- W2174917967 abstract "The effects of coating (with Codep B) and of creep-fatigue interactions on creep and fatigue properties of the turbine blade material Rene 80 at 900 °C were investigated. Coating reduced the high cycle fatigue life because of crack initiation at brittle particles in the coating. This process played no role for creep, where crack initiation took place at carbides in the base metal. Coating affected the creep properties by changes of the load-bearing cross-section: Initially the coating Increased this cross-section and consequently the minimum creep rate decreased. However, after exhaustion of the coating ductility coating cracks reduced the load-bearing area and thereby reduced the creep rupture life. Both for coated and uncoated Rene 80 short prior creep times increased subsequent fatigue life since the interfacial dislocation network around the cuboidal y' precipitates densified during creep. Long prior creep times were unfavourable because of coarsening of the y' spheroids. Prior fatigue had little influence on creep rupture life since the dislocations introduced during fatigue were annealed out during creep." @default.
- W2174917967 created "2016-06-24" @default.
- W2174917967 creator A5047252726 @default.
- W2174917967 date "1985-10-29" @default.
- W2174917967 modified "2023-10-01" @default.
- W2174917967 title "Creep, fatigue and their interaction in coated and uncoated René 80" @default.
- W2174917967 hasPublicationYear "1985" @default.
- W2174917967 type Work @default.
- W2174917967 sameAs 2174917967 @default.
- W2174917967 citedByCount "0" @default.
- W2174917967 crossrefType "journal-article" @default.
- W2174917967 hasAuthorship W2174917967A5047252726 @default.
- W2174917967 hasConcept C136478896 @default.
- W2174917967 hasConcept C149912024 @default.
- W2174917967 hasConcept C159985019 @default.
- W2174917967 hasConcept C191897082 @default.
- W2174917967 hasConcept C192562407 @default.
- W2174917967 hasConcept C199978012 @default.
- W2174917967 hasConcept C205649164 @default.
- W2174917967 hasConcept C2776512210 @default.
- W2174917967 hasConcept C2781448156 @default.
- W2174917967 hasConcept C58640448 @default.
- W2174917967 hasConceptScore W2174917967C136478896 @default.
- W2174917967 hasConceptScore W2174917967C149912024 @default.
- W2174917967 hasConceptScore W2174917967C159985019 @default.
- W2174917967 hasConceptScore W2174917967C191897082 @default.
- W2174917967 hasConceptScore W2174917967C192562407 @default.
- W2174917967 hasConceptScore W2174917967C199978012 @default.
- W2174917967 hasConceptScore W2174917967C205649164 @default.
- W2174917967 hasConceptScore W2174917967C2776512210 @default.
- W2174917967 hasConceptScore W2174917967C2781448156 @default.
- W2174917967 hasConceptScore W2174917967C58640448 @default.
- W2174917967 hasLocation W21749179671 @default.
- W2174917967 hasOpenAccess W2174917967 @default.
- W2174917967 hasPrimaryLocation W21749179671 @default.
- W2174917967 hasRelatedWork W134494151 @default.
- W2174917967 hasRelatedWork W190449425 @default.
- W2174917967 hasRelatedWork W199876853 @default.
- W2174917967 hasRelatedWork W2002666480 @default.
- W2174917967 hasRelatedWork W2022904511 @default.
- W2174917967 hasRelatedWork W2024436696 @default.
- W2174917967 hasRelatedWork W2041424619 @default.
- W2174917967 hasRelatedWork W2066128783 @default.
- W2174917967 hasRelatedWork W2071813847 @default.
- W2174917967 hasRelatedWork W2074517760 @default.
- W2174917967 hasRelatedWork W2080740155 @default.
- W2174917967 hasRelatedWork W2379800734 @default.
- W2174917967 hasRelatedWork W247169649 @default.
- W2174917967 hasRelatedWork W250327688 @default.
- W2174917967 hasRelatedWork W2514855248 @default.
- W2174917967 hasRelatedWork W2936590201 @default.
- W2174917967 hasRelatedWork W3090127334 @default.
- W2174917967 hasRelatedWork W3096670640 @default.
- W2174917967 hasRelatedWork W3201576150 @default.
- W2174917967 hasRelatedWork W2944323869 @default.
- W2174917967 isParatext "false" @default.
- W2174917967 isRetracted "false" @default.
- W2174917967 magId "2174917967" @default.
- W2174917967 workType "article" @default.