• W2209540892 abstract "TiZrNbMoxVy high-entropy alloys (HEAs) with x = 0–2, y = 1 and y = 0.3, respectively, were designed and prepared by copper mold casting technology. The phase composition and stability of these HEAs were investigated. It is shown that the HEAs with low content of V are composed of only one type of bcc solid solution phase (SSP), and demonstrate excellent phase stability at 1273 K. The high content of V and Mo results in the formation of two types of bcc SSPs and the decrease of phase stability in the HEAs. Based on the previously proposed criteria, the formation ability of solid solution phase for this kind of HEAs was comprehensively evaluated. The compressive mechanical properties of the as-cast and annealed HEAs were measured. It has been found that Mo plays a strong solid solution strengthening effect on this kind of HEAs. Especially, TiZrNbMo0.3V0.3 has the yield strength and plastic strain of 1312 MPa and >50%, respectively, and still maintains the excellent plastic deformation ability even after annealed at 1273 K for 72 h. The strengthening effect in this kind of HEAs is considered to be due to the shear modulus mismatch. The solubility limit of HEAs is correspondent to shear modulus mismatch of 29." @default.
• W2209540892 created "2016-06-24" @default.
• W2209540892 creator A5006741800 @default.
• W2209540892 creator A5009953858 @default.
• W2209540892 creator A5012106887 @default.
• W2209540892 creator A5028687964 @default.
• W2209540892 creator A5034283326 @default.
• W2209540892 creator A5069716476 @default.
• W2209540892 creator A5074549597 @default.
• W2209540892 creator A5083043777 @default.
• W2209540892 date "2015-10-01" @default.
• W2209540892 modified "2023-10-14" @default.
• W2209540892 title "Phase composition and solid solution strengthening effect in TiZrNbMoV high-entropy alloys" @default.
• W2209540892 cites W1658338080 @default.
• W2209540892 cites W1970165422 @default.
• W2209540892 cites W1980574713 @default.
• W2209540892 cites W1980695249 @default.
• W2209540892 cites W1982726391 @default.
• W2209540892 cites W1992300997 @default.
• W2209540892 cites W1996359833 @default.
• W2209540892 cites W2000310380 @default.
• W2209540892 cites W2003975937 @default.
• W2209540892 cites W2007876110 @default.
• W2209540892 cites W2010953085 @default.
• W2209540892 cites W2016140457 @default.
• W2209540892 cites W2020462182 @default.
• W2209540892 cites W2025847715 @default.
• W2209540892 cites W2036745117 @default.
• W2209540892 cites W2038651671 @default.
• W2209540892 cites W2045291582 @default.
• W2209540892 cites W2049639367 @default.
• W2209540892 cites W2054168515 @default.
• W2209540892 cites W2058085399 @default.
• W2209540892 cites W2060666874 @default.
• W2209540892 cites W2060742044 @default.
• W2209540892 cites W2062453104 @default.
• W2209540892 cites W2068415766 @default.
• W2209540892 cites W2069811316 @default.
• W2209540892 cites W2072976701 @default.
• W2209540892 cites W2076855563 @default.
• W2209540892 cites W2079235125 @default.
• W2209540892 cites W2080443265 @default.
• W2209540892 cites W2086062149 @default.
• W2209540892 cites W2090989574 @default.
• W2209540892 cites W2091037363 @default.
• W2209540892 cites W2092703780 @default.
• W2209540892 cites W2094752119 @default.
• W2209540892 cites W2106528824 @default.
• W2209540892 cites W2110862556 @default.
• W2209540892 cites W2137374762 @default.
• W2209540892 cites W2158195347 @default.
• W2209540892 doi "https://doi.org/10.1016/j.matdes.2015.06.072" @default.
• W2209540892 hasPublicationYear "2015" @default.
• W2209540892 type Work @default.
• W2209540892 sameAs 2209540892 @default.
• W2209540892 citedByCount "166" @default.
• W2209540892 countsByYear W22095408922015 @default.
• W2209540892 countsByYear W22095408922016 @default.
• W2209540892 countsByYear W22095408922017 @default.
• W2209540892 countsByYear W22095408922018 @default.
• W2209540892 countsByYear W22095408922019 @default.
• W2209540892 countsByYear W22095408922020 @default.
• W2209540892 countsByYear W22095408922021 @default.
• W2209540892 countsByYear W22095408922022 @default.
• W2209540892 countsByYear W22095408922023 @default.
• W2209540892 crossrefType "journal-article" @default.
• W2209540892 hasAuthorship W2209540892A5006741800 @default.
• W2209540892 hasAuthorship W2209540892A5009953858 @default.
• W2209540892 hasAuthorship W2209540892A5012106887 @default.
• W2209540892 hasAuthorship W2209540892A5028687964 @default.
• W2209540892 hasAuthorship W2209540892A5034283326 @default.
• W2209540892 hasAuthorship W2209540892A5069716476 @default.
• W2209540892 hasAuthorship W2209540892A5074549597 @default.
• W2209540892 hasAuthorship W2209540892A5083043777 @default.
• W2209540892 hasConcept C138999460 @default.
• W2209540892 hasConcept C159985019 @default.
• W2209540892 hasConcept C178790620 @default.
• W2209540892 hasConcept C185592680 @default.
• W2209540892 hasConcept C191897082 @default.
• W2209540892 hasConcept C192562407 @default.
• W2209540892 hasConcept C193705005 @default.
• W2209540892 hasConcept C2780026712 @default.
• W2209540892 hasConcept C2780299837 @default.
• W2209540892 hasConcept C44280652 @default.
• W2209540892 hasConcept C79186407 @default.
• W2209540892 hasConceptScore W2209540892C138999460 @default.
• W2209540892 hasConceptScore W2209540892C159985019 @default.
• W2209540892 hasConceptScore W2209540892C178790620 @default.
• W2209540892 hasConceptScore W2209540892C185592680 @default.
• W2209540892 hasConceptScore W2209540892C191897082 @default.
• W2209540892 hasConceptScore W2209540892C192562407 @default.
• W2209540892 hasConceptScore W2209540892C193705005 @default.
• W2209540892 hasConceptScore W2209540892C2780026712 @default.
• W2209540892 hasConceptScore W2209540892C2780299837 @default.
• W2209540892 hasConceptScore W2209540892C44280652 @default.
• W2209540892 hasConceptScore W2209540892C79186407 @default.
• W2209540892 hasFunder F4320321001 @default.
• W2209540892 hasLocation W22095408921 @default.

• next