- W2337441851 abstract "The effect of elevated temperatures on basalt textile reinforced calcium aluminate cementitious composite is reported. After being exposed for 1 h at various constant temperature levels, samples were tested in hot as well as after cooling down at room temperature conditions (termed as residual tests). Targeted constant temperatures considered varied from 25 up to 400 °C, representing the range that affects the main dehydration of hydration products present in the matrix. The residual mechanical response of basalt fabric at similar temperature ranges was also measured. Thermogravimetry and X-ray diffraction analysis were used to study phase changes as a function of temperature. Scanning electron microscopy (SEM) was used to study damage processes in the fiber–matrix interfaces. Results indicate that the tensile strength of composites in residual conditions is higher than that in hot conditions. This traced back the mechanism that the fabric-coating visco-elastic/plastic interface changes with temperature, which affects the textile-cementitious adhesion properties. When the composite was tested in hot conditions, a much more aggressive loss of the load-carrying capacity was observed. With increasing temperature, the hot tests, showed a significant reduction in tensile strength, elastic modulus and strain capacity. Ultimate direct tensile strength values obtained under hot condition were, on average, 50% lower than the residual ones." @default.
- W2337441851 created "2016-06-24" @default.
- W2337441851 creator A5030810436 @default.
- W2337441851 creator A5039035767 @default.
- W2337441851 creator A5050518044 @default.
- W2337441851 creator A5068799106 @default.
- W2337441851 creator A5091389687 @default.
- W2337441851 date "2016-07-01" @default.
- W2337441851 modified "2023-10-14" @default.
- W2337441851 title "Tensile strength of a calcium-aluminate cementitious composite reinforced with basalt textile in a high-temperature environment" @default.
- W2337441851 cites W1974302437 @default.
- W2337441851 cites W1976142012 @default.
- W2337441851 cites W1990518213 @default.
- W2337441851 cites W2002831333 @default.
- W2337441851 cites W2025621218 @default.
- W2337441851 cites W2030046625 @default.
- W2337441851 cites W2054376315 @default.
- W2337441851 cites W2063256611 @default.
- W2337441851 cites W2076324425 @default.
- W2337441851 cites W2080768474 @default.
- W2337441851 cites W2105963205 @default.
- W2337441851 cites W2154080551 @default.
- W2337441851 doi "https://doi.org/10.1016/j.cemconcomp.2016.04.006" @default.
- W2337441851 hasPublicationYear "2016" @default.
- W2337441851 type Work @default.
- W2337441851 sameAs 2337441851 @default.
- W2337441851 citedByCount "36" @default.
- W2337441851 countsByYear W23374418512016 @default.
- W2337441851 countsByYear W23374418512017 @default.
- W2337441851 countsByYear W23374418512018 @default.
- W2337441851 countsByYear W23374418512019 @default.
- W2337441851 countsByYear W23374418512020 @default.
- W2337441851 countsByYear W23374418512021 @default.
- W2337441851 countsByYear W23374418512022 @default.
- W2337441851 countsByYear W23374418512023 @default.
- W2337441851 crossrefType "journal-article" @default.
- W2337441851 hasAuthorship W2337441851A5030810436 @default.
- W2337441851 hasAuthorship W2337441851A5039035767 @default.
- W2337441851 hasAuthorship W2337441851A5050518044 @default.
- W2337441851 hasAuthorship W2337441851A5068799106 @default.
- W2337441851 hasAuthorship W2337441851A5091389687 @default.
- W2337441851 hasConcept C104779481 @default.
- W2337441851 hasConcept C112950240 @default.
- W2337441851 hasConcept C159985019 @default.
- W2337441851 hasConcept C192562407 @default.
- W2337441851 hasConcept C193483257 @default.
- W2337441851 hasConcept C26771246 @default.
- W2337441851 hasConcept C2777387946 @default.
- W2337441851 hasConcept C2781448156 @default.
- W2337441851 hasConcept C519885992 @default.
- W2337441851 hasConcept C523993062 @default.
- W2337441851 hasConceptScore W2337441851C104779481 @default.
- W2337441851 hasConceptScore W2337441851C112950240 @default.
- W2337441851 hasConceptScore W2337441851C159985019 @default.
- W2337441851 hasConceptScore W2337441851C192562407 @default.
- W2337441851 hasConceptScore W2337441851C193483257 @default.
- W2337441851 hasConceptScore W2337441851C26771246 @default.
- W2337441851 hasConceptScore W2337441851C2777387946 @default.
- W2337441851 hasConceptScore W2337441851C2781448156 @default.
- W2337441851 hasConceptScore W2337441851C519885992 @default.
- W2337441851 hasConceptScore W2337441851C523993062 @default.
- W2337441851 hasLocation W23374418511 @default.
- W2337441851 hasOpenAccess W2337441851 @default.
- W2337441851 hasPrimaryLocation W23374418511 @default.
- W2337441851 hasRelatedWork W2364658188 @default.
- W2337441851 hasRelatedWork W2376637741 @default.
- W2337441851 hasRelatedWork W2387004473 @default.
- W2337441851 hasRelatedWork W2810307866 @default.
- W2337441851 hasRelatedWork W2998262509 @default.
- W2337441851 hasRelatedWork W3123552942 @default.
- W2337441851 hasRelatedWork W3195851079 @default.
- W2337441851 hasRelatedWork W4206404873 @default.
- W2337441851 hasRelatedWork W4224272707 @default.
- W2337441851 hasRelatedWork W4281686140 @default.
- W2337441851 hasVolume "70" @default.
- W2337441851 isParatext "false" @default.
- W2337441851 isRetracted "false" @default.
- W2337441851 magId "2337441851" @default.
- W2337441851 workType "article" @default.