- W2154540897 abstract "Fatigue tests at 600°C in air were performed on U-notch specimens of wrought IN718, using l-l-l-l and 1-20-l-l trapezoidal cycles. SEM examination and acetate replication was used to study crack initiation and growth. In support of the fatigue tests, thermal exposure experiments were performed on unstressed specimens to study surface and sub-surface primary carbide oxidation. Compared to a 1 second dwell, a dwell time of 20 seconds at maximum load had a beneficial effect on fatigue lifetime. Polishing the U-notch to remove broaching marks also had a beneficial effect on fatigue life. Multi-site crack initiation along the root of the U-notch was observed in fatigue specimens. Many of the cracks initiated at bulge-like features, associated with the oxidation of sub-surface primary carbides. Crack initiation was first observed as early as 12% of the total fatigue life, with further crack initiation occurring as tests progressed. Short cracks in the U-notches grew at a constant rate, except when interactions between parallel cracks resulted in crack arrest or coalescence. Significant crack coalescence occurred towards the end of the fatigue life, producing a dominant defect which propagated rapidly to failure. Surface eruptions and localised surface deformation were observed in fatigue and unstressed thermal exposure specimens, demonstrating a considerable volume expansion when primary (Nb,Ti)C carbides oxidised. It is proposed that the misfit strains due to primary carbide oxidation were superimposed on the plastic strain field in the U-notch due to external loading. This would create local strains high enough to cause rupture of the matrix, hence initiating a fatigue crack." @default.
- W2154540897 created "2016-06-24" @default.
- W2154540897 creator A5036983026 @default.
- W2154540897 creator A5060903591 @default.
- W2154540897 creator A5083280016 @default.
- W2154540897 date "2000-01-01" @default.
- W2154540897 modified "2023-09-26" @default.
- W2154540897 title "Effect of Oxidation on High Temperature Fatigue Crack Initiation and Short Crack Growth in Inconel 718" @default.
- W2154540897 cites W1966596642 @default.
- W2154540897 cites W1967051057 @default.
- W2154540897 cites W1969524148 @default.
- W2154540897 cites W1972430324 @default.
- W2154540897 cites W1975157821 @default.
- W2154540897 cites W1988483120 @default.
- W2154540897 cites W1988724527 @default.
- W2154540897 cites W1994842046 @default.
- W2154540897 cites W2008432616 @default.
- W2154540897 cites W2013333935 @default.
- W2154540897 cites W2013533391 @default.
- W2154540897 cites W2014773668 @default.
- W2154540897 cites W2052532925 @default.
- W2154540897 cites W2054442585 @default.
- W2154540897 cites W2056671416 @default.
- W2154540897 cites W2090295667 @default.
- W2154540897 cites W2108623911 @default.
- W2154540897 cites W2125121216 @default.
- W2154540897 cites W2138450295 @default.
- W2154540897 cites W2144592719 @default.
- W2154540897 cites W2163949126 @default.
- W2154540897 cites W2334483273 @default.
- W2154540897 cites W567635880 @default.
- W2154540897 doi "https://doi.org/10.7449/2000/superalloys_2000_435_444" @default.
- W2154540897 hasPublicationYear "2000" @default.
- W2154540897 type Work @default.
- W2154540897 sameAs 2154540897 @default.
- W2154540897 citedByCount "7" @default.
- W2154540897 countsByYear W21545408972014 @default.
- W2154540897 countsByYear W21545408972018 @default.
- W2154540897 countsByYear W21545408972019 @default.
- W2154540897 countsByYear W21545408972020 @default.
- W2154540897 countsByYear W21545408972023 @default.
- W2154540897 crossrefType "proceedings-article" @default.
- W2154540897 hasAuthorship W2154540897A5036983026 @default.
- W2154540897 hasAuthorship W2154540897A5060903591 @default.
- W2154540897 hasAuthorship W2154540897A5083280016 @default.
- W2154540897 hasConcept C159985019 @default.
- W2154540897 hasConcept C191897082 @default.
- W2154540897 hasConcept C192562407 @default.
- W2154540897 hasConcept C2778703219 @default.
- W2154540897 hasConcept C2780026712 @default.
- W2154540897 hasConcept C2985278600 @default.
- W2154540897 hasConcept C59085676 @default.
- W2154540897 hasConcept C69809600 @default.
- W2154540897 hasConcept C75512024 @default.
- W2154540897 hasConceptScore W2154540897C159985019 @default.
- W2154540897 hasConceptScore W2154540897C191897082 @default.
- W2154540897 hasConceptScore W2154540897C192562407 @default.
- W2154540897 hasConceptScore W2154540897C2778703219 @default.
- W2154540897 hasConceptScore W2154540897C2780026712 @default.
- W2154540897 hasConceptScore W2154540897C2985278600 @default.
- W2154540897 hasConceptScore W2154540897C59085676 @default.
- W2154540897 hasConceptScore W2154540897C69809600 @default.
- W2154540897 hasConceptScore W2154540897C75512024 @default.
- W2154540897 hasLocation W21545408971 @default.
- W2154540897 hasOpenAccess W2154540897 @default.
- W2154540897 hasPrimaryLocation W21545408971 @default.
- W2154540897 hasRelatedWork W1599511694 @default.
- W2154540897 hasRelatedWork W2025469295 @default.
- W2154540897 hasRelatedWork W2030880137 @default.
- W2154540897 hasRelatedWork W2048217115 @default.
- W2154540897 hasRelatedWork W2049617453 @default.
- W2154540897 hasRelatedWork W2076538527 @default.
- W2154540897 hasRelatedWork W2085413320 @default.
- W2154540897 hasRelatedWork W2143829778 @default.
- W2154540897 hasRelatedWork W2410586433 @default.
- W2154540897 hasRelatedWork W1878506120 @default.
- W2154540897 isParatext "false" @default.
- W2154540897 isRetracted "false" @default.
- W2154540897 magId "2154540897" @default.
- W2154540897 workType "article" @default.