- W2317665246 abstract "本文采用微波辅助合成壳聚糖基Ni-Al水滑石(LDHs)，研究了焙烧水滑石(C-LDHs)以及未焙烧水滑石(LDHs)对水溶液中氟离子的吸附行为，以壳聚糖基Ni-Al水滑石为吸附剂，研究了吸附剂用量、pH值、干扰离子、焙烧温度等对水中氟离子吸附的影响。同时用X射线衍射(XRD)和红外分析(FTIR)对LDHs以及吸附氟离子后的LDHs的结构和性质进行了表征，并且对样品进行了热重差热(TG-DTA)和透射电镜(TEM)分析。结果表明：Ni-Al水滑石的焙烧温度过高会导致水滑石的层状结构被破坏，原样的吸附性能优于焙烧产物的吸附性能。低浓度氟离子有利于水滑石的吸附，吸附剂用量为0.2 g/L，吸附率达到85.78%，pH值在6~7之间吸附氟离子效果最佳，强酸和强碱环境都不利于吸附氟离子。 In this study, microwave assisted method was used for preparing chitosan based NiAl-hydrotalcite, and NiAl-hydrotalcites with and without calcination were used in the adsorption of fluoride from aqueous solution. Various conditions such as adsorbent dosage, solution pH value, co-existing interfering ions and calcination temperature etc., were investigated. The adsorption mechanism was studied by contrasting analysis of X-ray diffract pattern and FTIR of as-prepared sample before and after adsorption, and the sample was characterized by TG-DTA and TEM. The results indicated that the structure of chitosan based NiAl-hydrotalcite would be destroyed when the calcination temperature is higher. Adsorption properties of the sample without calcination were better than those of the calcined sample. The lower fluorine ion concentration was beneficial to adsorption of hydrotalcite, when the adsorbent dosage was 0.2 g/L, the removal rate was 85.78%. It had the best removal efficiency when the pH of solution was in the range of 6 to 7, and strong acid and strong base were not conducive to the adsorption of fluoride ion." @default.
- W2317665246 created "2016-06-24" @default.
- W2317665246 creator A5056435802 @default.
- W2317665246 date "2014-01-01" @default.
- W2317665246 modified "2023-09-25" @default.
- W2317665246 title "The Preparation and Adsorption Properties of Ni-Al Hydrotalcite Based on Chitosan" @default.
- W2317665246 cites W1975026076 @default.
- W2317665246 cites W1998373932 @default.
- W2317665246 cites W2001001421 @default.
- W2317665246 cites W2001917932 @default.
- W2317665246 cites W2017892943 @default.
- W2317665246 cites W2018614585 @default.
- W2317665246 cites W2020073503 @default.
- W2317665246 cites W2021490308 @default.
- W2317665246 cites W2080376386 @default.
- W2317665246 cites W2084669016 @default.
- W2317665246 cites W2088946908 @default.
- W2317665246 cites W2089128499 @default.
- W2317665246 cites W2158201087 @default.
- W2317665246 doi "https://doi.org/10.12677/amc.2014.22004" @default.
- W2317665246 hasPublicationYear "2014" @default.
- W2317665246 type Work @default.
- W2317665246 sameAs 2317665246 @default.
- W2317665246 citedByCount "0" @default.
- W2317665246 crossrefType "journal-article" @default.
- W2317665246 hasAuthorship W2317665246A5056435802 @default.
- W2317665246 hasBestOaLocation W23176652461 @default.
- W2317665246 hasConcept C127413603 @default.
- W2317665246 hasConcept C13965031 @default.
- W2317665246 hasConcept C150394285 @default.
- W2317665246 hasConcept C160892712 @default.
- W2317665246 hasConcept C161790260 @default.
- W2317665246 hasConcept C178790620 @default.
- W2317665246 hasConcept C179104552 @default.
- W2317665246 hasConcept C184651966 @default.
- W2317665246 hasConcept C185592680 @default.
- W2317665246 hasConcept C191897082 @default.
- W2317665246 hasConcept C192562407 @default.
- W2317665246 hasConcept C27501479 @default.
- W2317665246 hasConcept C2778002958 @default.
- W2317665246 hasConcept C2780026712 @default.
- W2317665246 hasConcept C2780289051 @default.
- W2317665246 hasConcept C2780828025 @default.
- W2317665246 hasConcept C42360764 @default.
- W2317665246 hasConcept C64792281 @default.
- W2317665246 hasConcept C7082614 @default.
- W2317665246 hasConceptScore W2317665246C127413603 @default.
- W2317665246 hasConceptScore W2317665246C13965031 @default.
- W2317665246 hasConceptScore W2317665246C150394285 @default.
- W2317665246 hasConceptScore W2317665246C160892712 @default.
- W2317665246 hasConceptScore W2317665246C161790260 @default.
- W2317665246 hasConceptScore W2317665246C178790620 @default.
- W2317665246 hasConceptScore W2317665246C179104552 @default.
- W2317665246 hasConceptScore W2317665246C184651966 @default.
- W2317665246 hasConceptScore W2317665246C185592680 @default.
- W2317665246 hasConceptScore W2317665246C191897082 @default.
- W2317665246 hasConceptScore W2317665246C192562407 @default.
- W2317665246 hasConceptScore W2317665246C27501479 @default.
- W2317665246 hasConceptScore W2317665246C2778002958 @default.
- W2317665246 hasConceptScore W2317665246C2780026712 @default.
- W2317665246 hasConceptScore W2317665246C2780289051 @default.
- W2317665246 hasConceptScore W2317665246C2780828025 @default.
- W2317665246 hasConceptScore W2317665246C42360764 @default.
- W2317665246 hasConceptScore W2317665246C64792281 @default.
- W2317665246 hasConceptScore W2317665246C7082614 @default.
- W2317665246 hasLocation W23176652461 @default.
- W2317665246 hasOpenAccess W2317665246 @default.
- W2317665246 hasPrimaryLocation W23176652461 @default.
- W2317665246 isParatext "false" @default.
- W2317665246 isRetracted "false" @default.
- W2317665246 magId "2317665246" @default.
- W2317665246 workType "article" @default.