- W2155341401 abstract "Joints between a silicon-germanium thermoelectric semiconductor and electrodes were prepared by hot-pressing. Tungsten or carbon electrodes were joined to either side of n-type Si/sub 0.8/Ge/sub 0.2/ (P 0.3 at.%) respectively, with thin sheets of titanium foil inserted between them, and then pressed and joined at 1523 K in vacuum. The size of the resulting electrode/SiGe semiconductor/electrode units measured 5 mm/spl times/ 5 mm/spl times/9 mm. Observations through SEM and EPMA showed the presence of many voids in the junction layers of the SiGe/tungsten electrodes, whereas the SiGe/carbon electrodes exhibited no voids in their junction layers. In the SiGe/carbon electrodes, the titanium atoms were enriched in the junction layer, and other atoms also remained undiffused. In the SiGe/tungsten electrodes, the tungsten and silicon atoms showed counter diffusion. Resistance and Seebeck coefficient of the carbon/SiGe/carbon electrodes were measured in the temperature range from 600 to 1100 K. Resistance ranged from 0.012 to 0.015 /spl Omega/, and the Seebeck coefficient from 200/spl times/10/sup -6/ to 250/spl times/10/sup -6/ V/K. To evaluate the upper limit of heating dependence, the carbon/SiGe/carbon electrodes were exposed in an argon atmosphere at 1273 K and 1373 K for 300 hours. After exposure testing, SEM observation showed the presence of many voids in the junction layer of the SiGe/carbon electrode, which had not previously shown any voids either at the stage of joining by hot-pressing or exposure at 1273 K." @default.
- W2155341401 created "2016-06-24" @default.
- W2155341401 creator A5014454676 @default.
- W2155341401 creator A5015504655 @default.
- W2155341401 creator A5052600945 @default.
- W2155341401 creator A5055006595 @default.
- W2155341401 creator A5056448365 @default.
- W2155341401 creator A5071709095 @default.
- W2155341401 date "2002-11-23" @default.
- W2155341401 modified "2023-09-28" @default.
- W2155341401 title "Thermoelectric semiconductor and electrode-fabrication and evaluation of SiGe/electrode" @default.
- W2155341401 doi "https://doi.org/10.1109/ict.1997.667602" @default.
- W2155341401 hasPublicationYear "2002" @default.
- W2155341401 type Work @default.
- W2155341401 sameAs 2155341401 @default.
- W2155341401 citedByCount "2" @default.
- W2155341401 countsByYear W21553414012013 @default.
- W2155341401 crossrefType "proceedings-article" @default.
- W2155341401 hasAuthorship W2155341401A5014454676 @default.
- W2155341401 hasAuthorship W2155341401A5015504655 @default.
- W2155341401 hasAuthorship W2155341401A5052600945 @default.
- W2155341401 hasAuthorship W2155341401A5055006595 @default.
- W2155341401 hasAuthorship W2155341401A5056448365 @default.
- W2155341401 hasAuthorship W2155341401A5071709095 @default.
- W2155341401 hasConcept C104779481 @default.
- W2155341401 hasConcept C108225325 @default.
- W2155341401 hasConcept C112625512 @default.
- W2155341401 hasConcept C113196181 @default.
- W2155341401 hasConcept C121332964 @default.
- W2155341401 hasConcept C140205800 @default.
- W2155341401 hasConcept C147789679 @default.
- W2155341401 hasConcept C159985019 @default.
- W2155341401 hasConcept C17525397 @default.
- W2155341401 hasConcept C185592680 @default.
- W2155341401 hasConcept C191897082 @default.
- W2155341401 hasConcept C192562407 @default.
- W2155341401 hasConcept C2779227376 @default.
- W2155341401 hasConcept C43617362 @default.
- W2155341401 hasConcept C49040817 @default.
- W2155341401 hasConcept C506065880 @default.
- W2155341401 hasConcept C542268612 @default.
- W2155341401 hasConcept C544956773 @default.
- W2155341401 hasConcept C63024428 @default.
- W2155341401 hasConcept C97346530 @default.
- W2155341401 hasConcept C97355855 @default.
- W2155341401 hasConceptScore W2155341401C104779481 @default.
- W2155341401 hasConceptScore W2155341401C108225325 @default.
- W2155341401 hasConceptScore W2155341401C112625512 @default.
- W2155341401 hasConceptScore W2155341401C113196181 @default.
- W2155341401 hasConceptScore W2155341401C121332964 @default.
- W2155341401 hasConceptScore W2155341401C140205800 @default.
- W2155341401 hasConceptScore W2155341401C147789679 @default.
- W2155341401 hasConceptScore W2155341401C159985019 @default.
- W2155341401 hasConceptScore W2155341401C17525397 @default.
- W2155341401 hasConceptScore W2155341401C185592680 @default.
- W2155341401 hasConceptScore W2155341401C191897082 @default.
- W2155341401 hasConceptScore W2155341401C192562407 @default.
- W2155341401 hasConceptScore W2155341401C2779227376 @default.
- W2155341401 hasConceptScore W2155341401C43617362 @default.
- W2155341401 hasConceptScore W2155341401C49040817 @default.
- W2155341401 hasConceptScore W2155341401C506065880 @default.
- W2155341401 hasConceptScore W2155341401C542268612 @default.
- W2155341401 hasConceptScore W2155341401C544956773 @default.
- W2155341401 hasConceptScore W2155341401C63024428 @default.
- W2155341401 hasConceptScore W2155341401C97346530 @default.
- W2155341401 hasConceptScore W2155341401C97355855 @default.
- W2155341401 hasLocation W21553414011 @default.
- W2155341401 hasOpenAccess W2155341401 @default.
- W2155341401 hasPrimaryLocation W21553414011 @default.
- W2155341401 hasRelatedWork W1969381622 @default.
- W2155341401 hasRelatedWork W1977991479 @default.
- W2155341401 hasRelatedWork W1998672177 @default.
- W2155341401 hasRelatedWork W2020769062 @default.
- W2155341401 hasRelatedWork W2048208733 @default.
- W2155341401 hasRelatedWork W2054207401 @default.
- W2155341401 hasRelatedWork W2067844473 @default.
- W2155341401 hasRelatedWork W2157338538 @default.
- W2155341401 hasRelatedWork W2329856647 @default.
- W2155341401 hasRelatedWork W2338176868 @default.
- W2155341401 hasRelatedWork W3011159563 @default.
- W2155341401 hasRelatedWork W3092955386 @default.
- W2155341401 hasRelatedWork W640959199 @default.
- W2155341401 hasRelatedWork W2781804460 @default.
- W2155341401 hasRelatedWork W2820917995 @default.
- W2155341401 hasRelatedWork W2824053262 @default.
- W2155341401 hasRelatedWork W2842062759 @default.
- W2155341401 hasRelatedWork W2850493631 @default.
- W2155341401 hasRelatedWork W2866802008 @default.
- W2155341401 hasRelatedWork W2880788466 @default.
- W2155341401 isParatext "false" @default.
- W2155341401 isRetracted "false" @default.
- W2155341401 magId "2155341401" @default.
- W2155341401 workType "article" @default.