptScore W2119073650C2779263046 @default.
- W2119073650 hasConceptScore W2119073650C3019280483 @default.
- W2119073650 hasConceptScore W2119073650C68928338 @default.
- W2119073650 hasConceptScore W2119073650C71924100 @default.
- W2119073650 hasLocation W21190736501 @default.
- W2119073650 hasOpenAccess W2119073650 @default.
- W2119073650 hasPrimaryLocation W21190736501 @default.
- W2119073650 hasRelatedWork W102201848 @default.
- W2119073650 hasRelatedWork W1491013837 @default.
- W2119073650 hasRelatedWork W1603970846 @default.
- W2119073650 hasRelatedWork W1788230182 @default.
- W2119073650 hasRelatedWork W1799542307 @default.
- W2119073650 hasRelatedWork W1977009291 @default.
- W2119073650 hasRelatedWork W2020795058 @default.
- W2119073650 hasRelatedWork W2032460144 @default.
- W2119073650 hasRelatedWork W2057962391 @default.
- W2119073650 hasRelatedWork W2062099318 @default.
- W2119073650 hasRelatedWork W2077813527 @default.
- W2119073650 hasRelatedWork W2083325992 @default.
- W2119073650 hasRelatedWork W2090738022 @default.
- W2119073650 hasRelatedWork W2137295487 @default.
- W2119073650 hasRelatedWork W2163566925 @default.
- W2119073650 hasRelatedWork W2171203434 @default.
- W2119073650 hasRelatedWork W2301336284 @default.
- W2119073650 hasRelatedWork W2389835663 @default.
- W2119073650 hasRelatedWork W2414835526 @default.
- W2119073650 hasRelatedWork W2520314094 @default.
- W2119073650 isParatext "false" @default.
- W2119073650 isRetracted "false" @default.
- W2119073650 magId "2119073650" @default.
- W2119073650 workType "article" @default.