- W2217388713 endingPage "180" @default.
- W2217388713 startingPage "169" @default.
- W2217388713 abstract "Abstract This article reports a study on the microstructural and mechanical properties of the Alkali Activated Slag mortars (AAS) upon exposing to the elevated temperatures up to 800 °C. Slag cement is activated by sodium silicate (Na 2 SiO 3 ) and sodium hydroxide (NaOH) solutions with silicate modulus (Ms = SiO 2 /Na 2 O) of 1.0 and sodium (Na) dosages of 5%. AAS mortars were being subjected to the ambient and high temperature curing (6 h under 60 °C) after undisturbed for 24 h in mold at room temperature. Ordinary Portland cement (OPC) mortar was also prepared as control. Bending and compression tests were conducted at ambient temperature and after exposure to high temperatures at 28 days. Both AAS and OPC mortars were subjected to the X-ray diffraction (XRD), scanning electron microscope (SEM), and thermogravimetric analysis (TGA) tests to find out the microstructural variation due to the exposed temperature level. Test results revealed that the high temperature resistance of the alkali activated slag mortars and Portland cement mortars are clearly different from each other’s. Contrary to the expectations, brilliant mechanical and high temperature resistance might not be observed at the alkali activated slag mortars irrespective of the applied cured conditions. Additionally, applied curing regime and exposed temperature level had a significant effect on the TGA, XRD and SEM images." @default.
- W2217388713 created "2016-06-24" @default.
- W2217388713 creator A5014639264 @default.
- W2217388713 creator A5019797113 @default.
- W2217388713 creator A5033717385 @default.
- W2217388713 creator A5064884562 @default.
- W2217388713 creator A5072476839 @default.
- W2217388713 date "2016-02-01" @default.
- W2217388713 modified "2023-10-05" @default.
- W2217388713 title "Microstructural alteration of alkali activated slag mortars depend on exposed high temperature level" @default.
- W2217388713 cites W1605313824 @default.
- W2217388713 cites W1965622709 @default.
- W2217388713 cites W1967914975 @default.
- W2217388713 cites W1968341997 @default.
- W2217388713 cites W1970067112 @default.
- W2217388713 cites W1971694228 @default.
- W2217388713 cites W1981205379 @default.
- W2217388713 cites W1982158307 @default.
- W2217388713 cites W1985788812 @default.
- W2217388713 cites W1988651307 @default.
- W2217388713 cites W1993016649 @default.
- W2217388713 cites W2002584459 @default.
- W2217388713 cites W2007833236 @default.
- W2217388713 cites W2010459989 @default.
- W2217388713 cites W2012403713 @default.
- W2217388713 cites W2022113185 @default.
- W2217388713 cites W2024545280 @default.
- W2217388713 cites W2040180618 @default.
- W2217388713 cites W2045052433 @default.
- W2217388713 cites W2047036241 @default.
- W2217388713 cites W2047837657 @default.
- W2217388713 cites W2048798797 @default.
- W2217388713 cites W2049698421 @default.
- W2217388713 cites W2049723709 @default.
- W2217388713 cites W2050313018 @default.
- W2217388713 cites W2051102166 @default.
- W2217388713 cites W2056684968 @default.
- W2217388713 cites W2061661809 @default.
- W2217388713 cites W2069679711 @default.
- W2217388713 cites W2071316633 @default.
- W2217388713 cites W2078287527 @default.
- W2217388713 cites W2078362061 @default.
- W2217388713 cites W2081291385 @default.
- W2217388713 cites W2081925947 @default.
- W2217388713 cites W2081957142 @default.
- W2217388713 cites W2084667390 @default.
- W2217388713 cites W2090733702 @default.
- W2217388713 cites W2098422296 @default.
- W2217388713 cites W2111306017 @default.
- W2217388713 cites W2114711884 @default.
- W2217388713 cites W2138813377 @default.
- W2217388713 cites W40831481 @default.
- W2217388713 doi "https://doi.org/10.1016/j.conbuildmat.2015.12.070" @default.
- W2217388713 hasPublicationYear "2016" @default.
- W2217388713 type Work @default.
- W2217388713 sameAs 2217388713 @default.
- W2217388713 citedByCount "93" @default.
- W2217388713 countsByYear W22173887132016 @default.
- W2217388713 countsByYear W22173887132017 @default.
- W2217388713 countsByYear W22173887132018 @default.
- W2217388713 countsByYear W22173887132019 @default.
- W2217388713 countsByYear W22173887132020 @default.
- W2217388713 countsByYear W22173887132021 @default.
- W2217388713 countsByYear W22173887132022 @default.
- W2217388713 countsByYear W22173887132023 @default.
- W2217388713 crossrefType "journal-article" @default.
- W2217388713 hasAuthorship W2217388713A5014639264 @default.
- W2217388713 hasAuthorship W2217388713A5019797113 @default.
- W2217388713 hasAuthorship W2217388713A5033717385 @default.
- W2217388713 hasAuthorship W2217388713A5064884562 @default.
- W2217388713 hasAuthorship W2217388713A5072476839 @default.
- W2217388713 hasConcept C130767629 @default.
- W2217388713 hasConcept C159048435 @default.
- W2217388713 hasConcept C159985019 @default.
- W2217388713 hasConcept C178790620 @default.
- W2217388713 hasConcept C185592680 @default.
- W2217388713 hasConcept C191897082 @default.
- W2217388713 hasConcept C192562407 @default.
- W2217388713 hasConcept C198091228 @default.
- W2217388713 hasConceptScore W2217388713C130767629 @default.
- W2217388713 hasConceptScore W2217388713C159048435 @default.
- W2217388713 hasConceptScore W2217388713C159985019 @default.
- W2217388713 hasConceptScore W2217388713C178790620 @default.
- W2217388713 hasConceptScore W2217388713C185592680 @default.
- W2217388713 hasConceptScore W2217388713C191897082 @default.
- W2217388713 hasConceptScore W2217388713C192562407 @default.
- W2217388713 hasConceptScore W2217388713C198091228 @default.
- W2217388713 hasLocation W22173887131 @default.
- W2217388713 hasOpenAccess W2217388713 @default.
- W2217388713 hasPrimaryLocation W22173887131 @default.
- W2217388713 hasRelatedWork W2014315543 @default.
- W2217388713 hasRelatedWork W2051270029 @default.
- W2217388713 hasRelatedWork W2082293200 @default.
- W2217388713 hasRelatedWork W2137307547 @default.
- W2217388713 hasRelatedWork W2355517443 @default.
- W2217388713 hasRelatedWork W2380293314 @default.
- W2217388713 hasRelatedWork W2943188944 @default.
- W2217388713 hasRelatedWork W3016625885 @default.