- W2295313283 abstract "Glass fiber reinforced polymer matrix composites have poor translaminar properties which make them particularly susceptible to impact loads. In this research work, FRP laminates were prepared by different orientation of plies. In mode I test, a double cantilever beam specimen is employed to determine critical energy release rate, and in Mode II test, Interlaminar critical energy release rate is determined by employing an end notched flexure specimen. Modes I & II fracture toughness are determined under static conditions and impact induced damage area of interface under impact conditions. For low velocity impact, damage starts with the creation of a matrix crack. In some cases the target is flexible and the crack is created by tensile flexural stresses in the bottom ply of the laminate. This crack, which is usually perpendicular to the plane of the laminate, is called a tensile crack. For thick laminate, cracks appear near the top of the laminate and are created by the contact stresses. These cracks, called shear cracks, are inclined relative to the normal to the midplane. The impact is made with a mild steel striker to induce impact energy at impact velocity close to 50 m/s. A circular Teflon sheet is introduced as a penny crack to facilitate failure on the mid-plane of the laminate. The DAE (Damage area extension) initiated by the pre-crack is observed to significantly modify the DAE as amount of XNBR (Carboxylated acrylonitrile butadiene) in the Epibond varied from different percentage. The microscopic analysis shows that the fibres are more damaged in symmetric laminate compare to any other type of laminate, because the centre of the laminate orientation is same in this laminates." @default.
- W2295313283 created "2016-06-24" @default.
- W2295313283 creator A5055956892 @default.
- W2295313283 date "2015-01-01" @default.
- W2295313283 modified "2023-09-23" @default.
- W2295313283 title "Damage Tolerance and Microscopic Study of GFRP Laminates" @default.
- W2295313283 cites W1966757849 @default.
- W2295313283 cites W1967636616 @default.
- W2295313283 cites W1969188970 @default.
- W2295313283 cites W1999089823 @default.
- W2295313283 cites W2023328004 @default.
- W2295313283 cites W2026778217 @default.
- W2295313283 cites W2037002540 @default.
- W2295313283 cites W2044908837 @default.
- W2295313283 cites W2054915274 @default.
- W2295313283 cites W2072404045 @default.
- W2295313283 cites W2085899985 @default.
- W2295313283 cites W2085956884 @default.
- W2295313283 cites W2105682695 @default.
- W2295313283 cites W2123997055 @default.
- W2295313283 cites W2155416515 @default.
- W2295313283 cites W264454005 @default.
- W2295313283 hasPublicationYear "2015" @default.
- W2295313283 type Work @default.
- W2295313283 sameAs 2295313283 @default.
- W2295313283 citedByCount "0" @default.
- W2295313283 crossrefType "journal-article" @default.
- W2295313283 hasAuthorship W2295313283A5055956892 @default.
- W2295313283 hasConcept C112950240 @default.
- W2295313283 hasConcept C151730666 @default.
- W2295313283 hasConcept C159985019 @default.
- W2295313283 hasConcept C192562407 @default.
- W2295313283 hasConcept C30239060 @default.
- W2295313283 hasConcept C32860805 @default.
- W2295313283 hasConcept C43369102 @default.
- W2295313283 hasConcept C58097730 @default.
- W2295313283 hasConcept C76344452 @default.
- W2295313283 hasConcept C77928131 @default.
- W2295313283 hasConcept C86803240 @default.
- W2295313283 hasConcept C96035792 @default.
- W2295313283 hasConceptScore W2295313283C112950240 @default.
- W2295313283 hasConceptScore W2295313283C151730666 @default.
- W2295313283 hasConceptScore W2295313283C159985019 @default.
- W2295313283 hasConceptScore W2295313283C192562407 @default.
- W2295313283 hasConceptScore W2295313283C30239060 @default.
- W2295313283 hasConceptScore W2295313283C32860805 @default.
- W2295313283 hasConceptScore W2295313283C43369102 @default.
- W2295313283 hasConceptScore W2295313283C58097730 @default.
- W2295313283 hasConceptScore W2295313283C76344452 @default.
- W2295313283 hasConceptScore W2295313283C77928131 @default.
- W2295313283 hasConceptScore W2295313283C86803240 @default.
- W2295313283 hasConceptScore W2295313283C96035792 @default.
- W2295313283 hasLocation W22953132831 @default.
- W2295313283 hasOpenAccess W2295313283 @default.
- W2295313283 hasPrimaryLocation W22953132831 @default.
- W2295313283 hasRelatedWork W1495712090 @default.
- W2295313283 hasRelatedWork W1552151744 @default.
- W2295313283 hasRelatedWork W179638255 @default.
- W2295313283 hasRelatedWork W1821913858 @default.
- W2295313283 hasRelatedWork W1968038381 @default.
- W2295313283 hasRelatedWork W1968085858 @default.
- W2295313283 hasRelatedWork W1986486273 @default.
- W2295313283 hasRelatedWork W2036017185 @default.
- W2295313283 hasRelatedWork W2037428036 @default.
- W2295313283 hasRelatedWork W2050081325 @default.
- W2295313283 hasRelatedWork W2059150227 @default.
- W2295313283 hasRelatedWork W2082918667 @default.
- W2295313283 hasRelatedWork W2088616562 @default.
- W2295313283 hasRelatedWork W2245143313 @default.
- W2295313283 hasRelatedWork W2326748536 @default.
- W2295313283 hasRelatedWork W2774010702 @default.
- W2295313283 hasRelatedWork W2885865057 @default.
- W2295313283 hasRelatedWork W2971986666 @default.
- W2295313283 hasRelatedWork W3164895211 @default.
- W2295313283 hasRelatedWork W934091077 @default.
- W2295313283 isParatext "false" @default.
- W2295313283 isRetracted "false" @default.
- W2295313283 magId "2295313283" @default.
- W2295313283 workType "article" @default.