- W2333075013 abstract "Al-Fe-Cr-Ti and Al-V-Fe alloys prepared by the powder metallurgy (P/M) process have high strength exceeding 600 MPa, high-elevated temperature strength exceeding 300 MPa after holding for 100 hours at 573 K and more excellent wear resistance than commercial A390 aluminum alloy. In this work mechanical properties of the P/M Al93Fe3Cr2Ti2 and Al94V4Fe2 alloys were found to be improved by the addition of misch metal (Mm). P/M Al92Fe3Cr2Ti2Mm1 alloys containing quasicrystalline phase were prepared by extrusion of argon gas atomized powders at 673 K, where the atomized powders sieved into the sizes smaller than 75μm were used. The P/M Al92Fe3Cr2Ti2Mm1 alloy has a mixed structure consisting of Al, quasicrystal and compounds phases and exhibits good mechanical properties as follows: ultimate tensile strength (σUTS) of 680±13 MPa, 0.2% proof strength (σ0.2) of 670±10 MPa, plastic elongation (eP) of 0.3±0.1%, Young's modulus (E) of 91±3 GPa and Vickers hardness (Hv) of 230±3, respectively, at room temperature, and alas of 347±5 MPa, σ0.2 of 315±3 MPa and eP of 1.8±0.3%, respectively, after holding for 100 hours at 573 K." @default.
- W2333075013 created "2016-06-24" @default.
- W2333075013 creator A5008412118 @default.
- W2333075013 creator A5021784369 @default.
- W2333075013 creator A5046184213 @default.
- W2333075013 creator A5060351709 @default.
- W2333075013 creator A5060551151 @default.
- W2333075013 creator A5065989461 @default.
- W2333075013 date "2001-01-01" @default.
- W2333075013 modified "2023-10-03" @default.
- W2333075013 title "Microstructure and Mechanical Properties of P/M Al-Fe-Cr-Ti-Mm (Mm: Misch Metal) and Al-V-Fe-Mm Alloys." @default.
- W2333075013 cites W1722357568 @default.
- W2333075013 cites W1966136218 @default.
- W2333075013 cites W1981420425 @default.
- W2333075013 cites W1982585787 @default.
- W2333075013 cites W1994476683 @default.
- W2333075013 cites W2017323493 @default.
- W2333075013 cites W2053170550 @default.
- W2333075013 cites W2070235411 @default.
- W2333075013 cites W2146540617 @default.
- W2333075013 cites W2475058470 @default.
- W2333075013 doi "https://doi.org/10.2497/jjspm.48.1126" @default.
- W2333075013 hasPublicationYear "2001" @default.
- W2333075013 type Work @default.
- W2333075013 sameAs 2333075013 @default.
- W2333075013 citedByCount "1" @default.
- W2333075013 crossrefType "journal-article" @default.
- W2333075013 hasAuthorship W2333075013A5008412118 @default.
- W2333075013 hasAuthorship W2333075013A5021784369 @default.
- W2333075013 hasAuthorship W2333075013A5046184213 @default.
- W2333075013 hasAuthorship W2333075013A5060351709 @default.
- W2333075013 hasAuthorship W2333075013A5060551151 @default.
- W2333075013 hasAuthorship W2333075013A5065989461 @default.
- W2333075013 hasBestOaLocation W23330750131 @default.
- W2333075013 hasConcept C112950240 @default.
- W2333075013 hasConcept C133392424 @default.
- W2333075013 hasConcept C178790620 @default.
- W2333075013 hasConcept C185592680 @default.
- W2333075013 hasConcept C191897082 @default.
- W2333075013 hasConcept C192562407 @default.
- W2333075013 hasConcept C203101518 @default.
- W2333075013 hasConcept C2778958987 @default.
- W2333075013 hasConcept C2780026712 @default.
- W2333075013 hasConcept C33947775 @default.
- W2333075013 hasConcept C44280652 @default.
- W2333075013 hasConcept C544153396 @default.
- W2333075013 hasConcept C8010536 @default.
- W2333075013 hasConcept C87976508 @default.
- W2333075013 hasConceptScore W2333075013C112950240 @default.
- W2333075013 hasConceptScore W2333075013C133392424 @default.
- W2333075013 hasConceptScore W2333075013C178790620 @default.
- W2333075013 hasConceptScore W2333075013C185592680 @default.
- W2333075013 hasConceptScore W2333075013C191897082 @default.
- W2333075013 hasConceptScore W2333075013C192562407 @default.
- W2333075013 hasConceptScore W2333075013C203101518 @default.
- W2333075013 hasConceptScore W2333075013C2778958987 @default.
- W2333075013 hasConceptScore W2333075013C2780026712 @default.
- W2333075013 hasConceptScore W2333075013C33947775 @default.
- W2333075013 hasConceptScore W2333075013C44280652 @default.
- W2333075013 hasConceptScore W2333075013C544153396 @default.
- W2333075013 hasConceptScore W2333075013C8010536 @default.
- W2333075013 hasConceptScore W2333075013C87976508 @default.
- W2333075013 hasLocation W23330750131 @default.
- W2333075013 hasOpenAccess W2333075013 @default.
- W2333075013 hasPrimaryLocation W23330750131 @default.
- W2333075013 hasRelatedWork W146587524 @default.
- W2333075013 hasRelatedWork W1980486017 @default.
- W2333075013 hasRelatedWork W1987348420 @default.
- W2333075013 hasRelatedWork W2047305640 @default.
- W2333075013 hasRelatedWork W2052611968 @default.
- W2333075013 hasRelatedWork W2068068775 @default.
- W2333075013 hasRelatedWork W2072655070 @default.
- W2333075013 hasRelatedWork W2080825098 @default.
- W2333075013 hasRelatedWork W2146540617 @default.
- W2333075013 hasRelatedWork W2312251663 @default.
- W2333075013 hasRelatedWork W2317587212 @default.
- W2333075013 hasRelatedWork W2359495073 @default.
- W2333075013 hasRelatedWork W2382656152 @default.
- W2333075013 hasRelatedWork W2385438469 @default.
- W2333075013 hasRelatedWork W2559672700 @default.
- W2333075013 hasRelatedWork W2811298223 @default.
- W2333075013 hasRelatedWork W3048157064 @default.
- W2333075013 hasRelatedWork W762890074 @default.
- W2333075013 hasRelatedWork W1486455767 @default.
- W2333075013 hasRelatedWork W2842454348 @default.
- W2333075013 isParatext "false" @default.
- W2333075013 isRetracted "false" @default.
- W2333075013 magId "2333075013" @default.
- W2333075013 workType "article" @default.