• W2122535885 abstract "The kinetics of nucleation and crystal growth in a Li2B4O7 glass were investigated using differential thermal analysis (DTA) and differential scanning calorimetry (DSC). This melt forms a glass even when it is cooled at a very slow rate (2 K/min). The temperature range of nucleation was determined by comparing the heights of the exothermic DTA crystallization peaks for samples that were annealed at different temperatures for a fixed time (10 min). Nucleation for this glass occurred in the temperature region of glass transition, where the nucleation rate had a maximum value at ∼770 K. The real detectable enthalpy change that was due to crystallization occurred at temperatures well above the temperature range for nucleation; hence, the temperature regions for nucleation and crystal growth were assumed to be well separated. The glass sample with an almost-saturated number of nuclei, which was prepared by annealing at a temperature of 770 K for 10 min while the melt was cooled, was subjected to DSC measurements at various heating rates (φh). The kinetics of crystal growth were analyzed via the conventional isoconversion method. For the sample without any annealing treatment, the number of nuclei for growth varied, depending on the thermal histories within the temperature region for nucleation, which was characterized by the linear cooling rate (φc) of the melt and the linear heating rate φh of the glass. A kinetic approach that considered the dependence of the number of nuclei on φc and φh was applied to the crystal growth in the nonannealed glass. The three-dimensional growth of the preexisting nuclei with apparent activation energies (E) of 315.6 ± 4.6 kJ/mol for the annealed glasses and 300.6 ± 9.5 kJ/mol for the nonannealed glasses was determined. This agreement in the values of E indicates that the change in the number of nuclei, depending on φc and φh, can be treated successfully by the present kinetic approach for crystal growth." @default.
• W2122535885 created "2016-06-24" @default.
• W2122535885 creator A5022739665 @default.
• W2122535885 creator A5063758922 @default.
• W2122535885 date "2004-12-20" @default.
• W2122535885 modified "2023-10-16" @default.
• W2122535885 title "Crystal Nucleation and Growth in Lithium Diborate Glass by Thermal Analysis" @default.
• W2122535885 cites W1910378497 @default.
• W2122535885 cites W2001308987 @default.
• W2122535885 cites W2008854263 @default.
• W2122535885 cites W2017043259 @default.
• W2122535885 cites W2026085516 @default.
• W2122535885 cites W2035634141 @default.
• W2122535885 cites W2042657612 @default.
• W2122535885 cites W2045581650 @default.
• W2122535885 cites W2054525145 @default.
• W2122535885 cites W2063532700 @default.
• W2122535885 cites W2069321098 @default.
• W2122535885 cites W2084777440 @default.
• W2122535885 cites W2091654061 @default.
• W2122535885 cites W2095018772 @default.
• W2122535885 cites W2097597965 @default.
• W2122535885 cites W2103718996 @default.
• W2122535885 cites W2118396678 @default.
• W2122535885 cites W2156414889 @default.
• W2122535885 cites W2158595960 @default.
• W2122535885 cites W4236739280 @default.
• W2122535885 doi "https://doi.org/10.1111/j.1151-2916.2000.tb01460.x" @default.
• W2122535885 hasPublicationYear "2004" @default.
• W2122535885 type Work @default.
• W2122535885 sameAs 2122535885 @default.
• W2122535885 citedByCount "30" @default.
• W2122535885 countsByYear W21225358852012 @default.
• W2122535885 countsByYear W21225358852013 @default.
• W2122535885 countsByYear W21225358852014 @default.
• W2122535885 countsByYear W21225358852015 @default.
• W2122535885 countsByYear W21225358852017 @default.
• W2122535885 countsByYear W21225358852018 @default.
• W2122535885 countsByYear W21225358852019 @default.
• W2122535885 countsByYear W21225358852020 @default.
• W2122535885 countsByYear W21225358852021 @default.
• W2122535885 countsByYear W21225358852022 @default.
• W2122535885 countsByYear W21225358852023 @default.
• W2122535885 crossrefType "journal-article" @default.
• W2122535885 hasAuthorship W2122535885A5022739665 @default.
• W2122535885 hasAuthorship W2122535885A5063758922 @default.
• W2122535885 hasConcept C112964491 @default.
• W2122535885 hasConcept C113196181 @default.
• W2122535885 hasConcept C120665830 @default.
• W2122535885 hasConcept C121332964 @default.
• W2122535885 hasConcept C122865956 @default.
• W2122535885 hasConcept C129446986 @default.
• W2122535885 hasConcept C159985019 @default.
• W2122535885 hasConcept C185592680 @default.
• W2122535885 hasConcept C191897082 @default.
• W2122535885 hasConcept C192562407 @default.
• W2122535885 hasConcept C199360897 @default.
• W2122535885 hasConcept C203036418 @default.
• W2122535885 hasConcept C204530211 @default.
• W2122535885 hasConcept C207114421 @default.
• W2122535885 hasConcept C26456737 @default.
• W2122535885 hasConcept C2777855556 @default.
• W2122535885 hasConcept C2781285689 @default.
• W2122535885 hasConcept C39353612 @default.
• W2122535885 hasConcept C39519442 @default.
• W2122535885 hasConcept C41008148 @default.
• W2122535885 hasConcept C43617362 @default.
• W2122535885 hasConcept C521977710 @default.
• W2122535885 hasConcept C61048295 @default.
• W2122535885 hasConcept C76804077 @default.
• W2122535885 hasConcept C8010536 @default.
• W2122535885 hasConcept C97355855 @default.
• W2122535885 hasConceptScore W2122535885C112964491 @default.
• W2122535885 hasConceptScore W2122535885C113196181 @default.
• W2122535885 hasConceptScore W2122535885C120665830 @default.
• W2122535885 hasConceptScore W2122535885C121332964 @default.
• W2122535885 hasConceptScore W2122535885C122865956 @default.
• W2122535885 hasConceptScore W2122535885C129446986 @default.
• W2122535885 hasConceptScore W2122535885C159985019 @default.
• W2122535885 hasConceptScore W2122535885C185592680 @default.
• W2122535885 hasConceptScore W2122535885C191897082 @default.
• W2122535885 hasConceptScore W2122535885C192562407 @default.
• W2122535885 hasConceptScore W2122535885C199360897 @default.
• W2122535885 hasConceptScore W2122535885C203036418 @default.
• W2122535885 hasConceptScore W2122535885C204530211 @default.
• W2122535885 hasConceptScore W2122535885C207114421 @default.
• W2122535885 hasConceptScore W2122535885C26456737 @default.
• W2122535885 hasConceptScore W2122535885C2777855556 @default.
• W2122535885 hasConceptScore W2122535885C2781285689 @default.
• W2122535885 hasConceptScore W2122535885C39353612 @default.
• W2122535885 hasConceptScore W2122535885C39519442 @default.
• W2122535885 hasConceptScore W2122535885C41008148 @default.
• W2122535885 hasConceptScore W2122535885C43617362 @default.
• W2122535885 hasConceptScore W2122535885C521977710 @default.
• W2122535885 hasConceptScore W2122535885C61048295 @default.
• W2122535885 hasConceptScore W2122535885C76804077 @default.
• W2122535885 hasConceptScore W2122535885C8010536 @default.
• W2122535885 hasConceptScore W2122535885C97355855 @default.

• next