- W2281205814 abstract "Abstract The dependence of fatigue lifetime on the minimum cyclic stress was assessed for the rubber matrix composite of bias aircraft tire carcass reinforced by nylon cords as well as two model rubber composites reinforced by steel wire cables. At a given stress range, the use of higher minimum stress up to a certain level led to longer fatigue life of the composite laminate. When the minimum stress exceeded this critical level, an opposite trend of shorter fatigue life occurred with a higher level of minimum stress. The initial trend of longer fatigue life of angle-plied, cord—rubber composite laminates with a higher level of minimum stress stems from a nonlinear stress—strain relationship with a tendency of strain stiffening. Under stress-controlled fatigue loading, a shorter strain range was experienced for the same stress range when the level of minimum stress was raised. However, the increase of minimum stress raises the potential for damage initiation and accumulation. This effect of increased damage potential became dominant above the critical level of minimum stress. When the fatigue life data were plotted against the values of strain range to clarify the role of damage potential, a general trend of shorter fatigue life with a higher level of minimum stress was observed at a given strain range, in striking contrast to the trend of the stress range vs the number of cycles to failure (S-N) curve in a conventional form. The result again confirms that the damage initiation and eventual fatigue failure of angle-plied, cord—rubber composite laminates are “strain-controlled” processes, as demonstrated in our preceding paper. A modified form of the Goodman equation appears to be valid in predicting the relationship between the strain range (instead of stress amplitude) and minimum strain (instead of mean stress) for a given lifetime of a cord—rubber composite laminate." @default.
- W2281205814 created "2016-06-24" @default.
- W2281205814 creator A5025549366 @default.
- W2281205814 creator A5034089097 @default.
- W2281205814 creator A5087841595 @default.
- W2281205814 date "1998-11-01" @default.
- W2281205814 modified "2023-09-26" @default.
- W2281205814 title "Fatigue of Cord—Rubber Composites: III. Minimum Stress Effect" @default.
- W2281205814 cites W1026327069 @default.
- W2281205814 cites W142288286 @default.
- W2281205814 cites W1514772904 @default.
- W2281205814 cites W1592014909 @default.
- W2281205814 cites W244870270 @default.
- W2281205814 cites W2498517146 @default.
- W2281205814 cites W6982502 @default.
- W2281205814 cites W1491175202 @default.
- W2281205814 cites W2506468604 @default.
- W2281205814 doi "https://doi.org/10.5254/1.3538516" @default.
- W2281205814 hasPublicationYear "1998" @default.
- W2281205814 type Work @default.
- W2281205814 sameAs 2281205814 @default.
- W2281205814 citedByCount "3" @default.
- W2281205814 countsByYear W22812058142014 @default.
- W2281205814 countsByYear W22812058142022 @default.
- W2281205814 crossrefType "journal-article" @default.
- W2281205814 hasAuthorship W2281205814A5025549366 @default.
- W2281205814 hasAuthorship W2281205814A5034089097 @default.
- W2281205814 hasAuthorship W2281205814A5087841595 @default.
- W2281205814 hasConcept C104779481 @default.
- W2281205814 hasConcept C108729823 @default.
- W2281205814 hasConcept C131850400 @default.
- W2281205814 hasConcept C138885662 @default.
- W2281205814 hasConcept C159985019 @default.
- W2281205814 hasConcept C176933379 @default.
- W2281205814 hasConcept C192562407 @default.
- W2281205814 hasConcept C21036866 @default.
- W2281205814 hasConcept C28539199 @default.
- W2281205814 hasConcept C41895202 @default.
- W2281205814 hasConcept C59085676 @default.
- W2281205814 hasConcept C61039299 @default.
- W2281205814 hasConceptScore W2281205814C104779481 @default.
- W2281205814 hasConceptScore W2281205814C108729823 @default.
- W2281205814 hasConceptScore W2281205814C131850400 @default.
- W2281205814 hasConceptScore W2281205814C138885662 @default.
- W2281205814 hasConceptScore W2281205814C159985019 @default.
- W2281205814 hasConceptScore W2281205814C176933379 @default.
- W2281205814 hasConceptScore W2281205814C192562407 @default.
- W2281205814 hasConceptScore W2281205814C21036866 @default.
- W2281205814 hasConceptScore W2281205814C28539199 @default.
- W2281205814 hasConceptScore W2281205814C41895202 @default.
- W2281205814 hasConceptScore W2281205814C59085676 @default.
- W2281205814 hasConceptScore W2281205814C61039299 @default.
- W2281205814 hasLocation W22812058141 @default.
- W2281205814 hasOpenAccess W2281205814 @default.
- W2281205814 hasPrimaryLocation W22812058141 @default.
- W2281205814 hasRelatedWork W1651078521 @default.
- W2281205814 hasRelatedWork W1971917354 @default.
- W2281205814 hasRelatedWork W1990846096 @default.
- W2281205814 hasRelatedWork W1993480274 @default.
- W2281205814 hasRelatedWork W1996891801 @default.
- W2281205814 hasRelatedWork W1997058752 @default.
- W2281205814 hasRelatedWork W2002631904 @default.
- W2281205814 hasRelatedWork W2005764059 @default.
- W2281205814 hasRelatedWork W2010370143 @default.
- W2281205814 hasRelatedWork W2056037286 @default.
- W2281205814 hasRelatedWork W2073092775 @default.
- W2281205814 hasRelatedWork W2087071551 @default.
- W2281205814 hasRelatedWork W2090914213 @default.
- W2281205814 hasRelatedWork W2111462931 @default.
- W2281205814 hasRelatedWork W2137352826 @default.
- W2281205814 hasRelatedWork W2158386931 @default.
- W2281205814 hasRelatedWork W2253617537 @default.
- W2281205814 hasRelatedWork W294124323 @default.
- W2281205814 hasRelatedWork W337378924 @default.
- W2281205814 hasRelatedWork W871731367 @default.
- W2281205814 isParatext "false" @default.
- W2281205814 isRetracted "false" @default.
- W2281205814 magId "2281205814" @default.
- W2281205814 workType "article" @default.