- W2196134637 abstract "Performance of graphite foil electrodes coated by porous carbon black (i.e., Vulcan) was investigated in comparison with metal electrodes for reverse electrodialysis (RED) application. The electrode slurry that was used for fabrication of the porous carbon-coated graphite foil is composed of 7.2 wt% of carbon black (Vulcan X-72), 0.8 wt% of a polymer binder (polyvinylidene fluoride, PVdF), and 92.0 wt% of a mixing solvent (dimethylacetamide, DMAc). Cyclic voltammograms of both the porous carbon (i.e., Vulcan)-coated graphite foil electrode and the graphite foil electrode without Vulcan showed good reversibility in the hexacyanoferrate(III) (i.e., Fe(CN)63−) and hexacyanoferrate(II) (i.e., Fe(CN)64−) redox couple and 1 M Na2SO4 at room temperature. However, anodic and cathodic current of the Vulcan-coated graphite foil electrode was much higher than those of the graphite foil electrode. Using a bench-scale RED stack, the current–voltage polarization curve of the Vulcan-coated graphite electrode was compared to that of metal electrodes such as iridium (Ir) and platinum (Pt). From the results, it was confirmed that resistance of four different electrodes increased with the following order: the Vulcan-coated graphite foil<the Ir-coated titanium (Ti) mesh<the Pt-coated Ti plate<the graphite foil. Moreover, the Vulcan-coated graphite foil showed 5–10% higher power density than the metal mesh electrodes. From the polarization curve of the Vulcan-coated graphite foil electrode, it was found that total resistance decreased as thickness and geometric surface area of the electrode increased." @default.
- W2196134637 created "2016-06-24" @default.
- W2196134637 creator A5026081925 @default.
- W2196134637 creator A5041130636 @default.
- W2196134637 creator A5056081741 @default.
- W2196134637 creator A5071808397 @default.
- W2196134637 creator A5072107405 @default.
- W2196134637 creator A5077139018 @default.
- W2196134637 creator A5078512668 @default.
- W2196134637 creator A5079454521 @default.
- W2196134637 date "2016-04-01" @default.
- W2196134637 modified "2023-09-26" @default.
- W2196134637 title "Porous carbon-coated graphite electrodes for energy production from salinity gradient using reverse electrodialysis" @default.
- W2196134637 cites W1971632431 @default.
- W2196134637 cites W1977549077 @default.
- W2196134637 cites W1985914364 @default.
- W2196134637 cites W1994598334 @default.
- W2196134637 cites W1994780933 @default.
- W2196134637 cites W2006856011 @default.
- W2196134637 cites W2017930213 @default.
- W2196134637 cites W2021120899 @default.
- W2196134637 cites W2028241950 @default.
- W2196134637 cites W2041156939 @default.
- W2196134637 cites W2044560300 @default.
- W2196134637 cites W2048454971 @default.
- W2196134637 cites W2058747299 @default.
- W2196134637 cites W2061297960 @default.
- W2196134637 cites W2068682971 @default.
- W2196134637 cites W2084902380 @default.
- W2196134637 cites W2093156170 @default.
- W2196134637 cites W2104762466 @default.
- W2196134637 cites W2127628079 @default.
- W2196134637 cites W2163250623 @default.
- W2196134637 cites W4254720078 @default.
- W2196134637 doi "https://doi.org/10.1016/j.jpcs.2015.12.006" @default.
- W2196134637 hasPublicationYear "2016" @default.
- W2196134637 type Work @default.
- W2196134637 sameAs 2196134637 @default.
- W2196134637 citedByCount "24" @default.
- W2196134637 countsByYear W21961346372016 @default.
- W2196134637 countsByYear W21961346372017 @default.
- W2196134637 countsByYear W21961346372018 @default.
- W2196134637 countsByYear W21961346372019 @default.
- W2196134637 countsByYear W21961346372020 @default.
- W2196134637 countsByYear W21961346372021 @default.
- W2196134637 countsByYear W21961346372022 @default.
- W2196134637 countsByYear W21961346372023 @default.
- W2196134637 crossrefType "journal-article" @default.
- W2196134637 hasAuthorship W2196134637A5026081925 @default.
- W2196134637 hasAuthorship W2196134637A5041130636 @default.
- W2196134637 hasAuthorship W2196134637A5056081741 @default.
- W2196134637 hasAuthorship W2196134637A5071808397 @default.
- W2196134637 hasAuthorship W2196134637A5072107405 @default.
- W2196134637 hasAuthorship W2196134637A5077139018 @default.
- W2196134637 hasAuthorship W2196134637A5078512668 @default.
- W2196134637 hasAuthorship W2196134637A5079454521 @default.
- W2196134637 hasConcept C147789679 @default.
- W2196134637 hasConcept C159985019 @default.
- W2196134637 hasConcept C17525397 @default.
- W2196134637 hasConcept C176933379 @default.
- W2196134637 hasConcept C185592680 @default.
- W2196134637 hasConcept C192562407 @default.
- W2196134637 hasConcept C2779698641 @default.
- W2196134637 hasConcept C44038986 @default.
- W2196134637 hasConcept C7363328 @default.
- W2196134637 hasConceptScore W2196134637C147789679 @default.
- W2196134637 hasConceptScore W2196134637C159985019 @default.
- W2196134637 hasConceptScore W2196134637C17525397 @default.
- W2196134637 hasConceptScore W2196134637C176933379 @default.
- W2196134637 hasConceptScore W2196134637C185592680 @default.
- W2196134637 hasConceptScore W2196134637C192562407 @default.
- W2196134637 hasConceptScore W2196134637C2779698641 @default.
- W2196134637 hasConceptScore W2196134637C44038986 @default.
- W2196134637 hasConceptScore W2196134637C7363328 @default.
- W2196134637 hasLocation W21961346371 @default.
- W2196134637 hasOpenAccess W2196134637 @default.
- W2196134637 hasPrimaryLocation W21961346371 @default.
- W2196134637 hasRelatedWork W1515783128 @default.
- W2196134637 hasRelatedWork W1993353379 @default.
- W2196134637 hasRelatedWork W2016101288 @default.
- W2196134637 hasRelatedWork W2047116889 @default.
- W2196134637 hasRelatedWork W2356189956 @default.
- W2196134637 hasRelatedWork W2380293314 @default.
- W2196134637 hasRelatedWork W2800765646 @default.
- W2196134637 hasRelatedWork W2943188944 @default.
- W2196134637 hasRelatedWork W3082440218 @default.
- W2196134637 hasRelatedWork W77208362 @default.
- W2196134637 hasVolume "91" @default.
- W2196134637 isParatext "false" @default.
- W2196134637 isRetracted "false" @default.
- W2196134637 magId "2196134637" @default.
- W2196134637 workType "article" @default.