- W217907316 abstract "High-strength U-3/4 wt % Ti alloy in the form of 3.3-cm-diameter round and straight bar was produced. The starting constituents were derby uranium and titanium sponge. The constituents were vacuum-induction melted at 1350/sup 0/C and gang cast into preheated molds forming hot-topped ingots 13.3 cm in diameter. After homogenization, the ingots were converted to extrusion billets by cropping the hot-top and sawing the remainder in half. The billets were scalped to a diameter of 12.7 cm. They were then heated in a salt bath at 625/sup 0/C and forward extruded to a diameter of 4.1 cm. The reduction ratio was 10, and the extrusion constant averaged 25 tons per square inch. 11 refs., 10 figs., 8 tabs." @default.
- W217907316 created "2016-06-24" @default.
- W217907316 creator A5070105995 @default.
- W217907316 creator A5076968810 @default.
- W217907316 date "1987-08-07" @default.
- W217907316 modified "2023-09-27" @default.
- W217907316 title "Fabrication and properties of high-strength uranium-3/4 weight percent titanium alloy large-diameter straight bar stock" @default.
- W217907316 hasPublicationYear "1987" @default.
- W217907316 type Work @default.
- W217907316 sameAs 217907316 @default.
- W217907316 citedByCount "0" @default.
- W217907316 crossrefType "journal-article" @default.
- W217907316 hasAuthorship W217907316A5070105995 @default.
- W217907316 hasAuthorship W217907316A5076968810 @default.
- W217907316 hasConcept C130217890 @default.
- W217907316 hasConcept C136525101 @default.
- W217907316 hasConcept C142724271 @default.
- W217907316 hasConcept C159985019 @default.
- W217907316 hasConcept C18903297 @default.
- W217907316 hasConcept C191897082 @default.
- W217907316 hasConcept C192562407 @default.
- W217907316 hasConcept C204787440 @default.
- W217907316 hasConcept C2778722038 @default.
- W217907316 hasConcept C2778958987 @default.
- W217907316 hasConcept C2780026712 @default.
- W217907316 hasConcept C506065880 @default.
- W217907316 hasConcept C555451288 @default.
- W217907316 hasConcept C71924100 @default.
- W217907316 hasConcept C86803240 @default.
- W217907316 hasConceptScore W217907316C130217890 @default.
- W217907316 hasConceptScore W217907316C136525101 @default.
- W217907316 hasConceptScore W217907316C142724271 @default.
- W217907316 hasConceptScore W217907316C159985019 @default.
- W217907316 hasConceptScore W217907316C18903297 @default.
- W217907316 hasConceptScore W217907316C191897082 @default.
- W217907316 hasConceptScore W217907316C192562407 @default.
- W217907316 hasConceptScore W217907316C204787440 @default.
- W217907316 hasConceptScore W217907316C2778722038 @default.
- W217907316 hasConceptScore W217907316C2778958987 @default.
- W217907316 hasConceptScore W217907316C2780026712 @default.
- W217907316 hasConceptScore W217907316C506065880 @default.
- W217907316 hasConceptScore W217907316C555451288 @default.
- W217907316 hasConceptScore W217907316C71924100 @default.
- W217907316 hasConceptScore W217907316C86803240 @default.
- W217907316 hasLocation W2179073161 @default.
- W217907316 hasOpenAccess W217907316 @default.
- W217907316 hasPrimaryLocation W2179073161 @default.
- W217907316 isParatext "false" @default.
- W217907316 isRetracted "false" @default.
- W217907316 magId "217907316" @default.
- W217907316 workType "article" @default.