- W2129170178 abstract "The use of pressed and sintered aluminum, obtained by the powder metallurgy route, to produce large quantities of near-net-shaped components is increasing rapidly in the automobile industry. The production of lightweight pieces of Al by powder metallurgy has attracted increasing attention due to its unique properties. Sintering helps develop mechanical strength and other properties in commercial alloys obtained by powder metallurgy. Sintering of Al can be achieved only upon formation of a liquid phase capable of destroying the extremely stable oxide layer on the surface of the Al particles. The aim of this investigation was to analyze the effect of compaction pressure on sintering of atomized ASTM 2124 type alloy. Powder characterization was carried out using scanning electron microscopy (SEM). The specimens were axially compacted at pressures of 500, 600 and 700 MPa. Differential scanning calorimetry (DSC) was carried out to determine the sintering temperature of the alloy powder. The specimens were sintered at 570° C. Characterization of the sintered material consisted of density measurements and optical as well as SEM examinations. Nevertheless, even the low recycling cost of Al , what increases its useful time and stabilizes its value, the large amount of energy required to obtain it reduce its application." @default.
- W2129170178 created "2016-06-24" @default.
- W2129170178 creator A5018592663 @default.
- W2129170178 creator A5021116847 @default.
- W2129170178 creator A5040145123 @default.
- W2129170178 creator A5069137990 @default.
- W2129170178 date "2010-10-01" @default.
- W2129170178 modified "2023-09-23" @default.
- W2129170178 title "Effect of Compacting Pressure on Liquid Phase Sintering of ASTM 2124 Alloy" @default.
- W2129170178 cites W1964710468 @default.
- W2129170178 cites W2071720287 @default.
- W2129170178 cites W2076361133 @default.
- W2129170178 cites W4210963906 @default.
- W2129170178 doi "https://doi.org/10.4028/www.scientific.net/msf.660-661.623" @default.
- W2129170178 hasPublicationYear "2010" @default.
- W2129170178 type Work @default.
- W2129170178 sameAs 2129170178 @default.
- W2129170178 citedByCount "1" @default.
- W2129170178 countsByYear W21291701782015 @default.
- W2129170178 crossrefType "journal-article" @default.
- W2129170178 hasAuthorship W2129170178A5018592663 @default.
- W2129170178 hasAuthorship W2129170178A5021116847 @default.
- W2129170178 hasAuthorship W2129170178A5040145123 @default.
- W2129170178 hasAuthorship W2129170178A5069137990 @default.
- W2129170178 hasConcept C121332964 @default.
- W2129170178 hasConcept C159985019 @default.
- W2129170178 hasConcept C178790620 @default.
- W2129170178 hasConcept C185592680 @default.
- W2129170178 hasConcept C191897082 @default.
- W2129170178 hasConcept C192562407 @default.
- W2129170178 hasConcept C196715460 @default.
- W2129170178 hasConcept C26771246 @default.
- W2129170178 hasConcept C2777581544 @default.
- W2129170178 hasConcept C2780026712 @default.
- W2129170178 hasConcept C39519442 @default.
- W2129170178 hasConcept C44280652 @default.
- W2129170178 hasConcept C7794659 @default.
- W2129170178 hasConcept C87976508 @default.
- W2129170178 hasConcept C97355855 @default.
- W2129170178 hasConceptScore W2129170178C121332964 @default.
- W2129170178 hasConceptScore W2129170178C159985019 @default.
- W2129170178 hasConceptScore W2129170178C178790620 @default.
- W2129170178 hasConceptScore W2129170178C185592680 @default.
- W2129170178 hasConceptScore W2129170178C191897082 @default.
- W2129170178 hasConceptScore W2129170178C192562407 @default.
- W2129170178 hasConceptScore W2129170178C196715460 @default.
- W2129170178 hasConceptScore W2129170178C26771246 @default.
- W2129170178 hasConceptScore W2129170178C2777581544 @default.
- W2129170178 hasConceptScore W2129170178C2780026712 @default.
- W2129170178 hasConceptScore W2129170178C39519442 @default.
- W2129170178 hasConceptScore W2129170178C44280652 @default.
- W2129170178 hasConceptScore W2129170178C7794659 @default.
- W2129170178 hasConceptScore W2129170178C87976508 @default.
- W2129170178 hasConceptScore W2129170178C97355855 @default.
- W2129170178 hasLocation W21291701781 @default.
- W2129170178 hasOpenAccess W2129170178 @default.
- W2129170178 hasPrimaryLocation W21291701781 @default.
- W2129170178 hasRelatedWork W1980188376 @default.
- W2129170178 hasRelatedWork W2054243438 @default.
- W2129170178 hasRelatedWork W2094830166 @default.
- W2129170178 hasRelatedWork W2183090839 @default.
- W2129170178 hasRelatedWork W2359655419 @default.
- W2129170178 hasRelatedWork W2363223004 @default.
- W2129170178 hasRelatedWork W2744534931 @default.
- W2129170178 hasRelatedWork W2793004223 @default.
- W2129170178 hasRelatedWork W3082170855 @default.
- W2129170178 hasRelatedWork W3187929430 @default.
- W2129170178 hasVolume "660-661" @default.
- W2129170178 isParatext "false" @default.
- W2129170178 isRetracted "false" @default.
- W2129170178 magId "2129170178" @default.
- W2129170178 workType "article" @default.