- W2338072014 abstract "The composite cement mixtures were prepared by mixing brushite (B) with, the amorphous hydrated calcium silicate phosphate (CSPH) or annealed calcium silicate phosphate (CSP composed of Si-saturated hydroxyapatite, wollastonite and silica) phases and water as liquid component. The contents of the silicate-phosphate phase in composites were 10.30 and 50 wt%. The significant effect of both the Ca/P ratio and different solubility of calcium silicate phosphate component in starting cement systems on setting time and phase composition of the final composite cements was demonstrated. The compressive strength of the set cements increased with the filler addition and the highest value (~ 48 MPa) exhibited the 50CSP/B cement composite. The final setting times of the composite cements decreased with the CSPH addition from about 25 to 17 min in 50CSHP/B and setting time of CSP/B composites was around 30 min. The higher content of silica in cements caused the precipitation of fine hydroxyapatite particles in the form of nanoneedles or thin plates perpendicularly oriented to sample surface. The analysis of in vitro cement cytotoxicity demonstrated the strong reduction in cytotoxicity of 10CSPH/B composite with time of cultivation (a low cytotoxicity after 9 days of culture) contrary to cements with higher calcium silicate-phosphate content. These results were attributed to the different surface topography of composite substrates and possible stimulation of cell proliferation by the slow continuously release of ions from 10CSPH/B cement." @default.
- W2338072014 created "2016-06-24" @default.
- W2338072014 creator A5016338474 @default.
- W2338072014 creator A5022680882 @default.
- W2338072014 creator A5022730775 @default.
- W2338072014 creator A5023479192 @default.
- W2338072014 creator A5052016783 @default.
- W2338072014 creator A5063075121 @default.
- W2338072014 creator A5077243715 @default.
- W2338072014 date "2016-07-01" @default.
- W2338072014 modified "2023-10-18" @default.
- W2338072014 title "Effect of phase composition of calcium silicate phosphate component on properties of brushite based composite cements" @default.
- W2338072014 cites W1490204844 @default.
- W2338072014 cites W1490849973 @default.
- W2338072014 cites W1966296130 @default.
- W2338072014 cites W1966481184 @default.
- W2338072014 cites W1977671835 @default.
- W2338072014 cites W1977933417 @default.
- W2338072014 cites W1980247428 @default.
- W2338072014 cites W1981904320 @default.
- W2338072014 cites W1984516703 @default.
- W2338072014 cites W1985441897 @default.
- W2338072014 cites W2001554453 @default.
- W2338072014 cites W2003252624 @default.
- W2338072014 cites W2004395503 @default.
- W2338072014 cites W2004438690 @default.
- W2338072014 cites W2012091631 @default.
- W2338072014 cites W2012682158 @default.
- W2338072014 cites W2015547112 @default.
- W2338072014 cites W2017133020 @default.
- W2338072014 cites W2017648505 @default.
- W2338072014 cites W2022540420 @default.
- W2338072014 cites W2034287320 @default.
- W2338072014 cites W2044490838 @default.
- W2338072014 cites W2047117461 @default.
- W2338072014 cites W2047157588 @default.
- W2338072014 cites W2059139841 @default.
- W2338072014 cites W2065179124 @default.
- W2338072014 cites W2065695374 @default.
- W2338072014 cites W2067644085 @default.
- W2338072014 cites W2069523649 @default.
- W2338072014 cites W2070169744 @default.
- W2338072014 cites W2077107164 @default.
- W2338072014 cites W2077301067 @default.
- W2338072014 cites W2078713276 @default.
- W2338072014 cites W2080930971 @default.
- W2338072014 cites W2084007382 @default.
- W2338072014 cites W2087429753 @default.
- W2338072014 cites W2092463281 @default.
- W2338072014 cites W2095392615 @default.
- W2338072014 cites W2099884403 @default.
- W2338072014 cites W2116036920 @default.
- W2338072014 cites W2136413739 @default.
- W2338072014 cites W2144494087 @default.
- W2338072014 cites W2145172006 @default.
- W2338072014 cites W2145421666 @default.
- W2338072014 cites W2146897140 @default.
- W2338072014 cites W2165221289 @default.
- W2338072014 cites W2168018521 @default.
- W2338072014 cites W2171802389 @default.
- W2338072014 cites W2327816241 @default.
- W2338072014 doi "https://doi.org/10.1016/j.matchar.2016.04.011" @default.
- W2338072014 hasPublicationYear "2016" @default.
- W2338072014 type Work @default.
- W2338072014 sameAs 2338072014 @default.
- W2338072014 citedByCount "15" @default.
- W2338072014 countsByYear W23380720142017 @default.
- W2338072014 countsByYear W23380720142018 @default.
- W2338072014 countsByYear W23380720142019 @default.
- W2338072014 countsByYear W23380720142020 @default.
- W2338072014 countsByYear W23380720142021 @default.
- W2338072014 countsByYear W23380720142022 @default.
- W2338072014 countsByYear W23380720142023 @default.
- W2338072014 crossrefType "journal-article" @default.
- W2338072014 hasAuthorship W2338072014A5016338474 @default.
- W2338072014 hasAuthorship W2338072014A5022680882 @default.
- W2338072014 hasAuthorship W2338072014A5022730775 @default.
- W2338072014 hasAuthorship W2338072014A5023479192 @default.
- W2338072014 hasAuthorship W2338072014A5052016783 @default.
- W2338072014 hasAuthorship W2338072014A5063075121 @default.
- W2338072014 hasAuthorship W2338072014A5077243715 @default.
- W2338072014 hasConcept C104779481 @default.
- W2338072014 hasConcept C127413603 @default.
- W2338072014 hasConcept C13965031 @default.
- W2338072014 hasConcept C159985019 @default.
- W2338072014 hasConcept C178790620 @default.
- W2338072014 hasConcept C185592680 @default.
- W2338072014 hasConcept C191897082 @default.
- W2338072014 hasConcept C192562407 @default.
- W2338072014 hasConcept C199289684 @default.
- W2338072014 hasConcept C22502612 @default.
- W2338072014 hasConcept C2777001299 @default.
- W2338072014 hasConcept C2777132085 @default.
- W2338072014 hasConcept C2777335606 @default.
- W2338072014 hasConcept C2780300285 @default.
- W2338072014 hasConcept C42360764 @default.
- W2338072014 hasConcept C519063684 @default.
- W2338072014 hasConcept C523993062 @default.