- W2307483570 abstract "Abstract The tribological properties of Ni-P/SiC nanocomposite coatings annealed at different temperatures (350–500 °C) were investigated in order to determine the optimal temperature needed to enhance their wear resistance as well as to reveal the underlying wear mechanisms. With increasing annealing temperature, the hardness of the annealed coatings gradually decreased from 8.2±0.5 to 7.1±0.6 GPa as a result of the Hall-Petch effect, nevertheless these values obtained were constantly higher than that of the as-plated coating (6.3±0.3 GPa) due to the formation of a hard Ni 3 P phase. Regarding to tribological properties, the Ni-P/SiC coating annealed at 350 °C presented a poorer wear resistance (6.1×10 −5 mm 3 /Nm) compared to the as-plated coating (3.9×10 −5 mm 3 /Nm) owing to a rougher original contact surface and the subsequent generation of nickel and iron oxides on the wear track. In contrast, coatings annealed at temperatures ranging between 400–500 °C exhibited the improved wear resistance (4.3×10 −5 –7.8×10 −6 mm 3 /Nm) attributable to their smoother surfaces and to the lubrication effect of H 3 PO 4 arising from the tribochemical reaction between Ni 3 P and the environment. Overall, the Ni-P/SiC coating annealed at 500 °C containing the largest amount of Ni 3 P exhibited the lowest friction coefficient (0.51) and wear rate (7.8×10 −6 mm 3 /Nm)." @default.
- W2307483570 created "2016-06-24" @default.
- W2307483570 creator A5013506935 @default.
- W2307483570 creator A5014961672 @default.
- W2307483570 creator A5024447035 @default.
- W2307483570 creator A5047103030 @default.
- W2307483570 creator A5063972004 @default.
- W2307483570 creator A5075399110 @default.
- W2307483570 creator A5076585197 @default.
- W2307483570 creator A5083495022 @default.
- W2307483570 date "2016-06-01" @default.
- W2307483570 modified "2023-10-18" @default.
- W2307483570 title "Effect of annealing temperature on microstructure, mechanical and tribological properties of nano-SiC reinforced Ni-P coatings" @default.
- W2307483570 cites W1966975512 @default.
- W2307483570 cites W1967168009 @default.
- W2307483570 cites W1970338500 @default.
- W2307483570 cites W1980009725 @default.
- W2307483570 cites W1988815247 @default.
- W2307483570 cites W1990128820 @default.
- W2307483570 cites W1990768420 @default.
- W2307483570 cites W1993865750 @default.
- W2307483570 cites W1994753274 @default.
- W2307483570 cites W2000725726 @default.
- W2307483570 cites W2007086759 @default.
- W2307483570 cites W2009505123 @default.
- W2307483570 cites W2009664436 @default.
- W2307483570 cites W2010836679 @default.
- W2307483570 cites W2017911084 @default.
- W2307483570 cites W2023907092 @default.
- W2307483570 cites W2025893864 @default.
- W2307483570 cites W2030419797 @default.
- W2307483570 cites W2033317439 @default.
- W2307483570 cites W2035962170 @default.
- W2307483570 cites W2052486045 @default.
- W2307483570 cites W2054275753 @default.
- W2307483570 cites W2060464999 @default.
- W2307483570 cites W2061463666 @default.
- W2307483570 cites W2063154873 @default.
- W2307483570 cites W2070387645 @default.
- W2307483570 cites W2070798617 @default.
- W2307483570 cites W2080099522 @default.
- W2307483570 cites W2084043224 @default.
- W2307483570 cites W2093292436 @default.
- W2307483570 cites W2135766760 @default.
- W2307483570 cites W2319093269 @default.
- W2307483570 cites W2330981391 @default.
- W2307483570 doi "https://doi.org/10.1016/j.wear.2016.03.011" @default.
- W2307483570 hasPublicationYear "2016" @default.
- W2307483570 type Work @default.
- W2307483570 sameAs 2307483570 @default.
- W2307483570 citedByCount "22" @default.
- W2307483570 countsByYear W23074835702016 @default.
- W2307483570 countsByYear W23074835702018 @default.
- W2307483570 countsByYear W23074835702019 @default.
- W2307483570 countsByYear W23074835702020 @default.
- W2307483570 countsByYear W23074835702021 @default.
- W2307483570 countsByYear W23074835702022 @default.
- W2307483570 crossrefType "journal-article" @default.
- W2307483570 hasAuthorship W2307483570A5013506935 @default.
- W2307483570 hasAuthorship W2307483570A5014961672 @default.
- W2307483570 hasAuthorship W2307483570A5024447035 @default.
- W2307483570 hasAuthorship W2307483570A5047103030 @default.
- W2307483570 hasAuthorship W2307483570A5063972004 @default.
- W2307483570 hasAuthorship W2307483570A5075399110 @default.
- W2307483570 hasAuthorship W2307483570A5076585197 @default.
- W2307483570 hasAuthorship W2307483570A5083495022 @default.
- W2307483570 hasBestOaLocation W23074835702 @default.
- W2307483570 hasConcept C159985019 @default.
- W2307483570 hasConcept C167310744 @default.
- W2307483570 hasConcept C191897082 @default.
- W2307483570 hasConcept C192562407 @default.
- W2307483570 hasConcept C2777855556 @default.
- W2307483570 hasConcept C2780357685 @default.
- W2307483570 hasConcept C87976508 @default.
- W2307483570 hasConceptScore W2307483570C159985019 @default.
- W2307483570 hasConceptScore W2307483570C167310744 @default.
- W2307483570 hasConceptScore W2307483570C191897082 @default.
- W2307483570 hasConceptScore W2307483570C192562407 @default.
- W2307483570 hasConceptScore W2307483570C2777855556 @default.
- W2307483570 hasConceptScore W2307483570C2780357685 @default.
- W2307483570 hasConceptScore W2307483570C87976508 @default.
- W2307483570 hasLocation W23074835701 @default.
- W2307483570 hasLocation W23074835702 @default.
- W2307483570 hasOpenAccess W2307483570 @default.
- W2307483570 hasPrimaryLocation W23074835701 @default.
- W2307483570 hasRelatedWork W1983622139 @default.
- W2307483570 hasRelatedWork W2046292958 @default.
- W2307483570 hasRelatedWork W2347531304 @default.
- W2307483570 hasRelatedWork W2348902237 @default.
- W2307483570 hasRelatedWork W2351679394 @default.
- W2307483570 hasRelatedWork W2365957384 @default.
- W2307483570 hasRelatedWork W2380794779 @default.
- W2307483570 hasRelatedWork W3093466287 @default.
- W2307483570 hasRelatedWork W3205872284 @default.
- W2307483570 hasRelatedWork W4225264123 @default.
- W2307483570 hasVolume "356-357" @default.
- W2307483570 isParatext "false" @default.
- W2307483570 isRetracted "false" @default.