- W2331008087 endingPage "193" @default.
- W2331008087 startingPage "188" @default.
- W2331008087 abstract "The abrasion test was conducted on samples of cast iron, produced by various methods and annealed at various temperatures, with a rotor made of pearlite matrix annealed at 550°C. The following results were obtained.1) The residual stress of the specimen produced in gravity green sand mold (specimen mark; L) was greater than that of specimen in dry sand mold (Q) by centrifugal casting. The residual stress gradually decreased with the rise of annealing temperature when it was below 450°C; however, the stress was rapidly removed at 450-550°C.2) The relation between annealing temperature and wear loss was examined. Under the condition of the wear with mechanical rupture, the minimum wear loss was observed at 450-550°C in specimen L, or at 550-600°C in Q.3) When residual stress increased to a certain value, rapid increase of wear loss was observed.The critical value of the residual stress was called “Critical residual stress for wear.”" @default.
- W2331008087 created "2016-06-24" @default.
- W2331008087 creator A5089211321 @default.
- W2331008087 date "1964-01-01" @default.
- W2331008087 modified "2023-10-18" @default.
- W2331008087 title "Effects of Residual Stress on Wear of Cast Iron" @default.
- W2331008087 doi "https://doi.org/10.4139/sfj1950.15.188" @default.
- W2331008087 hasPublicationYear "1964" @default.
- W2331008087 type Work @default.
- W2331008087 sameAs 2331008087 @default.
- W2331008087 citedByCount "0" @default.
- W2331008087 crossrefType "journal-article" @default.
- W2331008087 hasAuthorship W2331008087A5089211321 @default.
- W2331008087 hasBestOaLocation W23310080871 @default.
- W2331008087 hasConcept C118231568 @default.
- W2331008087 hasConcept C159985019 @default.
- W2331008087 hasConcept C16635281 @default.
- W2331008087 hasConcept C191897082 @default.
- W2331008087 hasConcept C192562407 @default.
- W2331008087 hasConcept C2776735967 @default.
- W2331008087 hasConcept C2777855556 @default.
- W2331008087 hasConcept C2780566776 @default.
- W2331008087 hasConcept C37292000 @default.
- W2331008087 hasConcept C5701217 @default.
- W2331008087 hasConcept C87976508 @default.
- W2331008087 hasConcept C96288455 @default.
- W2331008087 hasConceptScore W2331008087C118231568 @default.
- W2331008087 hasConceptScore W2331008087C159985019 @default.
- W2331008087 hasConceptScore W2331008087C16635281 @default.
- W2331008087 hasConceptScore W2331008087C191897082 @default.
- W2331008087 hasConceptScore W2331008087C192562407 @default.
- W2331008087 hasConceptScore W2331008087C2776735967 @default.
- W2331008087 hasConceptScore W2331008087C2777855556 @default.
- W2331008087 hasConceptScore W2331008087C2780566776 @default.
- W2331008087 hasConceptScore W2331008087C37292000 @default.
- W2331008087 hasConceptScore W2331008087C5701217 @default.
- W2331008087 hasConceptScore W2331008087C87976508 @default.
- W2331008087 hasConceptScore W2331008087C96288455 @default.
- W2331008087 hasIssue "5" @default.
- W2331008087 hasLocation W23310080871 @default.
- W2331008087 hasOpenAccess W2331008087 @default.
- W2331008087 hasPrimaryLocation W23310080871 @default.
- W2331008087 hasRelatedWork W2364605234 @default.
- W2331008087 hasRelatedWork W2385486428 @default.
- W2331008087 hasRelatedWork W2385934138 @default.
- W2331008087 hasRelatedWork W2393455849 @default.
- W2331008087 hasRelatedWork W2522125416 @default.
- W2331008087 hasRelatedWork W2588943898 @default.
- W2331008087 hasRelatedWork W2595078964 @default.
- W2331008087 hasRelatedWork W2806935491 @default.
- W2331008087 hasRelatedWork W3151084947 @default.
- W2331008087 hasRelatedWork W4306870991 @default.
- W2331008087 hasVolume "15" @default.
- W2331008087 isParatext "false" @default.
- W2331008087 isRetracted "false" @default.
- W2331008087 magId "2331008087" @default.
- W2331008087 workType "article" @default.