- W221570683 abstract "A partial-bonding interlaminar toughening concept was evaluated for resistance to impact and for behavior of a loaded hole. Perforated Mylar sheets were interleaved between all 24 plies of a graphite/epoxy quasi-isotropic lay-up. Specimens were impacted by aluminum spheres while under tensile or compressive loads. Impact-failure thresholds and residual strengths were obtained. Loaded-hole specimens were tested in three configurations that were critical in bearing, shear, or tension. Partial bonding reduced the tensile and compressive strengths of undamaged specimens by about one-third. For impact, partial bonding did not change the threshold for impact failure under tensile preload. However, under compressive preload, partial bonding caused serious degradation of impact resistance. Partial bonding reduced the maximum load-carrying capacity of all three types of loaded-hole specimens. Overall, partial bonding degraded both impact resistance and bearing strength of holes." @default.
- W221570683 created "2016-06-24" @default.
- W221570683 creator A5006239572 @default.
- W221570683 date "1986-07-01" @default.
- W221570683 modified "2023-09-24" @default.
- W221570683 title "Effects of Partial Interlaminar Bonding on Impact Resistance and Loaded-Hole Behavior of Graphite/Epoxy Quasi-Isotropic Laminates." @default.
- W221570683 hasPublicationYear "1986" @default.
- W221570683 type Work @default.
- W221570683 sameAs 221570683 @default.
- W221570683 citedByCount "0" @default.
- W221570683 crossrefType "journal-article" @default.
- W221570683 hasAuthorship W221570683A5006239572 @default.
- W221570683 hasConcept C112950240 @default.
- W221570683 hasConcept C121332964 @default.
- W221570683 hasConcept C159985019 @default.
- W221570683 hasConcept C166595027 @default.
- W221570683 hasConcept C184050105 @default.
- W221570683 hasConcept C186068551 @default.
- W221570683 hasConcept C192562407 @default.
- W221570683 hasConcept C2779698641 @default.
- W221570683 hasConcept C30407753 @default.
- W221570683 hasConcept C62520636 @default.
- W221570683 hasConceptScore W221570683C112950240 @default.
- W221570683 hasConceptScore W221570683C121332964 @default.
- W221570683 hasConceptScore W221570683C159985019 @default.
- W221570683 hasConceptScore W221570683C166595027 @default.
- W221570683 hasConceptScore W221570683C184050105 @default.
- W221570683 hasConceptScore W221570683C186068551 @default.
- W221570683 hasConceptScore W221570683C192562407 @default.
- W221570683 hasConceptScore W221570683C2779698641 @default.
- W221570683 hasConceptScore W221570683C30407753 @default.
- W221570683 hasConceptScore W221570683C62520636 @default.
- W221570683 hasLocation W2215706831 @default.
- W221570683 hasOpenAccess W221570683 @default.
- W221570683 hasPrimaryLocation W2215706831 @default.
- W221570683 hasRelatedWork W1481372931 @default.
- W221570683 hasRelatedWork W1482329321 @default.
- W221570683 hasRelatedWork W1534202391 @default.
- W221570683 hasRelatedWork W1850144356 @default.
- W221570683 hasRelatedWork W2001804136 @default.
- W221570683 hasRelatedWork W2040102737 @default.
- W221570683 hasRelatedWork W2041971033 @default.
- W221570683 hasRelatedWork W2066744853 @default.
- W221570683 hasRelatedWork W2070061868 @default.
- W221570683 hasRelatedWork W2078171641 @default.
- W221570683 hasRelatedWork W2092494425 @default.
- W221570683 hasRelatedWork W2138757632 @default.
- W221570683 hasRelatedWork W2350044656 @default.
- W221570683 hasRelatedWork W2368410352 @default.
- W221570683 hasRelatedWork W265374193 @default.
- W221570683 hasRelatedWork W2743721830 @default.
- W221570683 hasRelatedWork W3109106737 @default.
- W221570683 hasRelatedWork W3125435559 @default.
- W221570683 hasRelatedWork W604555218 @default.
- W221570683 hasRelatedWork W78109598 @default.
- W221570683 isParatext "false" @default.
- W221570683 isRetracted "false" @default.
- W221570683 magId "221570683" @default.
- W221570683 workType "article" @default.