- W2349593451 abstract "Using the vacuum bag technique for the patches of boron fiber/epoxy(Bf/epoxy) composites,the center-cracked aluminum alloy plates with different thickness were repaired,and then the fatigue properties of the repaired specimens were tested.The fatigue life,crack growth rate and crack growth lag of the repaired specimens were investigated under fatigue loadings.The results show that the fatigue life of the center-cracked aluminum alloy plates is increased by repairing with Bf/epoxy patches,and the increment of fatigue life decreases with the increase of the plate thickness.The fatigue life of the repaired specimens with thicknesses of 1.76mm,5.20mm and 10.20mm is 22.30 times,12.84 times and 8.40 times that of those unrepaired specimens respectively.The repaired specimens with thickness of 1.76mm can still bear fatigue loading when the aluminum alloy plate fractured completely,while the repaired specimens with thickness of 5.20mm and 10.20mm can not do so.Both crack growth rate and normalized crack length difference increase with the increase of the plate thickness." @default.
- W2349593451 created "2016-06-24" @default.
- W2349593451 creator A5085059789 @default.
- W2349593451 date "2009-01-01" @default.
- W2349593451 modified "2023-09-28" @default.
- W2349593451 title "Thickness effects on fatigue properties of cracked aluminum alloy plate single-side repaired with boron fiber/epoxy patches" @default.
- W2349593451 hasPublicationYear "2009" @default.
- W2349593451 type Work @default.
- W2349593451 sameAs 2349593451 @default.
- W2349593451 citedByCount "0" @default.
- W2349593451 crossrefType "journal-article" @default.
- W2349593451 hasAuthorship W2349593451A5085059789 @default.
- W2349593451 hasConcept C159985019 @default.
- W2349593451 hasConcept C166595027 @default.
- W2349593451 hasConcept C192562407 @default.
- W2349593451 hasConcept C2780026712 @default.
- W2349593451 hasConcept C513153333 @default.
- W2349593451 hasConcept C59085676 @default.
- W2349593451 hasConcept C69809600 @default.
- W2349593451 hasConcept C75512024 @default.
- W2349593451 hasConceptScore W2349593451C159985019 @default.
- W2349593451 hasConceptScore W2349593451C166595027 @default.
- W2349593451 hasConceptScore W2349593451C192562407 @default.
- W2349593451 hasConceptScore W2349593451C2780026712 @default.
- W2349593451 hasConceptScore W2349593451C513153333 @default.
- W2349593451 hasConceptScore W2349593451C59085676 @default.
- W2349593451 hasConceptScore W2349593451C69809600 @default.
- W2349593451 hasConceptScore W2349593451C75512024 @default.
- W2349593451 hasLocation W23495934511 @default.
- W2349593451 hasOpenAccess W2349593451 @default.
- W2349593451 hasPrimaryLocation W23495934511 @default.
- W2349593451 hasRelatedWork W1593287974 @default.
- W2349593451 hasRelatedWork W1687006261 @default.
- W2349593451 hasRelatedWork W1965201587 @default.
- W2349593451 hasRelatedWork W1969483921 @default.
- W2349593451 hasRelatedWork W2058070547 @default.
- W2349593451 hasRelatedWork W2063407520 @default.
- W2349593451 hasRelatedWork W2074746668 @default.
- W2349593451 hasRelatedWork W2082256774 @default.
- W2349593451 hasRelatedWork W2169158569 @default.
- W2349593451 hasRelatedWork W2242147392 @default.
- W2349593451 hasRelatedWork W2331647828 @default.
- W2349593451 hasRelatedWork W2350387275 @default.
- W2349593451 hasRelatedWork W2354789555 @default.
- W2349593451 hasRelatedWork W2355251761 @default.
- W2349593451 hasRelatedWork W2386667958 @default.
- W2349593451 hasRelatedWork W2392392277 @default.
- W2349593451 hasRelatedWork W2415896541 @default.
- W2349593451 hasRelatedWork W2904684364 @default.
- W2349593451 hasRelatedWork W2991121254 @default.
- W2349593451 hasRelatedWork W641318737 @default.
- W2349593451 isParatext "false" @default.
- W2349593451 isRetracted "false" @default.
- W2349593451 magId "2349593451" @default.
- W2349593451 workType "article" @default.