- W2265082747 abstract "InP crystals and GaN films were irradiated by swift heavy ions 86Kr and 209Bi with kinetic energies of 25 and 9.5 MeV per nucleon and ion fluence in the range 5 × 1010 to 3.6 × 1012 ions/cm2. The characteristic optical bands were studied by Raman spectroscopy to reveal the disorder and defects induced in the samples during the irradiation process. The crystallinity of InP and GaN was found to be deteriorated after irradiation by the swift heavy ions and resulted in the amorphous nature of the samples along the ion tracks. The amorphous tracks observed by transmission electron microscopy (TEM) images confirmed the formation of lattice defects. In typical F2(LO) mode, in case of InP, the spectra shifted towards the lower wavenumbers with a maximum shift of 7.6 cm−1 induced by 1030 MeV Bi ion irradiation. While in case of GaN, the typical E2(high) mode shifted towards the higher wavenumbers, with maximum shift of 5.4 cm−1 induced by 760 MeV Bi ion irradiation at ion fluence of 1 × 1012 ions/cm2. The observed Raman shifts reveal the presence of lattice defects and disorder induced in the samples after irradiation by the swift heavy ions. This irradiation also generated lattice stress in the samples, which has been investigated and discussed in detail in this work." @default.
- W2265082747 created "2016-06-24" @default.
- W2265082747 creator A5005746586 @default.
- W2265082747 creator A5009744876 @default.
- W2265082747 creator A5034104847 @default.
- W2265082747 creator A5041257476 @default.
- W2265082747 creator A5059111675 @default.
- W2265082747 creator A5059648110 @default.
- W2265082747 creator A5062281721 @default.
- W2265082747 creator A5063734730 @default.
- W2265082747 creator A5077119616 @default.
- W2265082747 creator A5087917506 @default.
- W2265082747 date "2016-04-01" @default.
- W2265082747 modified "2023-10-17" @default.
- W2265082747 title "Raman investigation of lattice defects and stress induced in InP and GaN films by swift heavy ion irradiation" @default.
- W2265082747 cites W1535198421 @default.
- W2265082747 cites W1972712827 @default.
- W2265082747 cites W1973241830 @default.
- W2265082747 cites W1977289968 @default.
- W2265082747 cites W1982381330 @default.
- W2265082747 cites W1988088524 @default.
- W2265082747 cites W1988354490 @default.
- W2265082747 cites W1990964832 @default.
- W2265082747 cites W2006114292 @default.
- W2265082747 cites W2006757184 @default.
- W2265082747 cites W2007961035 @default.
- W2265082747 cites W2013947426 @default.
- W2265082747 cites W2016344850 @default.
- W2265082747 cites W2018670032 @default.
- W2265082747 cites W2028896994 @default.
- W2265082747 cites W2035832548 @default.
- W2265082747 cites W2036944802 @default.
- W2265082747 cites W2042035195 @default.
- W2265082747 cites W2043690724 @default.
- W2265082747 cites W2045811312 @default.
- W2265082747 cites W2048772886 @default.
- W2265082747 cites W2050506763 @default.
- W2265082747 cites W2057441167 @default.
- W2265082747 cites W2060039019 @default.
- W2265082747 cites W2063060034 @default.
- W2265082747 cites W2069272934 @default.
- W2265082747 cites W2071857659 @default.
- W2265082747 cites W2077950105 @default.
- W2265082747 cites W2081217877 @default.
- W2265082747 cites W2083365613 @default.
- W2265082747 cites W2100798510 @default.
- W2265082747 cites W2134369944 @default.
- W2265082747 cites W2166772524 @default.
- W2265082747 cites W3149695189 @default.
- W2265082747 cites W341709611 @default.
- W2265082747 doi "https://doi.org/10.1016/j.nimb.2016.01.031" @default.
- W2265082747 hasPublicationYear "2016" @default.
- W2265082747 type Work @default.
- W2265082747 sameAs 2265082747 @default.
- W2265082747 citedByCount "12" @default.
- W2265082747 countsByYear W22650827472016 @default.
- W2265082747 countsByYear W22650827472017 @default.
- W2265082747 countsByYear W22650827472018 @default.
- W2265082747 countsByYear W22650827472019 @default.
- W2265082747 countsByYear W22650827472020 @default.
- W2265082747 countsByYear W22650827472021 @default.
- W2265082747 countsByYear W22650827472022 @default.
- W2265082747 crossrefType "journal-article" @default.
- W2265082747 hasAuthorship W2265082747A5005746586 @default.
- W2265082747 hasAuthorship W2265082747A5009744876 @default.
- W2265082747 hasAuthorship W2265082747A5034104847 @default.
- W2265082747 hasAuthorship W2265082747A5041257476 @default.
- W2265082747 hasAuthorship W2265082747A5059111675 @default.
- W2265082747 hasAuthorship W2265082747A5059648110 @default.
- W2265082747 hasAuthorship W2265082747A5062281721 @default.
- W2265082747 hasAuthorship W2265082747A5063734730 @default.
- W2265082747 hasAuthorship W2265082747A5077119616 @default.
- W2265082747 hasAuthorship W2265082747A5087917506 @default.
- W2265082747 hasConcept C111337013 @default.
- W2265082747 hasConcept C113196181 @default.
- W2265082747 hasConcept C120665830 @default.
- W2265082747 hasConcept C121332964 @default.
- W2265082747 hasConcept C145148216 @default.
- W2265082747 hasConcept C159985019 @default.
- W2265082747 hasConcept C178790620 @default.
- W2265082747 hasConcept C185544564 @default.
- W2265082747 hasConcept C185592680 @default.
- W2265082747 hasConcept C192562407 @default.
- W2265082747 hasConcept C22078206 @default.
- W2265082747 hasConcept C2780981118 @default.
- W2265082747 hasConcept C40003534 @default.
- W2265082747 hasConcept C43617362 @default.
- W2265082747 hasConcept C46275449 @default.
- W2265082747 hasConcept C56052488 @default.
- W2265082747 hasConcept C8010536 @default.
- W2265082747 hasConceptScore W2265082747C111337013 @default.
- W2265082747 hasConceptScore W2265082747C113196181 @default.
- W2265082747 hasConceptScore W2265082747C120665830 @default.
- W2265082747 hasConceptScore W2265082747C121332964 @default.
- W2265082747 hasConceptScore W2265082747C145148216 @default.
- W2265082747 hasConceptScore W2265082747C159985019 @default.
- W2265082747 hasConceptScore W2265082747C178790620 @default.
- W2265082747 hasConceptScore W2265082747C185544564 @default.