- W2287612500 abstract "Since plasma-spray ceramic coating is comparatively easy to form thick coating, this coating method is already applied as thermal barrier coating. When these structural materials modificated by ceramic coating were exposed at hightemperature environment, various problems such as corrosion, erosion and oxidation and so on. have been experienced. And in case when applying ceramics coating to actual components, it is very important to understand their degradation characteristics. Therefore, in this study, oxidation degradation characteristics of plasma-spray ceramic coating was evaluated under cyclic heating condition. And then, by means of observing their micro structure, the interrelation between the above result and their degradation characteristics was examined. And, for the purpose of improving oxidation-resistant property, the effect of sealing treatment by ethylsilicate and nickel plating was examined. The result of cyclic heating test showed that in the early stages of cyclic heating, LPPS coating have superior oxidation-resistant property than APS coating. This result is caused by dense microstructure of LPPS coating. However, with the increase in cycles of heating, this relation is reversed due to the macrocrack generation in LPPS coating. And it is recognized that many pores in APS coating contributed to relieve the damage in cyclic heating. And it was recognized that sealing treatment is effective for improving oxidation-resistant and relieving the damage." @default.
- W2287612500 created "2016-06-24" @default.
- W2287612500 creator A5007300762 @default.
- W2287612500 creator A5059985874 @default.
- W2287612500 date "1997-07-10" @default.
- W2287612500 modified "2023-09-24" @default.
- W2287612500 title "Correlation Between Microstructure AndDegradation Characteristics Of Plasma-sprayCeramics Coating Under Cyclic Heating Condition" @default.
- W2287612500 doi "https://doi.org/10.2495/surf970111" @default.
- W2287612500 hasPublicationYear "1997" @default.
- W2287612500 type Work @default.
- W2287612500 sameAs 2287612500 @default.
- W2287612500 citedByCount "0" @default.
- W2287612500 crossrefType "journal-article" @default.
- W2287612500 hasAuthorship W2287612500A5007300762 @default.
- W2287612500 hasAuthorship W2287612500A5059985874 @default.
- W2287612500 hasConcept C121332964 @default.
- W2287612500 hasConcept C134132462 @default.
- W2287612500 hasConcept C149669645 @default.
- W2287612500 hasConcept C159985019 @default.
- W2287612500 hasConcept C176711861 @default.
- W2287612500 hasConcept C191897082 @default.
- W2287612500 hasConcept C192562407 @default.
- W2287612500 hasConcept C2779679103 @default.
- W2287612500 hasConcept C2781448156 @default.
- W2287612500 hasConcept C41008148 @default.
- W2287612500 hasConcept C62520636 @default.
- W2287612500 hasConcept C76155785 @default.
- W2287612500 hasConcept C82706917 @default.
- W2287612500 hasConcept C87976508 @default.
- W2287612500 hasConceptScore W2287612500C121332964 @default.
- W2287612500 hasConceptScore W2287612500C134132462 @default.
- W2287612500 hasConceptScore W2287612500C149669645 @default.
- W2287612500 hasConceptScore W2287612500C159985019 @default.
- W2287612500 hasConceptScore W2287612500C176711861 @default.
- W2287612500 hasConceptScore W2287612500C191897082 @default.
- W2287612500 hasConceptScore W2287612500C192562407 @default.
- W2287612500 hasConceptScore W2287612500C2779679103 @default.
- W2287612500 hasConceptScore W2287612500C2781448156 @default.
- W2287612500 hasConceptScore W2287612500C41008148 @default.
- W2287612500 hasConceptScore W2287612500C62520636 @default.
- W2287612500 hasConceptScore W2287612500C76155785 @default.
- W2287612500 hasConceptScore W2287612500C82706917 @default.
- W2287612500 hasConceptScore W2287612500C87976508 @default.
- W2287612500 hasLocation W22876125001 @default.
- W2287612500 hasOpenAccess W2287612500 @default.
- W2287612500 hasPrimaryLocation W22876125001 @default.
- W2287612500 hasRelatedWork W1978042132 @default.
- W2287612500 hasRelatedWork W1990546355 @default.
- W2287612500 hasRelatedWork W1991364587 @default.
- W2287612500 hasRelatedWork W2002900190 @default.
- W2287612500 hasRelatedWork W2009811491 @default.
- W2287612500 hasRelatedWork W2025679018 @default.
- W2287612500 hasRelatedWork W2053143193 @default.
- W2287612500 hasRelatedWork W2080594023 @default.
- W2287612500 hasRelatedWork W2181156861 @default.
- W2287612500 hasRelatedWork W2352394869 @default.
- W2287612500 hasRelatedWork W2358536274 @default.
- W2287612500 hasRelatedWork W2369539187 @default.
- W2287612500 hasRelatedWork W2373848072 @default.
- W2287612500 hasRelatedWork W2514305056 @default.
- W2287612500 hasRelatedWork W3023091252 @default.
- W2287612500 hasRelatedWork W3150632742 @default.
- W2287612500 hasRelatedWork W3151104430 @default.
- W2287612500 hasRelatedWork W2266338216 @default.
- W2287612500 hasRelatedWork W2856258165 @default.
- W2287612500 hasRelatedWork W2866203483 @default.
- W2287612500 hasVolume "17" @default.
- W2287612500 isParatext "false" @default.
- W2287612500 isRetracted "false" @default.
- W2287612500 magId "2287612500" @default.
- W2287612500 workType "article" @default.