- W2333835900 abstract "Magnetic carbon composite nanofibres, using the mixed homogeneous solution consist of polyacrylonitrile (PAN), ferric acetylacetonate (AAI) and dimetbylformamide (DMF) as raw material, were prepared by electrospinning-calcination technology. TEM analysis showed that the carbon nanofibre diameter of sample CF900 was about 130–210 nm, in which magnetic nanoparticles were uniformly distributed. The magnetic properties of carbon composite nanofibres under different carbonization temperature was also investigated. Results showed that saturation magnetization (Ms) and remanent magnetization (Mr) increased with the increase of the temperature. When carbonization temperature was 900 °C, the sample was of good magnetic property with high saturation magnetization (Ms=27.55 A·m/kg). Moreover, the specific surface area (SBET) and total pore volume (Vtotal) were up to 354.0 m/g and 0.315 mL/g, respectively." @default.
- W2333835900 created "2016-06-24" @default.
- W2333835900 creator A5013276481 @default.
- W2333835900 creator A5063498975 @default.
- W2333835900 creator A5071329167 @default.
- W2333835900 creator A5082806588 @default.
- W2333835900 creator A5090847382 @default.
- W2333835900 date "2014-01-01" @default.
- W2333835900 modified "2023-09-26" @default.
- W2333835900 title "Preparation and Characterization of Electrospun Magnetic Carbon Composite Nanofibres" @default.
- W2333835900 cites W1965229294 @default.
- W2333835900 cites W1966833500 @default.
- W2333835900 cites W1967993448 @default.
- W2333835900 cites W1970772018 @default.
- W2333835900 cites W1975082054 @default.
- W2333835900 cites W1975609719 @default.
- W2333835900 cites W1977202825 @default.
- W2333835900 cites W1980483897 @default.
- W2333835900 cites W1985358733 @default.
- W2333835900 cites W1990049354 @default.
- W2333835900 cites W1992035534 @default.
- W2333835900 cites W1992968857 @default.
- W2333835900 cites W1993707749 @default.
- W2333835900 cites W1998820660 @default.
- W2333835900 cites W1999688659 @default.
- W2333835900 cites W2008846604 @default.
- W2333835900 cites W2027172180 @default.
- W2333835900 cites W2031036452 @default.
- W2333835900 cites W2032643286 @default.
- W2333835900 cites W2033126464 @default.
- W2333835900 cites W2033794029 @default.
- W2333835900 cites W2037540440 @default.
- W2333835900 cites W2046284343 @default.
- W2333835900 cites W2052226324 @default.
- W2333835900 cites W2052965678 @default.
- W2333835900 cites W2054228641 @default.
- W2333835900 cites W2055465615 @default.
- W2333835900 cites W2057142050 @default.
- W2333835900 cites W2058562579 @default.
- W2333835900 cites W2058971825 @default.
- W2333835900 cites W2063339819 @default.
- W2333835900 cites W2063655014 @default.
- W2333835900 cites W2074994774 @default.
- W2333835900 cites W2075903537 @default.
- W2333835900 cites W2077670229 @default.
- W2333835900 cites W2078178892 @default.
- W2333835900 cites W2079760026 @default.
- W2333835900 cites W2085578567 @default.
- W2333835900 cites W2114515837 @default.
- W2333835900 cites W2138467877 @default.
- W2333835900 cites W2145963403 @default.
- W2333835900 cites W2152391887 @default.
- W2333835900 cites W2161931175 @default.
- W2333835900 cites W2163585067 @default.
- W2333835900 cites W2171898868 @default.
- W2333835900 cites W2186396837 @default.
- W2333835900 doi "https://doi.org/10.15541/jim20130577" @default.
- W2333835900 hasPublicationYear "2014" @default.
- W2333835900 type Work @default.
- W2333835900 sameAs 2333835900 @default.
- W2333835900 citedByCount "1" @default.
- W2333835900 countsByYear W23338359002016 @default.
- W2333835900 crossrefType "journal-article" @default.
- W2333835900 hasAuthorship W2333835900A5013276481 @default.
- W2333835900 hasAuthorship W2333835900A5063498975 @default.
- W2333835900 hasAuthorship W2333835900A5071329167 @default.
- W2333835900 hasAuthorship W2333835900A5082806588 @default.
- W2333835900 hasAuthorship W2333835900A5090847382 @default.
- W2333835900 hasBestOaLocation W23338359001 @default.
- W2333835900 hasConcept C104779481 @default.
- W2333835900 hasConcept C127413603 @default.
- W2333835900 hasConcept C140205800 @default.
- W2333835900 hasConcept C144796933 @default.
- W2333835900 hasConcept C159985019 @default.
- W2333835900 hasConcept C171250308 @default.
- W2333835900 hasConcept C192562407 @default.
- W2333835900 hasConcept C2780841128 @default.
- W2333835900 hasConcept C42360764 @default.
- W2333835900 hasConcept C521977710 @default.
- W2333835900 hasConceptScore W2333835900C104779481 @default.
- W2333835900 hasConceptScore W2333835900C127413603 @default.
- W2333835900 hasConceptScore W2333835900C140205800 @default.
- W2333835900 hasConceptScore W2333835900C144796933 @default.
- W2333835900 hasConceptScore W2333835900C159985019 @default.
- W2333835900 hasConceptScore W2333835900C171250308 @default.
- W2333835900 hasConceptScore W2333835900C192562407 @default.
- W2333835900 hasConceptScore W2333835900C2780841128 @default.
- W2333835900 hasConceptScore W2333835900C42360764 @default.
- W2333835900 hasConceptScore W2333835900C521977710 @default.
- W2333835900 hasIssue "8" @default.
- W2333835900 hasLocation W23338359001 @default.
- W2333835900 hasOpenAccess W2333835900 @default.
- W2333835900 hasPrimaryLocation W23338359001 @default.
- W2333835900 hasRelatedWork W2092319378 @default.
- W2333835900 hasRelatedWork W2171082064 @default.
- W2333835900 hasRelatedWork W2315337917 @default.
- W2333835900 hasRelatedWork W2347469006 @default.
- W2333835900 hasRelatedWork W2900524175 @default.