• W2141328686 abstract "The aim of the study was to evaluate the effect of annealing on the nanostructure and hardness of Co-Cr metal ceramic samples that were fabricated with a direct metal laser sintering (DMLS) technique.Five groups of Co-Cr dental alloy samples were manufactured in a rectangular form measuring 4 × 2 × 2 mm. Samples fabricated by a conventional casting technique (Group I) and prefabricated milling blanks (Group II) were examined as conventional technique groups. The DMLS samples were randomly divided into three groups as not annealed (Group III), annealed in argon atmosphere (Group IV), or annealed in oxygen atmosphere (Group V). The nanostructure was examined with the small-angle X-ray scattering method. The Rockwell hardness test was used to measure the hardness changes in each group, and the means and standard deviations were statistically analyzed by one-way ANOVA for comparison of continuous variables and Tukey's HSD test was used for post hoc analysis. P values of <.05 were accepted as statistically significant.The general nanostructures of the samples were composed of small spherical entities stacked atop one another in dendritic form. All groups also displayed different hardness values depending on the manufacturing technique. The annealing procedure and environment directly affected both the nanostructure and hardness of the Co-Cr alloy. Group III exhibited a non-homogeneous structure and increased hardness (48.16 ± 3.02 HRC) because the annealing process was incomplete and the inner stress was not relieved. Annealing in argon atmosphere of Group IV not only relieved the inner stresses but also decreased the hardness (27.40 ± 3.98 HRC). The results of fitting function presented that Group IV was the most homogeneous product as the minimum bilayer thickness was measured (7.11 Å).After the manufacturing with DMLS technique, annealing in argon atmosphere is an essential process for Co-Cr metal ceramic substructures. The dentists should be familiar with the materials that are used in clinic for prosthodontics treatments." @default.
• W2141328686 created "2016-06-24" @default.
• W2141328686 creator A5019662851 @default.
• W2141328686 creator A5025013281 @default.
• W2141328686 creator A5027004723 @default.
• W2141328686 creator A5064435464 @default.
• W2141328686 creator A5079478266 @default.
• W2141328686 creator A5079870637 @default.
• W2141328686 creator A5089045906 @default.
• W2141328686 date "2013-01-01" @default.
• W2141328686 modified "2023-10-14" @default.
• W2141328686 title "Annealing of Co-Cr dental alloy: effects on nanostructure and Rockwell hardness" @default.
• W2141328686 cites W1964002867 @default.
• W2141328686 cites W1964466197 @default.
• W2141328686 cites W1967641004 @default.
• W2141328686 cites W1976324320 @default.
• W2141328686 cites W1982570372 @default.
• W2141328686 cites W1983972908 @default.
• W2141328686 cites W1984320354 @default.
• W2141328686 cites W1985839956 @default.
• W2141328686 cites W1994243421 @default.
• W2141328686 cites W2014012466 @default.
• W2141328686 cites W2030495855 @default.
• W2141328686 cites W2033966676 @default.
• W2141328686 cites W2050228286 @default.
• W2141328686 cites W2052132609 @default.
• W2141328686 cites W2055724878 @default.
• W2141328686 cites W2071289791 @default.
• W2141328686 cites W2078375891 @default.
• W2141328686 cites W2100357516 @default.
• W2141328686 cites W2109806789 @default.
• W2141328686 cites W2135728553 @default.
• W2141328686 cites W2140404087 @default.
• W2141328686 cites W2145806768 @default.
• W2141328686 cites W2145916339 @default.
• W2141328686 cites W2146548795 @default.
• W2141328686 cites W2152218322 @default.
• W2141328686 cites W2157166524 @default.
• W2141328686 cites W2157870672 @default.
• W2141328686 cites W2168628686 @default.
• W2141328686 cites W2260642538 @default.
• W2141328686 doi "https://doi.org/10.4047/jap.2013.5.4.471" @default.
• W2141328686 hasPubMedCentralId "https://www.ncbi.nlm.nih.gov/pmc/articles/3865205" @default.
• W2141328686 hasPubMedId "https://pubmed.ncbi.nlm.nih.gov/24353888" @default.
• W2141328686 hasPublicationYear "2013" @default.
• W2141328686 type Work @default.
• W2141328686 sameAs 2141328686 @default.
• W2141328686 citedByCount "41" @default.
• W2141328686 countsByYear W21413286862014 @default.
• W2141328686 countsByYear W21413286862015 @default.
• W2141328686 countsByYear W21413286862016 @default.
• W2141328686 countsByYear W21413286862017 @default.
• W2141328686 countsByYear W21413286862018 @default.
• W2141328686 countsByYear W21413286862019 @default.
• W2141328686 countsByYear W21413286862020 @default.
• W2141328686 countsByYear W21413286862021 @default.
• W2141328686 countsByYear W21413286862022 @default.
• W2141328686 countsByYear W21413286862023 @default.
• W2141328686 crossrefType "journal-article" @default.
• W2141328686 hasAuthorship W2141328686A5019662851 @default.
• W2141328686 hasAuthorship W2141328686A5025013281 @default.
• W2141328686 hasAuthorship W2141328686A5027004723 @default.
• W2141328686 hasAuthorship W2141328686A5064435464 @default.
• W2141328686 hasAuthorship W2141328686A5079478266 @default.
• W2141328686 hasAuthorship W2141328686A5079870637 @default.
• W2141328686 hasAuthorship W2141328686A5089045906 @default.
• W2141328686 hasBestOaLocation W21413286861 @default.
• W2141328686 hasConcept C133392424 @default.
• W2141328686 hasConcept C171250308 @default.
• W2141328686 hasConcept C186187911 @default.
• W2141328686 hasConcept C191897082 @default.
• W2141328686 hasConcept C192562407 @default.
• W2141328686 hasConcept C2775868795 @default.
• W2141328686 hasConcept C2777855556 @default.
• W2141328686 hasConcept C2780026712 @default.
• W2141328686 hasConcept C87976508 @default.
• W2141328686 hasConcept C96606946 @default.
• W2141328686 hasConceptScore W2141328686C133392424 @default.
• W2141328686 hasConceptScore W2141328686C171250308 @default.
• W2141328686 hasConceptScore W2141328686C186187911 @default.
• W2141328686 hasConceptScore W2141328686C191897082 @default.
• W2141328686 hasConceptScore W2141328686C192562407 @default.
• W2141328686 hasConceptScore W2141328686C2775868795 @default.
• W2141328686 hasConceptScore W2141328686C2777855556 @default.
• W2141328686 hasConceptScore W2141328686C2780026712 @default.
• W2141328686 hasConceptScore W2141328686C87976508 @default.
• W2141328686 hasConceptScore W2141328686C96606946 @default.
• W2141328686 hasIssue "4" @default.
• W2141328686 hasLocation W21413286861 @default.
• W2141328686 hasLocation W21413286862 @default.
• W2141328686 hasLocation W21413286863 @default.
• W2141328686 hasLocation W21413286864 @default.
• W2141328686 hasOpenAccess W2141328686 @default.
• W2141328686 hasPrimaryLocation W21413286861 @default.
• W2141328686 hasRelatedWork W2067023182 @default.
• W2141328686 hasRelatedWork W2141328686 @default.
• W2141328686 hasRelatedWork W2351816252 @default.
• W2141328686 hasRelatedWork W2375172051 @default.

• next