- W2256852578 abstract "In this study, the formation of thermally growth ceramic oxides during initial oxidation on treated NiCrAlY bond-coat was investigated. The oxidation resistance of NiCrAlY bond-coat was enhanced by two approaches: (i) an inter-diffusion treatment in a tube furnace with flowing argon at 600 °C for 1 h, and (ii) a pre-oxidation treatment in static air at atmospheric pressure at 1000 °C for 1 h. Experimental results showed that, after diffusion treatment, the content of Al in the bond-coat increased. This led to the growth of θ-Al2O3 during the pre-oxidation process, which was then helped in the formation of a dense and continuous α-Al2O3/Cr2O3 multilayer on the surface of the bond-coat. Results on the cyclic oxidation at 1200 °C (for time≤204 h) showed that the treated NiCrAlY bond-coat exhibited better oxidation resistance than the NiCrAlY bond-coat samples without diffusion treatment and the samples pre-oxidized at 800 °C for 1 h. The formation of NiO, Cr2O3 and NiCr2O4 spinel oxides were suppressed due to the formation of α-Al2O3 scale during the initial oxidation on the surface of pre-treated NiCrAlY bond-coat." @default.
- W2256852578 created "2016-06-24" @default.
- W2256852578 creator A5017122679 @default.
- W2256852578 creator A5028713014 @default.
- W2256852578 creator A5070578537 @default.
- W2256852578 date "2016-05-01" @default.
- W2256852578 modified "2023-10-16" @default.
- W2256852578 title "A study of the diffusion and pre-oxidation treatment on the formation of Al 2 O 3 ceramic scale on NiCrAlY bond-coat during initial oxidation process" @default.
- W2256852578 cites W1409375116 @default.
- W2256852578 cites W1914780160 @default.
- W2256852578 cites W195386703 @default.
- W2256852578 cites W1968291371 @default.
- W2256852578 cites W1970452742 @default.
- W2256852578 cites W1972098333 @default.
- W2256852578 cites W1977158298 @default.
- W2256852578 cites W1979222695 @default.
- W2256852578 cites W1980917373 @default.
- W2256852578 cites W1981528373 @default.
- W2256852578 cites W1991855488 @default.
- W2256852578 cites W1992582275 @default.
- W2256852578 cites W2000122520 @default.
- W2256852578 cites W2004035022 @default.
- W2256852578 cites W2007887009 @default.
- W2256852578 cites W2008837503 @default.
- W2256852578 cites W2009947168 @default.
- W2256852578 cites W2010120375 @default.
- W2256852578 cites W2016599055 @default.
- W2256852578 cites W2050225178 @default.
- W2256852578 cites W2054479262 @default.
- W2256852578 cites W2063508759 @default.
- W2256852578 cites W2064458873 @default.
- W2256852578 cites W2068619106 @default.
- W2256852578 cites W2074513201 @default.
- W2256852578 cites W2075317174 @default.
- W2256852578 cites W2076140599 @default.
- W2256852578 cites W2077747834 @default.
- W2256852578 cites W2084916968 @default.
- W2256852578 cites W2085191181 @default.
- W2256852578 cites W2089520636 @default.
- W2256852578 cites W2091822820 @default.
- W2256852578 cites W2093271050 @default.
- W2256852578 cites W2105305416 @default.
- W2256852578 cites W2112479233 @default.
- W2256852578 cites W2145426799 @default.
- W2256852578 cites W2147841838 @default.
- W2256852578 cites W256203397 @default.
- W2256852578 cites W60561947 @default.
- W2256852578 doi "https://doi.org/10.1016/j.ceramint.2016.01.185" @default.
- W2256852578 hasPublicationYear "2016" @default.
- W2256852578 type Work @default.
- W2256852578 sameAs 2256852578 @default.
- W2256852578 citedByCount "23" @default.
- W2256852578 countsByYear W22568525782016 @default.
- W2256852578 countsByYear W22568525782017 @default.
- W2256852578 countsByYear W22568525782018 @default.
- W2256852578 countsByYear W22568525782019 @default.
- W2256852578 countsByYear W22568525782020 @default.
- W2256852578 countsByYear W22568525782021 @default.
- W2256852578 countsByYear W22568525782022 @default.
- W2256852578 countsByYear W22568525782023 @default.
- W2256852578 crossrefType "journal-article" @default.
- W2256852578 hasAuthorship W2256852578A5017122679 @default.
- W2256852578 hasAuthorship W2256852578A5028713014 @default.
- W2256852578 hasAuthorship W2256852578A5070578537 @default.
- W2256852578 hasConcept C121332964 @default.
- W2256852578 hasConcept C127413603 @default.
- W2256852578 hasConcept C134132462 @default.
- W2256852578 hasConcept C161790260 @default.
- W2256852578 hasConcept C178790620 @default.
- W2256852578 hasConcept C185592680 @default.
- W2256852578 hasConcept C191897082 @default.
- W2256852578 hasConcept C192562407 @default.
- W2256852578 hasConcept C2776230739 @default.
- W2256852578 hasConcept C2779851234 @default.
- W2256852578 hasConcept C2993759403 @default.
- W2256852578 hasConcept C42360764 @default.
- W2256852578 hasConcept C69357855 @default.
- W2256852578 hasConcept C74575197 @default.
- W2256852578 hasConcept C97355855 @default.
- W2256852578 hasConceptScore W2256852578C121332964 @default.
- W2256852578 hasConceptScore W2256852578C127413603 @default.
- W2256852578 hasConceptScore W2256852578C134132462 @default.
- W2256852578 hasConceptScore W2256852578C161790260 @default.
- W2256852578 hasConceptScore W2256852578C178790620 @default.
- W2256852578 hasConceptScore W2256852578C185592680 @default.
- W2256852578 hasConceptScore W2256852578C191897082 @default.
- W2256852578 hasConceptScore W2256852578C192562407 @default.
- W2256852578 hasConceptScore W2256852578C2776230739 @default.
- W2256852578 hasConceptScore W2256852578C2779851234 @default.
- W2256852578 hasConceptScore W2256852578C2993759403 @default.
- W2256852578 hasConceptScore W2256852578C42360764 @default.
- W2256852578 hasConceptScore W2256852578C69357855 @default.
- W2256852578 hasConceptScore W2256852578C74575197 @default.
- W2256852578 hasConceptScore W2256852578C97355855 @default.
- W2256852578 hasIssue "6" @default.
- W2256852578 hasLocation W22568525781 @default.
- W2256852578 hasOpenAccess W2256852578 @default.
- W2256852578 hasPrimaryLocation W22568525781 @default.