- W2164368478 abstract "The rates of corrosion of tin specimens either intermittently or continuously immersed in several alkaline solutions have been compared. Similar solutions have been used to wash specimens of tinned steel that were exposed to the weather between washes in imitation of the service life of some tinned steel containers.The relative corrosive action of various solutions on intermittently immersed tin depends on the experimental conditions and may differ from that observed when the metal is immersed continuously. The results obtained with short periods of immersion are strongly influenced by the variation with the nature of the solution, the temperature and the condition of the metal surface, and of a period of delay between immersion of the metal and the onset of corrosion. A high rate of corrosion during the period between removal of the metal from the test solution and rinsing also introduces a potential cause of variation in the results of intermittent-immersion tests.The deterioration in the protective quality of a tin coating on steel periodically washed in an alkaline solution can be predicted only moderately well from measurements of the corrosion rate of tin immersed in the solution. This deterioration results more from the enlargement of new pores formed in the coating during periods of exposure to the weather than from general dissolution of the tin, and silicates appear to restrain this action.In the conditions of the tests employed, with solutions of equivalent caustic alkalinity, sodium hydroxide, carbonate and phosphate had similar effects; sodium silicate (2 : 1) produced less deterioration; sodium metasilicate much less and sodium silicate (1 : 2), almost none. Additions of sodium sulphite to the washing solution had a negligible effect but additions of sodium chromate preserved both tin and steel. Additions of sodium hypochlorite either to washing or rinsing solutions accelerated deterioration of the coating except when made to solutions of sodium metasilicate or of sodium silicate (1 : 2)." @default.
- W2164368478 created "2016-06-24" @default.
- W2164368478 creator A5049405253 @default.
- W2164368478 creator A5081787591 @default.
- W2164368478 date "2007-05-04" @default.
- W2164368478 modified "2023-10-17" @default.
- W2164368478 title "The effects of repeated washing of tinned steel with alkaline solutions on its resistance to rusting" @default.
- W2164368478 cites W2036769813 @default.
- W2164368478 cites W2061610928 @default.
- W2164368478 cites W2129384950 @default.
- W2164368478 cites W2142085690 @default.
- W2164368478 cites W2613937617 @default.
- W2164368478 cites W2614988251 @default.
- W2164368478 doi "https://doi.org/10.1002/jctb.5010050808" @default.
- W2164368478 hasPublicationYear "2007" @default.
- W2164368478 type Work @default.
- W2164368478 sameAs 2164368478 @default.
- W2164368478 citedByCount "3" @default.
- W2164368478 crossrefType "journal-article" @default.
- W2164368478 hasAuthorship W2164368478A5049405253 @default.
- W2164368478 hasAuthorship W2164368478A5081787591 @default.
- W2164368478 hasConcept C147789679 @default.
- W2164368478 hasConcept C159985019 @default.
- W2164368478 hasConcept C178790620 @default.
- W2164368478 hasConcept C185592680 @default.
- W2164368478 hasConcept C191897082 @default.
- W2164368478 hasConcept C192562407 @default.
- W2164368478 hasConcept C199068039 @default.
- W2164368478 hasConcept C202444582 @default.
- W2164368478 hasConcept C20625102 @default.
- W2164368478 hasConcept C2778562268 @default.
- W2164368478 hasConcept C2778657360 @default.
- W2164368478 hasConcept C2779947509 @default.
- W2164368478 hasConcept C2781448156 @default.
- W2164368478 hasConcept C33923547 @default.
- W2164368478 hasConcept C45812177 @default.
- W2164368478 hasConcept C525849907 @default.
- W2164368478 hasConcept C537181965 @default.
- W2164368478 hasConcept C544153396 @default.
- W2164368478 hasConcept C88380143 @default.
- W2164368478 hasConceptScore W2164368478C147789679 @default.
- W2164368478 hasConceptScore W2164368478C159985019 @default.
- W2164368478 hasConceptScore W2164368478C178790620 @default.
- W2164368478 hasConceptScore W2164368478C185592680 @default.
- W2164368478 hasConceptScore W2164368478C191897082 @default.
- W2164368478 hasConceptScore W2164368478C192562407 @default.
- W2164368478 hasConceptScore W2164368478C199068039 @default.
- W2164368478 hasConceptScore W2164368478C202444582 @default.
- W2164368478 hasConceptScore W2164368478C20625102 @default.
- W2164368478 hasConceptScore W2164368478C2778562268 @default.
- W2164368478 hasConceptScore W2164368478C2778657360 @default.
- W2164368478 hasConceptScore W2164368478C2779947509 @default.
- W2164368478 hasConceptScore W2164368478C2781448156 @default.
- W2164368478 hasConceptScore W2164368478C33923547 @default.
- W2164368478 hasConceptScore W2164368478C45812177 @default.
- W2164368478 hasConceptScore W2164368478C525849907 @default.
- W2164368478 hasConceptScore W2164368478C537181965 @default.
- W2164368478 hasConceptScore W2164368478C544153396 @default.
- W2164368478 hasConceptScore W2164368478C88380143 @default.
- W2164368478 hasIssue "8" @default.
- W2164368478 hasLocation W21643684781 @default.
- W2164368478 hasOpenAccess W2164368478 @default.
- W2164368478 hasPrimaryLocation W21643684781 @default.
- W2164368478 hasRelatedWork W2013665547 @default.
- W2164368478 hasRelatedWork W2022507789 @default.
- W2164368478 hasRelatedWork W2070338356 @default.
- W2164368478 hasRelatedWork W2072503384 @default.
- W2164368478 hasRelatedWork W2079516676 @default.
- W2164368478 hasRelatedWork W2312389078 @default.
- W2164368478 hasRelatedWork W2748952813 @default.
- W2164368478 hasRelatedWork W2899084033 @default.
- W2164368478 hasRelatedWork W3046190049 @default.
- W2164368478 hasRelatedWork W4231413117 @default.
- W2164368478 hasVolume "5" @default.
- W2164368478 isParatext "false" @default.
- W2164368478 isRetracted "false" @default.
- W2164368478 magId "2164368478" @default.
- W2164368478 workType "article" @default.