- W2299690216 abstract "Two important classes of hydrogen storage materials were considered: metallic alloys and molecular borohydrides. Each of them has advantages and disadvantages. Alloys absorb and release hydrogen reversibly and promptly, but in relatively small amount, whereas borohydrides decompose irreversibly yielding over 10 wt% of H2. Two systems of suitable chemical composition were selected from such classes, and materials belonging to them were synthesized and characterized from the structural and thermal point of view; then detailed and thorough experiments of dehydrogenation were performed on them, in order to determine the thermodynamic and kinetic aspects of the hydrogen release. Within metallic alloys, the Mg-Al-Ni was selected to study the addition of Al to the Mg-Ni system. Samples with MgmAlNin composition (m,n ≤ 3) were synthesized by ball milling; by X-ray diffraction studies, they were found to be a basically single phase with substitutionally disordered CsCl-type cubic structure. Only compositions with m large and n small proved to segregate minor quantities of Mg and Mg2Ni. Hydrogenation experiments on the Mg2AlNi2 sample by the PCI technique (Sievert apparatus) showed a reversible absorption/desorption of 1.4 wt% H2 with formation / decomposition of the MgH2 and Mg2NiH4 hydrides. A particularly favourable dehydrogenation temperature (T ≥ 531 K for p ≥ 1 bar) was observed, by comparison with those of the single phase hydrides. Also the kinetics of the gas release proved to be satisfactory, indicating that addition of Al improves the H-storage performance of the Mg-Ni alloy substantially. The mixed LiBH4–Mg(BH4)2 borohydride system was investigated, to determine its possible better performance as hydrogen storage material with respect to the end-members pure borohydrides. Several composites were synthesized by ball milling, namely xLiBH4–(1-x)Mg(BH4)2 with x = 0, 0.10, 0.25, 0.33, 0.40, 0.50, 0.60, 0.66, 0.75, 0.80, 0.90, 1. The physical mixture was investigated by using Xray powder diffraction and thermal analysis. Interestingly, already a small amount of LiBH4 proved to make the α to β transition of Mg(BH4)2 reversible, which had not been reported before. The eutectic composition was found to exist at 0.50 < x < 0.60, exhibiting a eutectic melting at 180 °C. A phase diagram was built based on the data obtained in this study. Furthermore, the decomposition of the material begins right after the melting; thus the decomposition temperature of the composite is much lower than those of the pure borohydrides. At 270 °C the x = 0.50 composite releases about 7.0 wt% of hydrogen. A full thermodynamic study of the dehydrogenation reaction was performed (Sievert apparatus) on the eutectic mixture, 0.6LiBH4–0.4Mg(BH4)2, and on the end members LiBH4 and Mg(BH4)2. Both the dynamic technique (constant pressure, temperature ramp vs. time) and the equilibrium mode (constant temperature, variable pressure with waiting time for pressure equilibration) were" @default.
- W2299690216 created "2016-06-24" @default.
- W2299690216 creator A5017840917 @default.
- W2299690216 date "2011-01-21" @default.
- W2299690216 modified "2023-09-27" @default.
- W2299690216 title "Synthesis and characterization of Mg-Al-Ni alloys and Li-Mg borohydrides for hydrogen storage" @default.
- W2299690216 cites W1956074600 @default.
- W2299690216 cites W1969379719 @default.
- W2299690216 cites W1972004039 @default.
- W2299690216 cites W1972006169 @default.
- W2299690216 cites W1973994128 @default.
- W2299690216 cites W1977924704 @default.
- W2299690216 cites W1982539599 @default.
- W2299690216 cites W1983351262 @default.
- W2299690216 cites W1989293511 @default.
- W2299690216 cites W1989684250 @default.
- W2299690216 cites W1991616978 @default.
- W2299690216 cites W1992323852 @default.
- W2299690216 cites W1995638498 @default.
- W2299690216 cites W1999344634 @default.
- W2299690216 cites W2000791207 @default.
- W2299690216 cites W2001423077 @default.
- W2299690216 cites W2002765673 @default.
- W2299690216 cites W2002966725 @default.
- W2299690216 cites W2003543046 @default.
- W2299690216 cites W2005966343 @default.
- W2299690216 cites W2007547200 @default.
- W2299690216 cites W2023206598 @default.
- W2299690216 cites W2029123048 @default.
- W2299690216 cites W2043192670 @default.
- W2299690216 cites W2050319888 @default.
- W2299690216 cites W2051804190 @default.
- W2299690216 cites W2052241027 @default.
- W2299690216 cites W2057078858 @default.
- W2299690216 cites W2058364336 @default.
- W2299690216 cites W2060954663 @default.
- W2299690216 cites W2066983645 @default.
- W2299690216 cites W2069003934 @default.
- W2299690216 cites W2069190119 @default.
- W2299690216 cites W2070360781 @default.
- W2299690216 cites W2071321945 @default.
- W2299690216 cites W2071862239 @default.
- W2299690216 cites W2084172443 @default.
- W2299690216 cites W2093478501 @default.
- W2299690216 cites W2102097343 @default.
- W2299690216 cites W2106443480 @default.
- W2299690216 cites W2115842025 @default.
- W2299690216 cites W2127040954 @default.
- W2299690216 cites W2129324347 @default.
- W2299690216 cites W2130942021 @default.
- W2299690216 cites W2132061901 @default.
- W2299690216 cites W2160931103 @default.
- W2299690216 cites W2167383445 @default.
- W2299690216 cites W2167897131 @default.
- W2299690216 cites W2168007532 @default.
- W2299690216 cites W2168516863 @default.
- W2299690216 cites W2646953325 @default.
- W2299690216 cites W2951460037 @default.
- W2299690216 cites W618572747 @default.
- W2299690216 hasPublicationYear "2011" @default.
- W2299690216 type Work @default.
- W2299690216 sameAs 2299690216 @default.
- W2299690216 citedByCount "1" @default.
- W2299690216 countsByYear W22996902162013 @default.
- W2299690216 crossrefType "journal-article" @default.
- W2299690216 hasAuthorship W2299690216A5017840917 @default.
- W2299690216 hasConcept C113196181 @default.
- W2299690216 hasConcept C119889771 @default.
- W2299690216 hasConcept C127413603 @default.
- W2299690216 hasConcept C132186339 @default.
- W2299690216 hasConcept C160434732 @default.
- W2299690216 hasConcept C161790260 @default.
- W2299690216 hasConcept C178790620 @default.
- W2299690216 hasConcept C179104552 @default.
- W2299690216 hasConcept C185592680 @default.
- W2299690216 hasConcept C191897082 @default.
- W2299690216 hasConcept C192562407 @default.
- W2299690216 hasConcept C2778931688 @default.
- W2299690216 hasConcept C2780026712 @default.
- W2299690216 hasConcept C42360764 @default.
- W2299690216 hasConcept C44280652 @default.
- W2299690216 hasConcept C512968161 @default.
- W2299690216 hasConcept C544153396 @default.
- W2299690216 hasConcept C68044625 @default.
- W2299690216 hasConceptScore W2299690216C113196181 @default.
- W2299690216 hasConceptScore W2299690216C119889771 @default.
- W2299690216 hasConceptScore W2299690216C127413603 @default.
- W2299690216 hasConceptScore W2299690216C132186339 @default.
- W2299690216 hasConceptScore W2299690216C160434732 @default.
- W2299690216 hasConceptScore W2299690216C161790260 @default.
- W2299690216 hasConceptScore W2299690216C178790620 @default.
- W2299690216 hasConceptScore W2299690216C179104552 @default.
- W2299690216 hasConceptScore W2299690216C185592680 @default.
- W2299690216 hasConceptScore W2299690216C191897082 @default.
- W2299690216 hasConceptScore W2299690216C192562407 @default.
- W2299690216 hasConceptScore W2299690216C2778931688 @default.
- W2299690216 hasConceptScore W2299690216C2780026712 @default.
- W2299690216 hasConceptScore W2299690216C42360764 @default.
- W2299690216 hasConceptScore W2299690216C44280652 @default.
- W2299690216 hasConceptScore W2299690216C512968161 @default.